Structural and ionic conductivity studies of MgI2 - Mg3(PO4)2.5H2O solid electrolytes / Mohd Khairul Hazwan Mohd Yusof
In this study, MgI2 and Mg3(PO4)2.5H20 was ball milled and pelletized to make it as magnesium solid electrolyte. This study was conducted to determine the optimum composition of Mg-based solid electrolyte where MgI2 - Mg3(PO4)2.5H2O pellets are used for investigating maximum ionic conductivity and a...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Thesis |
| 语言: | English |
| 出版: |
2008
|
| 在线阅读: | https://ir.uitm.edu.my/id/eprint/101205/1/101205.pdf |
| 标签: |
添加标签
没有标签, 成为第一个标记此记录!
|
| id |
my-uitm-ir.101205 |
|---|---|
| record_format |
uketd_dc |
| spelling |
my-uitm-ir.1012052024-08-27T17:22:35Z Structural and ionic conductivity studies of MgI2 - Mg3(PO4)2.5H2O solid electrolytes / Mohd Khairul Hazwan Mohd Yusof 2008 Mohd Yusof, Mohd Khairul Hazwan In this study, MgI2 and Mg3(PO4)2.5H20 was ball milled and pelletized to make it as magnesium solid electrolyte. This study was conducted to determine the optimum composition of Mg-based solid electrolyte where MgI2 - Mg3(PO4)2.5H2O pellets are used for investigating maximum ionic conductivity and also it structural properties. A maximum conductivity of 7.00 x 10-4 S cm-1 was obtained with composition of weight 30% MgI2 and 70% Mg3(PO4)2.5H2O. The milling time was 1 hour that gave the optimum value of conductivity. FTIR analysis shows there is a strong interaction between these two pure samples thus resulting a higher conductivity to produce a higher performance of solid electrolyte. XRD patterns shows that MgI2 salt is more crystalline compared to pure Mg3(PO4)2 salt. There is a formation of new complex that gave maximum conductivity value to the magnesium solid electrolyte. The appearance of new peak at 56.36○ in the XRD diagram for 30% MgI2 – 70% Mg3(PO4)2 composition indicates complexation has occurred thus giving a high value of conductivity. 2008 Thesis https://ir.uitm.edu.my/id/eprint/101205/ https://ir.uitm.edu.my/id/eprint/101205/1/101205.pdf text en public degree Universiti Teknologi MARA (UiTM) Faculty of Applied Sciences |
| institution |
Universiti Teknologi MARA |
| collection |
UiTM Institutional Repository |
| language |
English |
| description |
In this study, MgI2 and Mg3(PO4)2.5H20 was ball milled and pelletized to make it as magnesium solid electrolyte. This study was conducted to determine the optimum composition of Mg-based solid electrolyte where MgI2 - Mg3(PO4)2.5H2O pellets are used for investigating maximum ionic conductivity and also it structural properties. A maximum conductivity of 7.00 x 10-4 S cm-1 was obtained with composition of weight 30% MgI2 and 70% Mg3(PO4)2.5H2O. The milling time was 1 hour that gave the optimum value of conductivity. FTIR analysis shows there is a strong interaction between these two pure samples thus resulting a higher conductivity to produce a higher performance of solid electrolyte. XRD patterns shows that MgI2 salt is more crystalline compared to pure Mg3(PO4)2 salt. There is a formation of new complex that gave maximum conductivity value to the magnesium solid electrolyte. The appearance of new peak at 56.36○ in the XRD diagram for 30% MgI2 – 70% Mg3(PO4)2 composition indicates complexation has occurred thus giving a high value of conductivity. |
| format |
Thesis |
| qualification_level |
Bachelor degree |
| author |
Mohd Yusof, Mohd Khairul Hazwan |
| spellingShingle |
Mohd Yusof, Mohd Khairul Hazwan Structural and ionic conductivity studies of MgI2 - Mg3(PO4)2.5H2O solid electrolytes / Mohd Khairul Hazwan Mohd Yusof |
| author_facet |
Mohd Yusof, Mohd Khairul Hazwan |
| author_sort |
Mohd Yusof, Mohd Khairul Hazwan |
| title |
Structural and ionic conductivity studies of MgI2 - Mg3(PO4)2.5H2O solid electrolytes / Mohd Khairul Hazwan Mohd Yusof |
| title_short |
Structural and ionic conductivity studies of MgI2 - Mg3(PO4)2.5H2O solid electrolytes / Mohd Khairul Hazwan Mohd Yusof |
| title_full |
Structural and ionic conductivity studies of MgI2 - Mg3(PO4)2.5H2O solid electrolytes / Mohd Khairul Hazwan Mohd Yusof |
| title_fullStr |
Structural and ionic conductivity studies of MgI2 - Mg3(PO4)2.5H2O solid electrolytes / Mohd Khairul Hazwan Mohd Yusof |
| title_full_unstemmed |
Structural and ionic conductivity studies of MgI2 - Mg3(PO4)2.5H2O solid electrolytes / Mohd Khairul Hazwan Mohd Yusof |
| title_sort |
structural and ionic conductivity studies of mgi2 - mg3(po4)2.5h2o solid electrolytes / mohd khairul hazwan mohd yusof |
| granting_institution |
Universiti Teknologi MARA (UiTM) |
| granting_department |
Faculty of Applied Sciences |
| publishDate |
2008 |
| url |
https://ir.uitm.edu.my/id/eprint/101205/1/101205.pdf |
| _version_ |
1811769145280167936 |