Elastic and structural studies on (95-x)TeO₂-5La₂O₃-xTiO₂ lanthanum tellurite and xLi₂O-(100-X)[0.65GeO₂.O35PbO]lead germanate glasses / Izyan Nuraini Sapian
Lanthanum tellurite and lead germanate glasses with compositions (95-x)TeO₂-5La₂O₃-xTiO₂ (x = 0 mol% to 20 mol%) and xLi₂O-(100-X)[0.65GeO₂.O35PbO] (x = 0 mol% to 40 mol%) were prepared by the melt quenching method, respectively. Elastic and structural properties of the glasses were studied by measu...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2016
|
| Online Access: | https://ir.uitm.edu.my/id/eprint/18484/2/TM_IZYAN%20NURAINI%20SAPIAN%20AS%2016_5.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Lanthanum tellurite and lead germanate glasses with compositions (95-x)TeO₂-5La₂O₃-xTiO₂ (x = 0 mol% to 20 mol%) and xLi₂O-(100-X)[0.65GeO₂.O35PbO] (x = 0 mol% to 40 mol%) were prepared by the melt quenching method, respectively. Elastic and structural properties of the glasses were studied by measuring sound velocity using the pulse-echo-overlap technique and Fourier Transform Infrared (FTIR) spectroscopy, respectively. For (95-x)TeO₂-5La₂O₃-xTiO₂ (x = 0 mol% to 20 mol%) samples, ultrasonic velocity measurements showed both independent moduli (Cʟ and μ ) and related elastic moduli such as bulk modulus (Kₑ), Young's modulus, hardness and Debye temperature were observed to increase gradually for x < 15 mol% followed by a large increase at x = 20 mol% addition of TiO₂. The results obtained showed that this glass system becomes more stable, rigid and stiffer with addition of TiC>2. Structural analysis showed increase in bridging-oxygen (BO) compared to non-bridging oxygen (NBO). Differential Scanning Calorimetry (DSC) measurements showed Tg increased with addition of TiO₂ and confirms the increasing rigidity of the network… |
|---|