Banana trunk / polyvinyl alcohol composite : the effect of filler loading and gult palmitate salt as coupling agent / Muhammad Syafiq Mohd Shukri
A Poly (vinyl alcohol) filled with banana trunk fibre (PVA/BT) film was prepared by solution casting technique. The glut Palmitate Salt (GP) as a coupling agent was added in the PVA/BT. The prepared films were studied for mechanical properties of tensile strength, Young’s Modulus and percentage of e...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Thesis |
| 語言: | English |
| 出版: |
2020
|
| 主題: | |
| 在線閱讀: | https://ir.uitm.edu.my/id/eprint/34277/1/34277.pdf |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | A Poly (vinyl alcohol) filled with banana trunk fibre (PVA/BT) film was prepared by solution casting technique. The glut Palmitate Salt (GP) as a coupling agent was added in the PVA/BT. The prepared films were studied for mechanical properties of tensile strength, Young’s Modulus and percentage of elongation at break. Then, the thermal behavior of the film was also studied and determined by using Differential Scanning Calorimetry (DSC). The result of melting temperature (Tm) and glass transition temperature (Tg) are recorded. The characteristic of PVA, BT, PVA/BT/GP was conducted by using Fourier Transform Infrared (FTIR) Spectroscopy Analysis. In addition, the prepared film was studied for physical properties by using density and water absorption test. The comparison between PVA/BT and PVA/BT/GP were made and it was found that the addition of GP has improved the tensile strength and Young’s Modulus due to GP improved the adhesion and interfacial bonding between matrix and fibers. For DSC analysis, the Tm was decreased by addition of BT due to the uneven intermolecular bonding between matrix and fibre. The study on percentage water absorption of the PVA/BT and PVA/BT/GP which by addition of GP was decreased the percentage due to the good adhesion between filler and matrix. The result showed that the increased in density value as the fibre loading increase. This is due to the increased in weight of banana trunk fibre in the film. |
|---|