The effect of treated kenaf fiber on HDPE / glass fiber hybrid composite: characterization and mechanical properties / Nur Nadqirah Abd Jamin

Composites of HDPE/Glass fiber reinforced with treated kenaf fiber have been prepared by melt mixing. The effect of kenaf fiber loading at 5, 10, and 15 % on mechanical and physical properties of composite sample were studied. FTIR Spectra show the removal of hemicellulose and reduction of OH group...

Full description

Saved in:

Bibliographic Details
Main Author:	Abd Jamin, Nur Nadqirah
Format:	Thesis
Language:	English
Published:	2020
Subjects:	Organic chemistry Synthetic products
Online Access:	https://ir.uitm.edu.my/id/eprint/34330/1/34330.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.34330
record_format	uketd_dc
spelling	my-uitm-ir.343302020-09-14T09:16:11Z The effect of treated kenaf fiber on HDPE / glass fiber hybrid composite: characterization and mechanical properties / Nur Nadqirah Abd Jamin 2020-09-07 Abd Jamin, Nur Nadqirah Organic chemistry Polymers. Macromolecules Synthetic products Composites of HDPE/Glass fiber reinforced with treated kenaf fiber have been prepared by melt mixing. The effect of kenaf fiber loading at 5, 10, and 15 % on mechanical and physical properties of composite sample were studied. FTIR Spectra show the removal of hemicellulose and reduction of OH group present in kenaf fiber surface after modification. DSC result indicated better thermal stability of kenaf fiber after surface modification is slightly increased of melting temperature from 25.01°C to 25.04°C and markedly increased in enthalpy from 282.6 J/g to 315.7 J/g compared to unmodified kenaf fiber. There are increase in tensile strength and tensile modulus at optimum loading of 5 % of kenaf fiber due to good bondability and wettability among the matrix and treated filler. Further increase (10 and 15%) kenaf fiber loading have resulted to reduced tensile strength and tensile modulus due to dispersion and agglomeration of filler in polymer matrix. In elongation at break, the neat HDPE is the highest percent elongation at break. However, the percent elongation at break becomes decreased when reinforced with glass fiber which tends to be more brittle or stiff for the composite sample. In further increasing kenaf fiber loading at 10 and 15 %, it shows the decreasing in percent elongation at break due to the poor interfacial adhesion between filler and matrix. From impact strength, it shows the declined trend of HDPE/Glass fiber reinforced with kenaf fiber in increasing amount of kenaf fiber. This result of impact strength is opposite to theory whereas the impact strength decreased as the decreased in percent crystallinity in high filler loading. This is may cause by the formation of voids during compression molding process. Water absorption showed higher percentage as increase amount of kenaf fiber loading due to OH group existed on the filler. However, comparison data of all properties from untreated and treated kenaf fiber at 5% indicating that treated fiber have higher values than untreated fiber. 2020-09 Thesis https://ir.uitm.edu.my/id/eprint/34330/ https://ir.uitm.edu.my/id/eprint/34330/1/34330.pdf text en public degree Universiti Teknologi Mara perlis Faculty of Applied Sciences
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
topic	Organic chemistry Organic chemistry Synthetic products
spellingShingle	Organic chemistry Organic chemistry Synthetic products Abd Jamin, Nur Nadqirah The effect of treated kenaf fiber on HDPE / glass fiber hybrid composite: characterization and mechanical properties / Nur Nadqirah Abd Jamin
description	Composites of HDPE/Glass fiber reinforced with treated kenaf fiber have been prepared by melt mixing. The effect of kenaf fiber loading at 5, 10, and 15 % on mechanical and physical properties of composite sample were studied. FTIR Spectra show the removal of hemicellulose and reduction of OH group present in kenaf fiber surface after modification. DSC result indicated better thermal stability of kenaf fiber after surface modification is slightly increased of melting temperature from 25.01°C to 25.04°C and markedly increased in enthalpy from 282.6 J/g to 315.7 J/g compared to unmodified kenaf fiber. There are increase in tensile strength and tensile modulus at optimum loading of 5 % of kenaf fiber due to good bondability and wettability among the matrix and treated filler. Further increase (10 and 15%) kenaf fiber loading have resulted to reduced tensile strength and tensile modulus due to dispersion and agglomeration of filler in polymer matrix. In elongation at break, the neat HDPE is the highest percent elongation at break. However, the percent elongation at break becomes decreased when reinforced with glass fiber which tends to be more brittle or stiff for the composite sample. In further increasing kenaf fiber loading at 10 and 15 %, it shows the decreasing in percent elongation at break due to the poor interfacial adhesion between filler and matrix. From impact strength, it shows the declined trend of HDPE/Glass fiber reinforced with kenaf fiber in increasing amount of kenaf fiber. This result of impact strength is opposite to theory whereas the impact strength decreased as the decreased in percent crystallinity in high filler loading. This is may cause by the formation of voids during compression molding process. Water absorption showed higher percentage as increase amount of kenaf fiber loading due to OH group existed on the filler. However, comparison data of all properties from untreated and treated kenaf fiber at 5% indicating that treated fiber have higher values than untreated fiber.
format	Thesis
qualification_level	Bachelor degree
author	Abd Jamin, Nur Nadqirah
author_facet	Abd Jamin, Nur Nadqirah
author_sort	Abd Jamin, Nur Nadqirah
title	The effect of treated kenaf fiber on HDPE / glass fiber hybrid composite: characterization and mechanical properties / Nur Nadqirah Abd Jamin
title_short	The effect of treated kenaf fiber on HDPE / glass fiber hybrid composite: characterization and mechanical properties / Nur Nadqirah Abd Jamin
title_full	The effect of treated kenaf fiber on HDPE / glass fiber hybrid composite: characterization and mechanical properties / Nur Nadqirah Abd Jamin
title_fullStr	The effect of treated kenaf fiber on HDPE / glass fiber hybrid composite: characterization and mechanical properties / Nur Nadqirah Abd Jamin
title_full_unstemmed	The effect of treated kenaf fiber on HDPE / glass fiber hybrid composite: characterization and mechanical properties / Nur Nadqirah Abd Jamin
title_sort	effect of treated kenaf fiber on hdpe / glass fiber hybrid composite: characterization and mechanical properties / nur nadqirah abd jamin
granting_institution	Universiti Teknologi Mara perlis
granting_department	Faculty of Applied Sciences
publishDate	2020
url	https://ir.uitm.edu.my/id/eprint/34330/1/34330.pdf
_version_	1783734263792795648

The effect of treated kenaf fiber on HDPE / glass fiber hybrid composite: characterization and mechanical properties / Nur Nadqirah Abd Jamin

Similar Items