The physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / Muhammad Mustakim Mohd Ghaztar

Natural fibre is a sustainable material however, its drawbacks limit its usage. Thus, this research draws from the existing fibre treatments that are meticulous and high energy consumption by utilizing a simple and practical coating treatment. This study was carried out by direct coating the combed...

Full description

Saved in:

Bibliographic Details
Main Author:	Mohd Ghaztar, Muhammad Mustakim
Format:	Thesis
Language:	English
Published:	2021
Subjects:	Polymers Macromolecules Analytical chemistry
Online Access:	https://ir.uitm.edu.my/id/eprint/46484/1/46484.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.46484
record_format	uketd_dc
spelling	my-uitm-ir.464842022-02-15T04:27:45Z The physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / Muhammad Mustakim Mohd Ghaztar 2021-03 Mohd Ghaztar, Muhammad Mustakim Polymers. Macromolecules Analytical chemistry Natural fibre is a sustainable material however, its drawbacks limit its usage. Thus, this research draws from the existing fibre treatments that are meticulous and high energy consumption by utilizing a simple and practical coating treatment. This study was carried out by direct coating the combed raw Kenaf fibres into 1:4, 1:5 and 1:6 coating solutions viscosities prior dried, pulverised and fabricated into the composite system. Each coated Kenaf fibre composite is varied by 10, 20, 30, 40 and 50 wt% fibre loadings; then analysed for its properties. The physical test consists of density, water absorption and hardness whereas; mechanical test includes tensile, flexural, compression and impact tests. The thermal and chemical characterisations are Thermogravimetric (TGA), Differential Scanning Calorimetry (DSC) and Fourier Transform Infrared (FTIR) respectively. The properties of both fibres and composites for coated samples were compared to the properties of pristine epoxy, untreated as well as NaOH/ Sil treated samples. In theory, fibres properties are highly influenced by the coating solutions viscosity which improves its surface interaction and stiffness once fabricated in the composite system. The optimum coating viscosity able to minimize the surface gap problem, by strongly adhere to the delicate surfaces of fibres and; concurrently penetrates also lock the fibres cell wall to creates a consistent deformation. The result showed that the 1:6 coating solution was the optimum viscosity as it highly penetrated the fibres system and form an individual coating formation as unachieved by other coating solutions viscosity. The high coating domination improved the fibres dispersion, density (72.7 %), shapes consistency, thermal stability (4.2 %) and mechanical stiffness (367 %). The improved fibres properties were proportional to the total improvement of composites density, voids content, specific water absorption as well as hardness properties. These also led to enhancement in composites stiffness in tensile (28.1 %), flexural (39.2 %), compression (46.1 %) and impact (227.8 %) properties. Since a well-stress distribution was observed at all samples fractured surfaces that contributed by the high mechanical interlocking and improved surface interaction. The 1:6 coated samples results were higher than treated NaOH/ Sil; followed by the coated 1:5, 1:4 and untreated samples. The coated 1:4 and 1:5 samples unable to perform well due to the low coating penetration as well as high coating deterioration that affect its overall properties. In general, the coating treatment might be a practical method for the industry as if offers a simple process that produces high strength of the treated materials. The treatment also might be a solution to revolutionize the other natural-based materials to venture in more robust applications for a sustainable future. 2021-03 Thesis https://ir.uitm.edu.my/id/eprint/46484/ https://ir.uitm.edu.my/id/eprint/46484/1/46484.pdf text en public phd doctoral Universiti Teknologi MARA Faculty of Applied Science
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
topic	Polymers Macromolecules Analytical chemistry
spellingShingle	Polymers Macromolecules Analytical chemistry Mohd Ghaztar, Muhammad Mustakim The physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / Muhammad Mustakim Mohd Ghaztar
description	Natural fibre is a sustainable material however, its drawbacks limit its usage. Thus, this research draws from the existing fibre treatments that are meticulous and high energy consumption by utilizing a simple and practical coating treatment. This study was carried out by direct coating the combed raw Kenaf fibres into 1:4, 1:5 and 1:6 coating solutions viscosities prior dried, pulverised and fabricated into the composite system. Each coated Kenaf fibre composite is varied by 10, 20, 30, 40 and 50 wt% fibre loadings; then analysed for its properties. The physical test consists of density, water absorption and hardness whereas; mechanical test includes tensile, flexural, compression and impact tests. The thermal and chemical characterisations are Thermogravimetric (TGA), Differential Scanning Calorimetry (DSC) and Fourier Transform Infrared (FTIR) respectively. The properties of both fibres and composites for coated samples were compared to the properties of pristine epoxy, untreated as well as NaOH/ Sil treated samples. In theory, fibres properties are highly influenced by the coating solutions viscosity which improves its surface interaction and stiffness once fabricated in the composite system. The optimum coating viscosity able to minimize the surface gap problem, by strongly adhere to the delicate surfaces of fibres and; concurrently penetrates also lock the fibres cell wall to creates a consistent deformation. The result showed that the 1:6 coating solution was the optimum viscosity as it highly penetrated the fibres system and form an individual coating formation as unachieved by other coating solutions viscosity. The high coating domination improved the fibres dispersion, density (72.7 %), shapes consistency, thermal stability (4.2 %) and mechanical stiffness (367 %). The improved fibres properties were proportional to the total improvement of composites density, voids content, specific water absorption as well as hardness properties. These also led to enhancement in composites stiffness in tensile (28.1 %), flexural (39.2 %), compression (46.1 %) and impact (227.8 %) properties. Since a well-stress distribution was observed at all samples fractured surfaces that contributed by the high mechanical interlocking and improved surface interaction. The 1:6 coated samples results were higher than treated NaOH/ Sil; followed by the coated 1:5, 1:4 and untreated samples. The coated 1:4 and 1:5 samples unable to perform well due to the low coating penetration as well as high coating deterioration that affect its overall properties. In general, the coating treatment might be a practical method for the industry as if offers a simple process that produces high strength of the treated materials. The treatment also might be a solution to revolutionize the other natural-based materials to venture in more robust applications for a sustainable future.
format	Thesis
qualification_name	Doctor of Philosophy (PhD.)
qualification_level	Doctorate
author	Mohd Ghaztar, Muhammad Mustakim
author_facet	Mohd Ghaztar, Muhammad Mustakim
author_sort	Mohd Ghaztar, Muhammad Mustakim
title	The physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / Muhammad Mustakim Mohd Ghaztar
title_short	The physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / Muhammad Mustakim Mohd Ghaztar
title_full	The physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / Muhammad Mustakim Mohd Ghaztar
title_fullStr	The physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / Muhammad Mustakim Mohd Ghaztar
title_full_unstemmed	The physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / Muhammad Mustakim Mohd Ghaztar
title_sort	physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / muhammad mustakim mohd ghaztar
granting_institution	Universiti Teknologi MARA
granting_department	Faculty of Applied Science
publishDate	2021
url	https://ir.uitm.edu.my/id/eprint/46484/1/46484.pdf
_version_	1783734753607811072

The physico-mechanical and thermal properties of coated kenaf fibres in epoxy matrix composite / Muhammad Mustakim Mohd Ghaztar

Similar Items