Investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / Noor Leha Abdul Rahman

Biomorphic Silicon Carbide (bioSiC) is a new class of porous ceramic materials derived directly from natural resources. Due to the increasing demand of global silicon carbide (nearly 16.1% from 2020 to 2027), this study is an attempt to overcome the depletion of petroleum resource faced by the comme...

Full description

Saved in:

Bibliographic Details
Main Author:	Abdul Rahman, Noor Leha
Format:	Thesis
Language:	English
Published:	2020
Subjects:	TP Chemical technology Synthetic products Chemical engineering
Online Access:	https://ir.uitm.edu.my/id/eprint/53835/1/53835.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.53835
record_format	uketd_dc
spelling	my-uitm-ir.538352022-04-12T00:58:53Z Investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / Noor Leha Abdul Rahman 2020-10 Abdul Rahman, Noor Leha TP Chemical technology Synthetic products Chemical engineering Biomorphic Silicon Carbide (bioSiC) is a new class of porous ceramic materials derived directly from natural resources. Due to the increasing demand of global silicon carbide (nearly 16.1% from 2020 to 2027), this study is an attempt to overcome the depletion of petroleum resource faced by the commercial silicon carbide. The proposed bioSiC is an alternative to the expensive commercial silicon carbide by using the wood waste from furniture industry. Among the natural resources available, natural wood has been identified as an attractive option of carbon precursor due to the availability and its anisotropic nature which gives the unique feature as a hierarchical preform. This ceramic material is fabricated by pyrolysis of wood waste in an inert atmosphere leaving an amorphous carbon preform. The amorphous carbon is infiltrated with molten Si at elevated temperature forming a porous bioSiC with a microstructure that is analogous to the wood precursor. The objective of this study is to investigate the processing, microstructure, and properties of bioSiC produced using wood-derived preform. This was accomplished by analysis of bioSiC from three different wood precursors, obtained from Malaysian rainforest which covered a range of pore volumes, pore sizes, and pore size distributions. In this work, Kapur, Dark Red Meranti and Kempas were pyrolyzed at the temperature of 850 C for 2 hours to produce the carbon preforms. BioSiC was prepared at two different temperatures, which were 1500 C and 1600 C. The silicon melt infiltration process was conducted at 1 to 5 hours holding time in order to investigate the effect of holding time on the properties of bioSiC. The decomposition behaviour of raw wood into carbon during pyrolysis was assessed using a thermo-gravimetric (TGA) system by heating the sample from 50 °C to 1000 °C. Scanning electron microscope (SEM) analysis of pyrolyzed samples and bioSiC showed that the structural feature preserved the original wood structure. Pore volume and porosity of the samples, as determined by mercury intrusion porosimetry, showed multimodal pore distribution of pyrolyzed samples from small to large pores. The density of bioSiC ranging from 0.6850 g/cm3 to 0.9983 g/cm3 was determined by the Archimedes method. The bioSiC phase of resulting product was analysed by X-ray diffraction (XRD), indicating that SiC has been produced without excess silicon after etching. The increasing holding time of infiltration enhanced the formation of bioSiC up to 3 hours. However, longer reaction to 5 hours reduced the bioSiC formation at infiltration temperature of 1500 C. Scanning electron microscope (SEM) analysis showed that the silicon infiltrated both larger and smaller vessels by retaining the original wood structure without being affected by the closure of the small pore and reduction of pore diameter. The mechanical performance indicated that the formation of bioSiC obtained by Dark Red Meranti was optimum at 3 hours holding time and temperature of 1500 C Therefore, among the three types of wood precursor selected, Dark Red Meranti showed more promising for the production of porous biomorphic silicon carbide compared to Kapur and Kempas. The synthesis of biomorphic porous SiC from sustainable and low-cost materials demonstrates the novelty of this study. The possibility of SiC production from Malaysian hardwood is promising with the prospect of potential application such as catalyst support, molten metal filter or high-performance advanced ceramics. 2020-10 Thesis https://ir.uitm.edu.my/id/eprint/53835/ https://ir.uitm.edu.my/id/eprint/53835/1/53835.pdf text en public phd doctoral Universiti Teknologi MARA Faculty of Mechanical Engineering Mei Hyie, Koay (Assoc. Prof.Ir.Dr.)
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
advisor	Mei Hyie, Koay (Assoc. Prof.Ir.Dr.)
topic	TP Chemical technology Synthetic products Chemical engineering
spellingShingle	TP Chemical technology Synthetic products Chemical engineering Abdul Rahman, Noor Leha Investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / Noor Leha Abdul Rahman
description	Biomorphic Silicon Carbide (bioSiC) is a new class of porous ceramic materials derived directly from natural resources. Due to the increasing demand of global silicon carbide (nearly 16.1% from 2020 to 2027), this study is an attempt to overcome the depletion of petroleum resource faced by the commercial silicon carbide. The proposed bioSiC is an alternative to the expensive commercial silicon carbide by using the wood waste from furniture industry. Among the natural resources available, natural wood has been identified as an attractive option of carbon precursor due to the availability and its anisotropic nature which gives the unique feature as a hierarchical preform. This ceramic material is fabricated by pyrolysis of wood waste in an inert atmosphere leaving an amorphous carbon preform. The amorphous carbon is infiltrated with molten Si at elevated temperature forming a porous bioSiC with a microstructure that is analogous to the wood precursor. The objective of this study is to investigate the processing, microstructure, and properties of bioSiC produced using wood-derived preform. This was accomplished by analysis of bioSiC from three different wood precursors, obtained from Malaysian rainforest which covered a range of pore volumes, pore sizes, and pore size distributions. In this work, Kapur, Dark Red Meranti and Kempas were pyrolyzed at the temperature of 850 C for 2 hours to produce the carbon preforms. BioSiC was prepared at two different temperatures, which were 1500 C and 1600 C. The silicon melt infiltration process was conducted at 1 to 5 hours holding time in order to investigate the effect of holding time on the properties of bioSiC. The decomposition behaviour of raw wood into carbon during pyrolysis was assessed using a thermo-gravimetric (TGA) system by heating the sample from 50 °C to 1000 °C. Scanning electron microscope (SEM) analysis of pyrolyzed samples and bioSiC showed that the structural feature preserved the original wood structure. Pore volume and porosity of the samples, as determined by mercury intrusion porosimetry, showed multimodal pore distribution of pyrolyzed samples from small to large pores. The density of bioSiC ranging from 0.6850 g/cm3 to 0.9983 g/cm3 was determined by the Archimedes method. The bioSiC phase of resulting product was analysed by X-ray diffraction (XRD), indicating that SiC has been produced without excess silicon after etching. The increasing holding time of infiltration enhanced the formation of bioSiC up to 3 hours. However, longer reaction to 5 hours reduced the bioSiC formation at infiltration temperature of 1500 C. Scanning electron microscope (SEM) analysis showed that the silicon infiltrated both larger and smaller vessels by retaining the original wood structure without being affected by the closure of the small pore and reduction of pore diameter. The mechanical performance indicated that the formation of bioSiC obtained by Dark Red Meranti was optimum at 3 hours holding time and temperature of 1500 C Therefore, among the three types of wood precursor selected, Dark Red Meranti showed more promising for the production of porous biomorphic silicon carbide compared to Kapur and Kempas. The synthesis of biomorphic porous SiC from sustainable and low-cost materials demonstrates the novelty of this study. The possibility of SiC production from Malaysian hardwood is promising with the prospect of potential application such as catalyst support, molten metal filter or high-performance advanced ceramics.
format	Thesis
qualification_name	Doctor of Philosophy (PhD.)
qualification_level	Doctorate
author	Abdul Rahman, Noor Leha
author_facet	Abdul Rahman, Noor Leha
author_sort	Abdul Rahman, Noor Leha
title	Investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / Noor Leha Abdul Rahman
title_short	Investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / Noor Leha Abdul Rahman
title_full	Investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / Noor Leha Abdul Rahman
title_fullStr	Investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / Noor Leha Abdul Rahman
title_full_unstemmed	Investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / Noor Leha Abdul Rahman
title_sort	investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / noor leha abdul rahman
granting_institution	Universiti Teknologi MARA
granting_department	Faculty of Mechanical Engineering
publishDate	2020
url	https://ir.uitm.edu.my/id/eprint/53835/1/53835.pdf
_version_	1783734880238043136

Investigation on the effect of infiltration parameters to the mechanical performance of biomorphic silicon carbide / Noor Leha Abdul Rahman

Similar Items