Synthesis of nanostructured cathode materials for li-ion battery / Roshidah Rusdi

Two types of lithium transition metal oxides, namely Lithium Nickel Cobalt Oxide (LiNi1-xCoxO2), and Lithium Nickel Cobalt Titanium Oxide (LiNi0.7-zCo0.3TizO2), were successfully synthesized using the modified combustion method. Stoichiometric and overlithiated samples were prepared. The overlithiat...

Full description

Saved in:

Bibliographic Details
Main Author:	Rusdi, Roshidah
Format:	Thesis
Language:	English
Published:	2020
Subjects:	Lithium cells
Online Access:	https://ir.uitm.edu.my/id/eprint/59751/1/59751.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.59751
record_format	uketd_dc
spelling	my-uitm-ir.597512022-05-17T08:25:00Z Synthesis of nanostructured cathode materials for li-ion battery / Roshidah Rusdi 2020-12 Rusdi, Roshidah Lithium cells Two types of lithium transition metal oxides, namely Lithium Nickel Cobalt Oxide (LiNi1-xCoxO2), and Lithium Nickel Cobalt Titanium Oxide (LiNi0.7-zCo0.3TizO2), were successfully synthesized using the modified combustion method. Stoichiometric and overlithiated samples were prepared. The overlithiated samples for both are overlithiation of Lithium Nickel Cobalt Oxide (Li1+yNi1-xCoxO2), and overlithiation of Lithium Nickel Cobalt Titanium Oxide (Li1+yNi0.6Co0.3Ti0.1O2 and Li1+yNi0.6- yCo0.3Ti0.1O2). Simultaneous Thermogravimetric Analysis (STA) were done on the parent samples LiNi1-xCoxO2 to study the thermal properties and decomposition of the precursors and to identify the right annealing temperature for parent and all modified compounds. The precursors were later heated for 24, 48 and 72 h at 700 oC. This is done to study the effect of annealing time on the characteristics of the materials as well as to get the optimum annealing temperature for good battery performance. XRay Diffractions of the samples were taken to confirm the identity of the materials and to determine the purity of the products. XRD results showed that the materials were all single phase with hexagonal layered structure of R-3m space group. The morphology of the materials and the crystallite size of the materials were determined using Field Emission Scanning Electron Microscopy (FESEM). Results show that the polyhedral like morphology of LiNi1-xCoxO2 obtained have particles in micron size while polyhedral morphology of LiNi0.6Co0.3Ti0.1O2 is in the form of plate-like crystals in nano-size (between 41 to 81 nm). Elemental analysis carried out using Energy Dispersive X-ray Spectroscopy (EDX) proved all synthesized materials have the stoichiometric ratio as calculated. Fabrication of the cathodes and assembling of the batteries were done to study the electrochemical properties. Overall performance show the best stoichiometry for LiNi1-xCoxO2 is LiNi0.7Co0.3O2. This compound is further improved by partial substitution with Ti producing LiNi0.7-zCo0.3TizO2 materials. The best stoichiometry with the best electrochemical performance for LiNi0.7-zCo0.3TizO2 group is LiNi0.6Co0.3Ti0.1O2 which is further improved by overlithiation is shows the interstitially doped Li material has better performance than substitutionally doped material. The specific capacity of the LiNi0.6Co0.3Ti0.1O2 is in the range of 141.6 to 146.0 mAh/g with a small capacity fading of 8.2% to 12.7% after cycling 70th cycle. The results are improved as compared to lab measurement of commercial LiCoO2 which is about 120 mAh/g for the first cycle. All the best stoichiometry were then subjected to in-depth study for crystal structure using the Rietveld refinement method, crystallite size studies using TEM and oxidation state studies using X-ray Photoelectron Spectroscopy (XPS). The relationship between the structure, oxidation state and the electrochemical performance were studied to deeply understand on why the material shows good electrochemical behaviour and performance. It was found that the oxidation state of the transition metals play an important role in cycleability of materials. The structural study also found that the side occupancy factor, cell parameter, cell structure and the stoichiometric amount of each transition metal in each structural site also influence the electrochemical performance. Therefore, this research was able to explain as to why the material shows good performance in terms of specific capacity and cycleability. 2020-12 Thesis https://ir.uitm.edu.my/id/eprint/59751/ https://ir.uitm.edu.my/id/eprint/59751/1/59751.pdf text en public phd doctoral Universiti Teknologi MARA Faculty of Applied Sciences Kamarulzaman, Norlida (Professor Dr.) Abd Rahman, Azilah (Assoc.Prof. Dr.) Yahaya Subhan, Ri Hanum (Professor Dr.)
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
advisor	Kamarulzaman, Norlida (Professor Dr.) Abd Rahman, Azilah (Assoc.Prof. Dr.) Yahaya Subhan, Ri Hanum (Professor Dr.)
topic	Lithium cells
spellingShingle	Lithium cells Rusdi, Roshidah Synthesis of nanostructured cathode materials for li-ion battery / Roshidah Rusdi
description	Two types of lithium transition metal oxides, namely Lithium Nickel Cobalt Oxide (LiNi1-xCoxO2), and Lithium Nickel Cobalt Titanium Oxide (LiNi0.7-zCo0.3TizO2), were successfully synthesized using the modified combustion method. Stoichiometric and overlithiated samples were prepared. The overlithiated samples for both are overlithiation of Lithium Nickel Cobalt Oxide (Li1+yNi1-xCoxO2), and overlithiation of Lithium Nickel Cobalt Titanium Oxide (Li1+yNi0.6Co0.3Ti0.1O2 and Li1+yNi0.6- yCo0.3Ti0.1O2). Simultaneous Thermogravimetric Analysis (STA) were done on the parent samples LiNi1-xCoxO2 to study the thermal properties and decomposition of the precursors and to identify the right annealing temperature for parent and all modified compounds. The precursors were later heated for 24, 48 and 72 h at 700 oC. This is done to study the effect of annealing time on the characteristics of the materials as well as to get the optimum annealing temperature for good battery performance. XRay Diffractions of the samples were taken to confirm the identity of the materials and to determine the purity of the products. XRD results showed that the materials were all single phase with hexagonal layered structure of R-3m space group. The morphology of the materials and the crystallite size of the materials were determined using Field Emission Scanning Electron Microscopy (FESEM). Results show that the polyhedral like morphology of LiNi1-xCoxO2 obtained have particles in micron size while polyhedral morphology of LiNi0.6Co0.3Ti0.1O2 is in the form of plate-like crystals in nano-size (between 41 to 81 nm). Elemental analysis carried out using Energy Dispersive X-ray Spectroscopy (EDX) proved all synthesized materials have the stoichiometric ratio as calculated. Fabrication of the cathodes and assembling of the batteries were done to study the electrochemical properties. Overall performance show the best stoichiometry for LiNi1-xCoxO2 is LiNi0.7Co0.3O2. This compound is further improved by partial substitution with Ti producing LiNi0.7-zCo0.3TizO2 materials. The best stoichiometry with the best electrochemical performance for LiNi0.7-zCo0.3TizO2 group is LiNi0.6Co0.3Ti0.1O2 which is further improved by overlithiation is shows the interstitially doped Li material has better performance than substitutionally doped material. The specific capacity of the LiNi0.6Co0.3Ti0.1O2 is in the range of 141.6 to 146.0 mAh/g with a small capacity fading of 8.2% to 12.7% after cycling 70th cycle. The results are improved as compared to lab measurement of commercial LiCoO2 which is about 120 mAh/g for the first cycle. All the best stoichiometry were then subjected to in-depth study for crystal structure using the Rietveld refinement method, crystallite size studies using TEM and oxidation state studies using X-ray Photoelectron Spectroscopy (XPS). The relationship between the structure, oxidation state and the electrochemical performance were studied to deeply understand on why the material shows good electrochemical behaviour and performance. It was found that the oxidation state of the transition metals play an important role in cycleability of materials. The structural study also found that the side occupancy factor, cell parameter, cell structure and the stoichiometric amount of each transition metal in each structural site also influence the electrochemical performance. Therefore, this research was able to explain as to why the material shows good performance in terms of specific capacity and cycleability.
format	Thesis
qualification_name	Doctor of Philosophy (PhD.)
qualification_level	Doctorate
author	Rusdi, Roshidah
author_facet	Rusdi, Roshidah
author_sort	Rusdi, Roshidah
title	Synthesis of nanostructured cathode materials for li-ion battery / Roshidah Rusdi
title_short	Synthesis of nanostructured cathode materials for li-ion battery / Roshidah Rusdi
title_full	Synthesis of nanostructured cathode materials for li-ion battery / Roshidah Rusdi
title_fullStr	Synthesis of nanostructured cathode materials for li-ion battery / Roshidah Rusdi
title_full_unstemmed	Synthesis of nanostructured cathode materials for li-ion battery / Roshidah Rusdi
title_sort	synthesis of nanostructured cathode materials for li-ion battery / roshidah rusdi
granting_institution	Universiti Teknologi MARA
granting_department	Faculty of Applied Sciences
publishDate	2020
url	https://ir.uitm.edu.my/id/eprint/59751/1/59751.pdf
_version_	1783735052456165376

Synthesis of nanostructured cathode materials for li-ion battery / Roshidah Rusdi

Similar Items