Surface modification of screen-printed carbon electrode by electrospun polyacrylic acid/ polyacrylonitrile and gold nanoparticles for non-enzymatic glucose sensor / Ilyani Ismail
The extensive knowledge and understanding regarding nanofiber through the electrospinning method has empower revolutionary of polymeric composites to be utilized for glucose sensor application. As compared to customary drop-casting method used to modify electrode surface, electrospun fibers score mo...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English |
Published: |
2021
|
Subjects: | |
Online Access: | https://ir.uitm.edu.my/id/eprint/59800/1/59800.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The extensive knowledge and understanding regarding nanofiber through the electrospinning method has empower revolutionary of polymeric composites to be utilized for glucose sensor application. As compared to customary drop-casting method used to modify electrode surface, electrospun fibers score more points. This is the starting point of this research, modifying electrode structure using electrospinning. Nanofibers enable porous structure which lead to high surface to volume ratio. Apart from that, nanofibers allow diffusion of analytes with minimal resistance and improve electron transfer by having great capacity for electron to transport. However, little attempt is made to study the correlation between the effect of electrospinning solution parameter on fiber morphology and how the fiber morphology difference affect the performance of sensor. From this perspective, the first part of this thesis focused on the manipulation of electrospinning solution concentration and resulted electrospun fiber morphology. The polymer used for the first part of this research was polyacrylic acid (PAA). Understanding the electrospun fiber morphology effect on its conductivity enables the correct PAA concentration selection to ensure the best sensor performance. PAA electrospun fiber was not viable to be directly applied for sensor application as the fiber structure cannot be retained if immersed in water. Thus, PAN solution at 9.5 wt% is introduced to optimal 6% (wt) PAA solution prior to electrospinning to render the fiber from insoluble in water. Three volume ratios of PAA/PAN were manipulated to select appropriate formulation for the best conductivity. The results showed that PAA/PAN at ratio 6:4 has the best conductivity. The noble metal gold in nano-sized (AuNPs) was employed in this research to increase the sensing element. The performance of sensor is related to surface area for analyte to adhere at active site. The electrochemically active surface area (ECSA) of an electrode is highly dependent on the nano-structured particles to generate high currents. Thus, adoption of AuNPs increased the sensitivity of sensor as it creates better electron transfer media and add more active sites. An electrochemical sensor consisting of a screen-printed carbon electrode (SPCE) modified with electrospun polyacrylic acid/ polyacrylonitrile and AuNPs (PAA/PAN/AuNPs) was developed for the non-enzymatic determination of glucose. To achieve the optimal electrocatalytic oxidation of glucose, the pH, deposition potential and deposition time were optimized using differential pulse voltammetry (DPV). Under the optimal conditions; pH:10, deposition potential: -0.35 V and deposition potential: 210 s calibration curves were made at which the sensor had a detection limit of 1.52 μM, sensitivity of 1071.1 μA cm-2 mM-1. Two linear ranges which are 2 to 10 Mμ and 2 mM to 16 mM were constructed. The modification made the device compact, low cost and reliable non-enzymatic glucose sensor. The modified SPCE was successfully used for the sensing of glucose. |
---|