The characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / Siti Nurzatul Ikma Omar

The characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / Siti Nurzatul Ikma Omar

This thesis reports the synthesis, characterisation as well as antibacterial activity of polyaniline (PANI) embedded in polyester fabric (PES) and cotton fabric (COT). The objective of this study is to determine the chemical, morphological, and electrical properties of phytic acid doped PANI fabric...

Full description

Saved in:
Bibliographic Details
Main Author: Omar, Siti Nurzatul Ikma
Format: Thesis
Language:English
Published: 2021
Subjects:
Textile fabrics
Online Access:https://ir.uitm.edu.my/id/eprint/60462/1/60462.pdf
Tags: Add Tag
No Tags, Be the first to tag this record!
id my-uitm-ir.60462
record_format uketd_dc
spelling my-uitm-ir.604622022-05-30T01:29:59Z The characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / Siti Nurzatul Ikma Omar 2021-09 Omar, Siti Nurzatul Ikma Textile fabrics This thesis reports the synthesis, characterisation as well as antibacterial activity of polyaniline (PANI) embedded in polyester fabric (PES) and cotton fabric (COT). The objective of this study is to determine the chemical, morphological, and electrical properties of phytic acid doped PANI fabric by using Fourier Transform Infrared (FTIR), X-ray Fluorescence (XRF), Field Emission Scanning Electron Microscope (FESEM), and Electrical Impedance Spectroscopy (EIS), respectively, and to evaluate the antibacterial activity of PANI fabric. PANI was successfully synthesised by a chemical oxidation method where three reactants were employed: aniline, hydrochloric acid (HCl), and ammonium persulphate. The synthesis PANI was then doped with phytic acid, which acted as a doping agent to induce conductivity. The concentration of phytic acid was varied between 10v/v%, 20 v/v/%, and 30 v/v/% to investigate the effect on conductivity activity of different doping levels of phytic acid. The fabricated fabrics were produced via immersion technique with 30 minutes and 24 hours of different immersion times. PANI fabrics were successfully embedded and characterised through FTIR, XRF, FESEM and EIS. The FTIR study affirmed that PANI was successfully synthesised, doped, and fabricated on fabrics with the present functional group of C-N observed in both fabrics. XRF determined the level of doping of phytic acid in PANI. This analysis proved that PANI was successfully doped with phytic acid in the presence of element phosphate (P2O5). The percentage composition of element P2O5 that was identified was increased as the percentage of phytic acid that was used was increased. The morphology study of PANI fabric showed that all the PANI fabric was evenly deposited with PANI particles. The coating presents flaky and globular morphology. The conductivity of PANI fabrics was determined by using EIS. From this study, PANI PES fabric with 30-minute time immersion showed the highest conductivity value with 2.15 x 10-2 ± 3.87 x 10-3 Sm-1. The optimum concentration of phytic acid was 30v/v% with 30 minutes of optimum time immersion. The PES fabric was the best candidate as a substrate compared to the COT fabric. The agar disc diffusion method was used against six bacteria strains, which were Klebsiella pneumoniae (K.pneumoniae), Staphylococcus aureus (S.aureus), Escherichia coli (E.coli), Serratia marcescens (S.marcescens), Bacillus cereus (B.cereus) and Bacillus subtilis (B.subtilis). This study showed inhibition zones around PANI fabrics, which proved that PANI fabrics were competent against bacteria strains. The most significant inhibition zone for PANI fabric against the bacterial strain is 10.3 ± 0.5 mm, which occurred when PANI coated onto PES fabric at a concentration of 30 v/v% against K.pneumaniae with 30 minutes of immersion. Lastly, PANI fabrics were tested for their stability in the base environment by immersion in tap water for 30 minutes and 24 hours. The results showed that both fabrics did not change their colour, proving that this PANI fabric doped with phytic acid can retain its conductivity state, emeraldine salt state. It can be concluded from this study that PANI has proven potent conductive and antibacterial properties by doping it with phytic acid. Phytic acid is the best candidate for doping agent as this acid is stable enough to prevent the charge carrier of PANI from leaching out when exposed to an alkaline environment. The PANI fabric is conductive when exposed to alkaline, specifically tap water; hence, this fabric can be used in bio-inspired applications operating at high pH and can be cleaned and washed. 2021-09 Thesis https://ir.uitm.edu.my/id/eprint/60462/ https://ir.uitm.edu.my/id/eprint/60462/1/60462.pdf text en public masters Universiti Teknologi MARA Faculty of Applied Sciences Mahat, Mohd Muzamir (Dr.)
institution Universiti Teknologi MARA
collection UiTM Institutional Repository
language English
advisor Mahat, Mohd Muzamir (Dr.)
topic Textile fabrics
spellingShingle Textile fabrics
Omar, Siti Nurzatul Ikma
The characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / Siti Nurzatul Ikma Omar
description This thesis reports the synthesis, characterisation as well as antibacterial activity of polyaniline (PANI) embedded in polyester fabric (PES) and cotton fabric (COT). The objective of this study is to determine the chemical, morphological, and electrical properties of phytic acid doped PANI fabric by using Fourier Transform Infrared (FTIR), X-ray Fluorescence (XRF), Field Emission Scanning Electron Microscope (FESEM), and Electrical Impedance Spectroscopy (EIS), respectively, and to evaluate the antibacterial activity of PANI fabric. PANI was successfully synthesised by a chemical oxidation method where three reactants were employed: aniline, hydrochloric acid (HCl), and ammonium persulphate. The synthesis PANI was then doped with phytic acid, which acted as a doping agent to induce conductivity. The concentration of phytic acid was varied between 10v/v%, 20 v/v/%, and 30 v/v/% to investigate the effect on conductivity activity of different doping levels of phytic acid. The fabricated fabrics were produced via immersion technique with 30 minutes and 24 hours of different immersion times. PANI fabrics were successfully embedded and characterised through FTIR, XRF, FESEM and EIS. The FTIR study affirmed that PANI was successfully synthesised, doped, and fabricated on fabrics with the present functional group of C-N observed in both fabrics. XRF determined the level of doping of phytic acid in PANI. This analysis proved that PANI was successfully doped with phytic acid in the presence of element phosphate (P2O5). The percentage composition of element P2O5 that was identified was increased as the percentage of phytic acid that was used was increased. The morphology study of PANI fabric showed that all the PANI fabric was evenly deposited with PANI particles. The coating presents flaky and globular morphology. The conductivity of PANI fabrics was determined by using EIS. From this study, PANI PES fabric with 30-minute time immersion showed the highest conductivity value with 2.15 x 10-2 ± 3.87 x 10-3 Sm-1. The optimum concentration of phytic acid was 30v/v% with 30 minutes of optimum time immersion. The PES fabric was the best candidate as a substrate compared to the COT fabric. The agar disc diffusion method was used against six bacteria strains, which were Klebsiella pneumoniae (K.pneumoniae), Staphylococcus aureus (S.aureus), Escherichia coli (E.coli), Serratia marcescens (S.marcescens), Bacillus cereus (B.cereus) and Bacillus subtilis (B.subtilis). This study showed inhibition zones around PANI fabrics, which proved that PANI fabrics were competent against bacteria strains. The most significant inhibition zone for PANI fabric against the bacterial strain is 10.3 ± 0.5 mm, which occurred when PANI coated onto PES fabric at a concentration of 30 v/v% against K.pneumaniae with 30 minutes of immersion. Lastly, PANI fabrics were tested for their stability in the base environment by immersion in tap water for 30 minutes and 24 hours. The results showed that both fabrics did not change their colour, proving that this PANI fabric doped with phytic acid can retain its conductivity state, emeraldine salt state. It can be concluded from this study that PANI has proven potent conductive and antibacterial properties by doping it with phytic acid. Phytic acid is the best candidate for doping agent as this acid is stable enough to prevent the charge carrier of PANI from leaching out when exposed to an alkaline environment. The PANI fabric is conductive when exposed to alkaline, specifically tap water; hence, this fabric can be used in bio-inspired applications operating at high pH and can be cleaned and washed.
format Thesis
qualification_level Master's degree
author Omar, Siti Nurzatul Ikma
author_facet Omar, Siti Nurzatul Ikma
author_sort Omar, Siti Nurzatul Ikma
title The characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / Siti Nurzatul Ikma Omar
title_short The characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / Siti Nurzatul Ikma Omar
title_full The characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / Siti Nurzatul Ikma Omar
title_fullStr The characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / Siti Nurzatul Ikma Omar
title_full_unstemmed The characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / Siti Nurzatul Ikma Omar
title_sort characterization of phytic acid-doped polyaniline embedded in fabrics for antibacterial applications / siti nurzatul ikma omar
granting_institution Universiti Teknologi MARA
granting_department Faculty of Applied Sciences
publishDate 2021
url https://ir.uitm.edu.my/id/eprint/60462/1/60462.pdf
_version_ 1783735130177667072

Similar Items