Synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / Mohd Iqbaldin Mohd Nayai

Reduced graphene oxide (rGO) was produced from sub-bituminous coal by using graphitization-activation process alongside with microwave heating system as a heating media in order to reduce the production time. The process was carried out by using FeCl3 and ZnCl as graphitizing and activating agents,...

Full description

Saved in:

Bibliographic Details
Main Author:	Mohd Nayai, Mohd Iqbaldin
Format:	Thesis
Language:	English
Published:	2020
Subjects:	Carbon disulfide Graphene Carbon
Online Access:	https://ir.uitm.edu.my/id/eprint/61107/1/61107.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.61107
record_format	uketd_dc
spelling	my-uitm-ir.611072022-06-08T02:01:36Z Synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / Mohd Iqbaldin Mohd Nayai 2020-11 Mohd Nayai, Mohd Iqbaldin Carbon disulfide. Graphene. Carbon Reduced graphene oxide (rGO) was produced from sub-bituminous coal by using graphitization-activation process alongside with microwave heating system as a heating media in order to reduce the production time. The process was carried out by using FeCl3 and ZnCl as graphitizing and activating agents, respectively. There are two parameters of microwave power levels and irradiation times were setup in order to study its effects on the production process. The power levels and irradiation times were setup in range of 600 to 1000 W and 10 to 30 minutes, respectively. The surface functional group and crystal structure were analyzed by using Fourier Transform Infrared (FTIR) and X-Ray Diffraction (XRD) spectroscopies, respectively. Meanwhile, Raman spectroscopy was used in order to analyse the defects, ordered and dis-ordered carbon of rGO produced. Further, the surface area and surface morphology of rGO produced were analyzed by using Bruneur Emmet Teller (BET) analysis, Scanning Electron Microscope (SEM) and Transition Electron Microscope (TEM), respectively. Specific capacitance value was determined by using Automatic Battery Cycler. G930 is rGO produced at power level and irradiation time of 900 W and 30 minutes, respectively was chosen as the most optimum product based on the results of FTIR, XRD and Raman spectroscopies, as well as product yield. G930 has two peaks at wavelength of 1083 and 1580 cm-1 of FTIR spectra assigned to C−O−H of stretching epoxy groups and C=C of skeletal vibration of graphene layers, respectively. XRD pattern of G930 has (002) peak at around 2θ = 26º which corresponding to the interlayer spacing of 0.35 nm. Based on Raman, the G930 has three band of D, G and 2D band at 1345, 1592 and 2800 cm-1, respectively with ID/IG ratio of 1.31. It was found that the rGO produced has high BET surface area and specific capacitance value of 1463.103 m2g-1 and 253.42 Fg-1, respectively with 48 % of product yield. SEM and TEM analyses shows that the rGO produced has a very good porous structure consists of multilayer graphene. Thus, it can be concluded that the graphitization-activation method has successfully produced a good quality of rGO from coal in a single step process, as well as reduced the production time. The rGO produced also was found to have a good potential to become as an electrode material for supercapacitor due to its high specific capacitance value. 2020-11 Thesis https://ir.uitm.edu.my/id/eprint/61107/ https://ir.uitm.edu.my/id/eprint/61107/1/61107.pdf text en public phd doctoral Universiti Teknologi MARA Faculty of Applied Sciences Ismail, Khudzir (Professor Dr.)
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
advisor	Ismail, Khudzir (Professor Dr.)
topic	Carbon disulfide Graphene Carbon
spellingShingle	Carbon disulfide Graphene Carbon Mohd Nayai, Mohd Iqbaldin Synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / Mohd Iqbaldin Mohd Nayai
description	Reduced graphene oxide (rGO) was produced from sub-bituminous coal by using graphitization-activation process alongside with microwave heating system as a heating media in order to reduce the production time. The process was carried out by using FeCl3 and ZnCl as graphitizing and activating agents, respectively. There are two parameters of microwave power levels and irradiation times were setup in order to study its effects on the production process. The power levels and irradiation times were setup in range of 600 to 1000 W and 10 to 30 minutes, respectively. The surface functional group and crystal structure were analyzed by using Fourier Transform Infrared (FTIR) and X-Ray Diffraction (XRD) spectroscopies, respectively. Meanwhile, Raman spectroscopy was used in order to analyse the defects, ordered and dis-ordered carbon of rGO produced. Further, the surface area and surface morphology of rGO produced were analyzed by using Bruneur Emmet Teller (BET) analysis, Scanning Electron Microscope (SEM) and Transition Electron Microscope (TEM), respectively. Specific capacitance value was determined by using Automatic Battery Cycler. G930 is rGO produced at power level and irradiation time of 900 W and 30 minutes, respectively was chosen as the most optimum product based on the results of FTIR, XRD and Raman spectroscopies, as well as product yield. G930 has two peaks at wavelength of 1083 and 1580 cm-1 of FTIR spectra assigned to C−O−H of stretching epoxy groups and C=C of skeletal vibration of graphene layers, respectively. XRD pattern of G930 has (002) peak at around 2θ = 26º which corresponding to the interlayer spacing of 0.35 nm. Based on Raman, the G930 has three band of D, G and 2D band at 1345, 1592 and 2800 cm-1, respectively with ID/IG ratio of 1.31. It was found that the rGO produced has high BET surface area and specific capacitance value of 1463.103 m2g-1 and 253.42 Fg-1, respectively with 48 % of product yield. SEM and TEM analyses shows that the rGO produced has a very good porous structure consists of multilayer graphene. Thus, it can be concluded that the graphitization-activation method has successfully produced a good quality of rGO from coal in a single step process, as well as reduced the production time. The rGO produced also was found to have a good potential to become as an electrode material for supercapacitor due to its high specific capacitance value.
format	Thesis
qualification_name	Doctor of Philosophy (PhD.)
qualification_level	Doctorate
author	Mohd Nayai, Mohd Iqbaldin
author_facet	Mohd Nayai, Mohd Iqbaldin
author_sort	Mohd Nayai, Mohd Iqbaldin
title	Synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / Mohd Iqbaldin Mohd Nayai
title_short	Synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / Mohd Iqbaldin Mohd Nayai
title_full	Synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / Mohd Iqbaldin Mohd Nayai
title_fullStr	Synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / Mohd Iqbaldin Mohd Nayai
title_full_unstemmed	Synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / Mohd Iqbaldin Mohd Nayai
title_sort	synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / mohd iqbaldin mohd nayai
granting_institution	Universiti Teknologi MARA
granting_department	Faculty of Applied Sciences
publishDate	2020
url	https://ir.uitm.edu.my/id/eprint/61107/1/61107.pdf
_version_	1783735213290946560

Synthesis of reduced graphene oxide from sub-bituminous coal using one step processing and microwave heating system / Mohd Iqbaldin Mohd Nayai

Similar Items