Development of rice straw hemicellulose based biocomposite films / Nur Hazlilla Zulyadi

Biocomposites film has gained significant attention due to their potential applications in various fields of materials science. In recent years, biocomposite films have been seen as viable alternatives for existing petroleum-based plastic for food packaging. Hemicellulose based film has received rec...

Full description

Saved in:

Bibliographic Details
Main Author:	Zulyadi, Nur Hazlilla
Format:	Thesis
Language:	English
Published:	2021
Subjects:	Films Foils
Online Access:	https://ir.uitm.edu.my/id/eprint/61112/1/61112.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.61112
record_format	uketd_dc
spelling	my-uitm-ir.611122022-06-08T02:29:41Z Development of rice straw hemicellulose based biocomposite films / Nur Hazlilla Zulyadi 2021-11 Zulyadi, Nur Hazlilla Films. Foils Biocomposites film has gained significant attention due to their potential applications in various fields of materials science. In recent years, biocomposite films have been seen as viable alternatives for existing petroleum-based plastic for food packaging. Hemicellulose based film has received recognition in food packaging applications due to their excellent film-forming capabilities and biodegradability. However, unmodified hemicellulose films are brittle, hydrophilic, sensitive towards water, and often show poor mechanical properties such as tensile strength which limit their applications. To overcome this issue, citric acid (CA) and Montmorillonite (MMT) were incorporated into hemicellulose films. The aim of this study was to develop hemicellulose, CA, and MMT biocomposite films from rice straw. Then the development of hemicellulose films was used for cherry tomatoes packaging application study. Hemicellulose was extracted from rice straw using alkaline extraction. The effects of different temperature (45°, 55°C, 65°C), NaOH concentrations (0.25M, 0.5M, 1M), and pH (4.5, 5.5, 6.5) on the hemicellulose yield was studied. The obtained hemicellulose was then used to develop hemicellulose film using casting method. CA was incorporated into hemicellulose film and designated as hemicellulose, citric acid (HCA) biocomposite film. Then MMT was incorporated into HCA biocomposite film and designated as HMMT. The appropriate composition of the films was prepared by varying the amounts of hemicellulose, CA, and MMT. The biocomposite film was characterized based on their water vapour permeability (WVP), water vapour transfer rate (WVTR), moisture content, solubility, thermal stability and tensile strength. Furthermore, the inhibitory effect and changes in physical properties (hardness, firmness, colour changes and weight changes) of cherry tomatoes packaged with HMMT biocompiste films were examined. The result showed that the highest yield of hemicellulose was 19.88% at 55°C, 5.5 pH and 1M NaOH. The addition of CA into the hemicellulose film revealed that the film was more stable, less brittle and also enhance the water barrier properties. The addition of 10% CA resulted in the highest values of WVP (10.15 x 10-5 g m-1 Pa-1 s-1) and WVTR (26.25 g m-2 s-1) as well as improved the thermal stability and tensile strength of the films. This indicated that HCA10 was found to be suitable for food packaging application. Increasing MMT ratio in hemicellulose biocomposite films has lowered the WVP and WVTR values, moisture content and solubility, however the thermal stability and tensile strength of the films were improved. The addition of MMT also imparted on the inhibitory effects towards E.coli growth. HMMT0.5, HMMT1 and HMMT2 films showed higher values of hardness, firmness and lower weight loss compared to unpackaged cherry tomatoes. HMMT1 packaging films with high WVP (5.6 x10-6 g m-1 Pa-1 s-1) and high WVTR (1.75 g m-2 s-1) values had the highest value of hardness (386N), firmness (3278N) and lowest weight loss of cherry tomatoes (7.07%) after 10 days of storage at room temperature (25°C). Therefore, it can be concluded that rice straw hemicellulose biocomposite film was successfully developed and HMMT1 biocomposite film shows promising suitability to preserve and extend the shelf life of cherry tomatoes. 2021-11 Thesis https://ir.uitm.edu.my/id/eprint/61112/ https://ir.uitm.edu.my/id/eprint/61112/1/61112.pdf text en public phd doctoral Universiti Teknologi MARA Faculty of Applied Sciences Saleh, Sabiha Hanim (Assoc. Prof. Dr.)
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
advisor	Saleh, Sabiha Hanim (Assoc. Prof. Dr.)
topic	Films Foils
spellingShingle	Films Foils Zulyadi, Nur Hazlilla Development of rice straw hemicellulose based biocomposite films / Nur Hazlilla Zulyadi
description	Biocomposites film has gained significant attention due to their potential applications in various fields of materials science. In recent years, biocomposite films have been seen as viable alternatives for existing petroleum-based plastic for food packaging. Hemicellulose based film has received recognition in food packaging applications due to their excellent film-forming capabilities and biodegradability. However, unmodified hemicellulose films are brittle, hydrophilic, sensitive towards water, and often show poor mechanical properties such as tensile strength which limit their applications. To overcome this issue, citric acid (CA) and Montmorillonite (MMT) were incorporated into hemicellulose films. The aim of this study was to develop hemicellulose, CA, and MMT biocomposite films from rice straw. Then the development of hemicellulose films was used for cherry tomatoes packaging application study. Hemicellulose was extracted from rice straw using alkaline extraction. The effects of different temperature (45°, 55°C, 65°C), NaOH concentrations (0.25M, 0.5M, 1M), and pH (4.5, 5.5, 6.5) on the hemicellulose yield was studied. The obtained hemicellulose was then used to develop hemicellulose film using casting method. CA was incorporated into hemicellulose film and designated as hemicellulose, citric acid (HCA) biocomposite film. Then MMT was incorporated into HCA biocomposite film and designated as HMMT. The appropriate composition of the films was prepared by varying the amounts of hemicellulose, CA, and MMT. The biocomposite film was characterized based on their water vapour permeability (WVP), water vapour transfer rate (WVTR), moisture content, solubility, thermal stability and tensile strength. Furthermore, the inhibitory effect and changes in physical properties (hardness, firmness, colour changes and weight changes) of cherry tomatoes packaged with HMMT biocompiste films were examined. The result showed that the highest yield of hemicellulose was 19.88% at 55°C, 5.5 pH and 1M NaOH. The addition of CA into the hemicellulose film revealed that the film was more stable, less brittle and also enhance the water barrier properties. The addition of 10% CA resulted in the highest values of WVP (10.15 x 10-5 g m-1 Pa-1 s-1) and WVTR (26.25 g m-2 s-1) as well as improved the thermal stability and tensile strength of the films. This indicated that HCA10 was found to be suitable for food packaging application. Increasing MMT ratio in hemicellulose biocomposite films has lowered the WVP and WVTR values, moisture content and solubility, however the thermal stability and tensile strength of the films were improved. The addition of MMT also imparted on the inhibitory effects towards E.coli growth. HMMT0.5, HMMT1 and HMMT2 films showed higher values of hardness, firmness and lower weight loss compared to unpackaged cherry tomatoes. HMMT1 packaging films with high WVP (5.6 x10-6 g m-1 Pa-1 s-1) and high WVTR (1.75 g m-2 s-1) values had the highest value of hardness (386N), firmness (3278N) and lowest weight loss of cherry tomatoes (7.07%) after 10 days of storage at room temperature (25°C). Therefore, it can be concluded that rice straw hemicellulose biocomposite film was successfully developed and HMMT1 biocomposite film shows promising suitability to preserve and extend the shelf life of cherry tomatoes.
format	Thesis
qualification_name	Doctor of Philosophy (PhD.)
qualification_level	Doctorate
author	Zulyadi, Nur Hazlilla
author_facet	Zulyadi, Nur Hazlilla
author_sort	Zulyadi, Nur Hazlilla
title	Development of rice straw hemicellulose based biocomposite films / Nur Hazlilla Zulyadi
title_short	Development of rice straw hemicellulose based biocomposite films / Nur Hazlilla Zulyadi
title_full	Development of rice straw hemicellulose based biocomposite films / Nur Hazlilla Zulyadi
title_fullStr	Development of rice straw hemicellulose based biocomposite films / Nur Hazlilla Zulyadi
title_full_unstemmed	Development of rice straw hemicellulose based biocomposite films / Nur Hazlilla Zulyadi
title_sort	development of rice straw hemicellulose based biocomposite films / nur hazlilla zulyadi
granting_institution	Universiti Teknologi MARA
granting_department	Faculty of Applied Sciences
publishDate	2021
url	https://ir.uitm.edu.my/id/eprint/61112/1/61112.pdf
_version_	1783735214711767040

Development of rice straw hemicellulose based biocomposite films / Nur Hazlilla Zulyadi

Similar Items