Sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / Siti Shafura A Karim

This study aimed to fabricate nano structured zinc oxide (ZnO) based metal semiconductor- metal (MSM) gas sensor by immersion method. Three stages of method were employed to fabricate nanostructured ZnO based MSM gas sensor which are: (1) preparation of ZnO nano-template by spin-coating method, (2)...

Full description

Saved in:

Bibliographic Details
Main Author:	A Karim, Siti Shafura
Format:	Thesis
Language:	English
Published:	2018
Subjects:	Chemical engineering
Online Access:	https://ir.uitm.edu.my/id/eprint/62943/1/62943.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.62943
record_format	uketd_dc
spelling	my-uitm-ir.629432022-08-11T04:13:09Z Sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / Siti Shafura A Karim 2018-03 A Karim, Siti Shafura Chemical engineering This study aimed to fabricate nano structured zinc oxide (ZnO) based metal semiconductor- metal (MSM) gas sensor by immersion method. Three stages of method were employed to fabricate nanostructured ZnO based MSM gas sensor which are: (1) preparation of ZnO nano-template by spin-coating method, (2) preparation of nanostructured ZnO on deposited ZnO nano-template layer by immersion method and (3) fabrication of nano structured ZnO based MSM gas sensor. For preparation of ZnO nano-template by spin-coating method, both effects of multilayer coating (1 to 9 layers) and annealing temperature (350 to 500°C) of ZnO nano-template were determined. The optimised properties of deposited ZnO nano-template was further employed as a seed layer to grow nano structured ZnO by immersion method. For preparation of nanostructured ZnO on deposited ZnO nano-template layer by immersion method, effect of molarity (0.02 to 0.10 M) and effect of n-type dopant (Sn) concentration (0.2 to 1.0 at.%) on nanostructured ZnO were evaluated. Field emission scanning electron microscope (FESEM), energy dispersive X-ray (EDS), atomic force microscopy (AFM) and X-ray diffraction (XRD) were employed to characterise the structural properties of deposited samples whereby UV-Vis-NIR spectrophotometer was used for the optical properties determination. The electrical properties were measured using current-voltage (I-V) measurement system (Keithley 2400). Next, gold (Au) was deposited on the nanostructured ZnO as an electrode for the fabrication of nanostructured ZnO based MSM gas sensor. The entire samples were characterised to determine their response and recovery time as well as the sensitivity. The sensitivity behavior of the fabricated samples were determined to detect 20 seem of methane (CH4) gas at operating temperature of 150°C. In preparation of ZnO nano-template by spin-coating method, the results revealed that 5 layers demonstrated a high uniformity with no crack and high electrical conductivity (l.lxlO"3 S/cm). Additionally, 500°C has emerged as an optimum temperature upon increment of annealing temperatures. During preparation of nanostructured ZnO on deposited ZnO nano-template layer by immersion method, unique nanostructure (flake-like morphologies) was observed upon the study of molarity effect on nanostructured ZnO (0.02-0.10 M). The electrical conductivity was obtained around 10"3 S/cm, which is comparable to previous reported studies. The optimum concentration at 0.06 M has exhibited a good uniformity with low roughness and the highest conductivity of 3.3x10"3 S/cm. The effect of n-type dopant (Sn) concentration (0.2-1.0 at.%) has been investigated. The width of flakes have slightly decreased from 64.1 to 41.9 nm as the n-type dopant (Sn) concentration increased. Increasing the ntype dopant (Sn) concentration has greatly enhanced the electrical conductivity from 6.5xl0"3 to 12.6xl0"3 S/cm. The highest sensitivity was achieved at 23% with utilisation of 1.0 at.%. The response and recovery time of 1.0 at.% were 46 and 64 s, respectively. Through this research work, the optimum preparation parameters were successfully identified for fabrication of nanostructured ZnO based MSM gas sensor. This work provides an opportunity to explore potential material for the development of gas sensor. 2018-03 Thesis https://ir.uitm.edu.my/id/eprint/62943/ https://ir.uitm.edu.my/id/eprint/62943/1/62943.pdf text en public masters Universiti Teknologi MARA Faculty of Electrical Engineering Mahmood, Mohamad Rusop (Prof. Dr.)
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
advisor	Mahmood, Mohamad Rusop (Prof. Dr.)
topic	Chemical engineering
spellingShingle	Chemical engineering A Karim, Siti Shafura Sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / Siti Shafura A Karim
description	This study aimed to fabricate nano structured zinc oxide (ZnO) based metal semiconductor- metal (MSM) gas sensor by immersion method. Three stages of method were employed to fabricate nanostructured ZnO based MSM gas sensor which are: (1) preparation of ZnO nano-template by spin-coating method, (2) preparation of nanostructured ZnO on deposited ZnO nano-template layer by immersion method and (3) fabrication of nano structured ZnO based MSM gas sensor. For preparation of ZnO nano-template by spin-coating method, both effects of multilayer coating (1 to 9 layers) and annealing temperature (350 to 500°C) of ZnO nano-template were determined. The optimised properties of deposited ZnO nano-template was further employed as a seed layer to grow nano structured ZnO by immersion method. For preparation of nanostructured ZnO on deposited ZnO nano-template layer by immersion method, effect of molarity (0.02 to 0.10 M) and effect of n-type dopant (Sn) concentration (0.2 to 1.0 at.%) on nanostructured ZnO were evaluated. Field emission scanning electron microscope (FESEM), energy dispersive X-ray (EDS), atomic force microscopy (AFM) and X-ray diffraction (XRD) were employed to characterise the structural properties of deposited samples whereby UV-Vis-NIR spectrophotometer was used for the optical properties determination. The electrical properties were measured using current-voltage (I-V) measurement system (Keithley 2400). Next, gold (Au) was deposited on the nanostructured ZnO as an electrode for the fabrication of nanostructured ZnO based MSM gas sensor. The entire samples were characterised to determine their response and recovery time as well as the sensitivity. The sensitivity behavior of the fabricated samples were determined to detect 20 seem of methane (CH4) gas at operating temperature of 150°C. In preparation of ZnO nano-template by spin-coating method, the results revealed that 5 layers demonstrated a high uniformity with no crack and high electrical conductivity (l.lxlO"3 S/cm). Additionally, 500°C has emerged as an optimum temperature upon increment of annealing temperatures. During preparation of nanostructured ZnO on deposited ZnO nano-template layer by immersion method, unique nanostructure (flake-like morphologies) was observed upon the study of molarity effect on nanostructured ZnO (0.02-0.10 M). The electrical conductivity was obtained around 10"3 S/cm, which is comparable to previous reported studies. The optimum concentration at 0.06 M has exhibited a good uniformity with low roughness and the highest conductivity of 3.3x10"3 S/cm. The effect of n-type dopant (Sn) concentration (0.2-1.0 at.%) has been investigated. The width of flakes have slightly decreased from 64.1 to 41.9 nm as the n-type dopant (Sn) concentration increased. Increasing the ntype dopant (Sn) concentration has greatly enhanced the electrical conductivity from 6.5xl0"3 to 12.6xl0"3 S/cm. The highest sensitivity was achieved at 23% with utilisation of 1.0 at.%. The response and recovery time of 1.0 at.% were 46 and 64 s, respectively. Through this research work, the optimum preparation parameters were successfully identified for fabrication of nanostructured ZnO based MSM gas sensor. This work provides an opportunity to explore potential material for the development of gas sensor.
format	Thesis
qualification_level	Master's degree
author	A Karim, Siti Shafura
author_facet	A Karim, Siti Shafura
author_sort	A Karim, Siti Shafura
title	Sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / Siti Shafura A Karim
title_short	Sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / Siti Shafura A Karim
title_full	Sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / Siti Shafura A Karim
title_fullStr	Sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / Siti Shafura A Karim
title_full_unstemmed	Sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / Siti Shafura A Karim
title_sort	sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / siti shafura a karim
granting_institution	Universiti Teknologi MARA
granting_department	Faculty of Electrical Engineering
publishDate	2018
url	https://ir.uitm.edu.my/id/eprint/62943/1/62943.pdf
_version_	1783735279683633152

Sensitivity behavior of nano structured zinc oxide based gas sensor fabricated by immersion method / Siti Shafura A Karim

Similar Items