A study on the effect of mechanical properties and rheologycal behaviour of polyproplene reinforced montmorillonite / Normuhaizah Mohd Zain
This research focused on the mechanical properties of polypropylene (PP) reinforced montmorillonite (MMT). The aim of this research is to determine the mechanical properties of PP/MMT nanocomposite with different concentration (2 wt%, 4 wt%, 6 wt% , 8 wt% and 10 wt%) of MMT. PP and MMT were mix by u...
محفوظ في:
| المؤلف الرئيسي: | |
|---|---|
| التنسيق: | أطروحة |
| اللغة: | English |
| منشور في: |
2010
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://ir.uitm.edu.my/id/eprint/64049/1/64049.pdf |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | This research focused on the mechanical properties of polypropylene (PP) reinforced montmorillonite (MMT). The aim of this research is to determine the mechanical properties of PP/MMT nanocomposite with different concentration (2 wt%, 4 wt%, 6 wt% , 8 wt% and 10 wt%) of MMT. PP and MMT were mix by using Dispersion Mixer. The material was mixed at temperature 190°C. After that, the material was fabricated by using hot press with 190°C for both upper and lower compressor. Mechanical properties of the sample were evaluated by tensile test, impact test, and three-point bending test according to BS EN ISO 527, BS EN 60811 and BS 6319 respectively. From the tensile test, the result obtained shown that the sample of 2wt.% and for impact test shown 6wt.% of clay loading which has the better mechanical properties. The rheological behavior also determined. All the concentration have pseudoplastic, but the better pseudoplastic is 8wt.% of loading clay. |
|---|