Development of palm olein as a corrosion inhibitor for aluminium alloy / Junaidah Jai

Aluminium (Al) is an amazing material due to its low cost, lightweight and corrosion resistance. However, Al is easily corroded when exposed in solution containing pitting agents. Suitable corrosion inhibitor should be used and palm olein has a promising characteristics. For this work, formulation o...

Full description

Saved in:

Bibliographic Details
Main Author:	Jai, Junaidah
Format:	Thesis
Language:	English
Published:	2010
Subjects:	Corrosion and anti-corrosives Metallurgy
Online Access:	https://ir.uitm.edu.my/id/eprint/65280/1/65280.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.65280
record_format	uketd_dc
spelling	my-uitm-ir.652802023-01-05T02:01:44Z Development of palm olein as a corrosion inhibitor for aluminium alloy / Junaidah Jai 2010 Jai, Junaidah Corrosion and anti-corrosives Metallurgy Aluminium (Al) is an amazing material due to its low cost, lightweight and corrosion resistance. However, Al is easily corroded when exposed in solution containing pitting agents. Suitable corrosion inhibitor should be used and palm olein has a promising characteristics. For this work, formulation of palm olein (PO) as corrosion inhibitor for Al in aqueous solution was developed. Tween 20, hexane and diethyl triamine were used as the additives and the formulated inhibitor was labeled as POT20HA. The X-ray diffractometer (XRD) spectrum revealed that the POT20HA was an amide compound. The inhibition efficiency (IE) and behaviour of the POT20HA were determined through weight loss (WL), potentiodynamic polarization (PP) and electrochemical impedance spectroscopy (EIS). For the tests, Al 6061 was immersed in 1 M HC1 solution at different temperatures of 26°C (299 K), 50°C (323 K) and 70°C (343 K) with different concentrations of POT20HA of 0, 0.03, 0.07, 0.10, 0.13 and 0.17 M. Scanning Electron Microscopy (SEM) coupled with Energy Dispersion X-ray analysis (EDAX) was used to examine the morphology of the corroded Al 6061. The WL test had shown that the IE increased with increasing concentration of POT20HA at all temperatures under study. However, the IE decreased with increasing of temperature and immersion time. The PP study revealed the POT20HA as a mixed type of inhibitor, which is capable of protecting both the anodic and cathodic reactions of the corrosion process. The EIS study had shown the ability of POT20HA in forming protective passive film on Al 6061 surface. The thickness of the passive film increased accordingly with the increase in concentration but decreased with increasing temperature. The corrosion tests showed that POT20HA adsorbed on the Al 6061 surface through physical adsorption according to the Langmuir isotherm relationship. The adsorption mechanism of POT20HA on the Al 6061 was through protonation of micelles by the HC1 solution. The protonated micelles, with the presence of CI" ions, adsorbed both on the cathodic and anodic sides of the corroding surface. Performance test had shown that the POT20HA has performed as an anticorrosion with glycerin as a coolant in an Al car radiator. 2010 Thesis https://ir.uitm.edu.my/id/eprint/65280/ https://ir.uitm.edu.my/id/eprint/65280/1/65280.pdf text en public phd doctoral Universiti Teknologi MARA (UiTM) Faculty of Chemical Engineering Wan Ali, Wan Shabuddin
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
advisor	Wan Ali, Wan Shabuddin
topic	Corrosion and anti-corrosives Metallurgy
spellingShingle	Corrosion and anti-corrosives Metallurgy Jai, Junaidah Development of palm olein as a corrosion inhibitor for aluminium alloy / Junaidah Jai
description	Aluminium (Al) is an amazing material due to its low cost, lightweight and corrosion resistance. However, Al is easily corroded when exposed in solution containing pitting agents. Suitable corrosion inhibitor should be used and palm olein has a promising characteristics. For this work, formulation of palm olein (PO) as corrosion inhibitor for Al in aqueous solution was developed. Tween 20, hexane and diethyl triamine were used as the additives and the formulated inhibitor was labeled as POT20HA. The X-ray diffractometer (XRD) spectrum revealed that the POT20HA was an amide compound. The inhibition efficiency (IE) and behaviour of the POT20HA were determined through weight loss (WL), potentiodynamic polarization (PP) and electrochemical impedance spectroscopy (EIS). For the tests, Al 6061 was immersed in 1 M HC1 solution at different temperatures of 26°C (299 K), 50°C (323 K) and 70°C (343 K) with different concentrations of POT20HA of 0, 0.03, 0.07, 0.10, 0.13 and 0.17 M. Scanning Electron Microscopy (SEM) coupled with Energy Dispersion X-ray analysis (EDAX) was used to examine the morphology of the corroded Al 6061. The WL test had shown that the IE increased with increasing concentration of POT20HA at all temperatures under study. However, the IE decreased with increasing of temperature and immersion time. The PP study revealed the POT20HA as a mixed type of inhibitor, which is capable of protecting both the anodic and cathodic reactions of the corrosion process. The EIS study had shown the ability of POT20HA in forming protective passive film on Al 6061 surface. The thickness of the passive film increased accordingly with the increase in concentration but decreased with increasing temperature. The corrosion tests showed that POT20HA adsorbed on the Al 6061 surface through physical adsorption according to the Langmuir isotherm relationship. The adsorption mechanism of POT20HA on the Al 6061 was through protonation of micelles by the HC1 solution. The protonated micelles, with the presence of CI" ions, adsorbed both on the cathodic and anodic sides of the corroding surface. Performance test had shown that the POT20HA has performed as an anticorrosion with glycerin as a coolant in an Al car radiator.
format	Thesis
qualification_name	Doctor of Philosophy (PhD.)
qualification_level	Doctorate
author	Jai, Junaidah
author_facet	Jai, Junaidah
author_sort	Jai, Junaidah
title	Development of palm olein as a corrosion inhibitor for aluminium alloy / Junaidah Jai
title_short	Development of palm olein as a corrosion inhibitor for aluminium alloy / Junaidah Jai
title_full	Development of palm olein as a corrosion inhibitor for aluminium alloy / Junaidah Jai
title_fullStr	Development of palm olein as a corrosion inhibitor for aluminium alloy / Junaidah Jai
title_full_unstemmed	Development of palm olein as a corrosion inhibitor for aluminium alloy / Junaidah Jai
title_sort	development of palm olein as a corrosion inhibitor for aluminium alloy / junaidah jai
granting_institution	Universiti Teknologi MARA (UiTM)
granting_department	Faculty of Chemical Engineering
publishDate	2010
url	https://ir.uitm.edu.my/id/eprint/65280/1/65280.pdf
_version_	1783735546715045888

Development of palm olein as a corrosion inhibitor for aluminium alloy / Junaidah Jai

Similar Items