Sodium silicate extraction from sugarcane bagasse ash (SCBA) via thermo chemical treatment for synthesis of Santa Barbara Amorphous-15 (SBA-15) / Norsuraya Sahiron

This study explores the potential of sugarcane bagasse ash (SCBA) as a precursor in the production of Santa Barbara Amorphous-15 (SBA-15) in order to determine the effect of temperature and time of the pyrolysis towards silica content. In this study the sugarcane bagasse (SCB) was pyrolysed at three...

Full description

Saved in:

Bibliographic Details
Main Author:	Sahiron, Norsuraya
Format:	Thesis
Language:	English
Published:	2018
Subjects:	Physical and theoretical chemistry
Online Access:	https://ir.uitm.edu.my/id/eprint/67509/1/67509.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.67509
record_format	uketd_dc
spelling	my-uitm-ir.675092023-03-06T08:31:55Z Sodium silicate extraction from sugarcane bagasse ash (SCBA) via thermo chemical treatment for synthesis of Santa Barbara Amorphous-15 (SBA-15) / Norsuraya Sahiron 2018 Sahiron, Norsuraya Physical and theoretical chemistry Gramineae (Grass). Bamboo This study explores the potential of sugarcane bagasse ash (SCBA) as a precursor in the production of Santa Barbara Amorphous-15 (SBA-15) in order to determine the effect of temperature and time of the pyrolysis towards silica content. In this study the sugarcane bagasse (SCB) was pyrolysed at three different temperatures which are 600°C, 800°C and 1000°C for 2 hours, 3 hours and 4 hours. The ash was then washed with hydrochloric acid (HC1) to remove impurities and characterised using X-ray fluorescence (XRF). The study indicates that the amount of silica in SCBA at 1000°C and 4 hours gave the highest silica content which is 88.13%. Next, the ash with the highest silica content was used in the extraction of sodium silicate (NaiSiOs) by using sodium hydroxide (NaOH). The formation of sodium silicate was characterised using Fourier Transform Infrared Spectroscopy (FTIR) and Inductive Coupled Plasma (ICP) to validate the silica content in the sodium silicate obtain. The FTIR pattern and ICP result has shown that the extracted sodium silicate gave a high silica concentration which is about 4873 ppm. Furthermore, the application, SBA-15 was synthesised using the extracted sodium silicate. Mesoporous silica, SBA-15 was prepared using extracted sodium silicate as the silica source and PI23 surfactant as the template. The SBA-15 formed was characterised using X-ray diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), Bruanauer-Emmett-Teller (BET) and Field Emission Scanning Electron Microscopy (FESEM). From the XRD analysis, SBA-15 obtained shows the characteristic of 2-D hexagonal mesoporous material at peak (100), (110), and (200) reflections associated to 2-D hexagonal with p6mm symmetry which indicate the mesoporous structure. The clear formed of mesoporous pore aligned uniformly. The pore dimensions estimated around 2.3 um to 781 nm with particle diameter approximately 80 nm to 251 nm, also with the large surface area, 466 m2/g. Therefore, mesoporous SBA-15 synthesised exhibited the similar morphology as commercial SBA-15. 2018 Thesis https://ir.uitm.edu.my/id/eprint/67509/ https://ir.uitm.edu.my/id/eprint/67509/1/67509.pdf text en public masters Universiti Teknologi MARA (UiTM) Faculty of Chemical Engineering Hamzah, Fazlena
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
advisor	Hamzah, Fazlena
topic	Physical and theoretical chemistry Physical and theoretical chemistry
spellingShingle	Physical and theoretical chemistry Physical and theoretical chemistry Sahiron, Norsuraya Sodium silicate extraction from sugarcane bagasse ash (SCBA) via thermo chemical treatment for synthesis of Santa Barbara Amorphous-15 (SBA-15) / Norsuraya Sahiron
description	This study explores the potential of sugarcane bagasse ash (SCBA) as a precursor in the production of Santa Barbara Amorphous-15 (SBA-15) in order to determine the effect of temperature and time of the pyrolysis towards silica content. In this study the sugarcane bagasse (SCB) was pyrolysed at three different temperatures which are 600°C, 800°C and 1000°C for 2 hours, 3 hours and 4 hours. The ash was then washed with hydrochloric acid (HC1) to remove impurities and characterised using X-ray fluorescence (XRF). The study indicates that the amount of silica in SCBA at 1000°C and 4 hours gave the highest silica content which is 88.13%. Next, the ash with the highest silica content was used in the extraction of sodium silicate (NaiSiOs) by using sodium hydroxide (NaOH). The formation of sodium silicate was characterised using Fourier Transform Infrared Spectroscopy (FTIR) and Inductive Coupled Plasma (ICP) to validate the silica content in the sodium silicate obtain. The FTIR pattern and ICP result has shown that the extracted sodium silicate gave a high silica concentration which is about 4873 ppm. Furthermore, the application, SBA-15 was synthesised using the extracted sodium silicate. Mesoporous silica, SBA-15 was prepared using extracted sodium silicate as the silica source and PI23 surfactant as the template. The SBA-15 formed was characterised using X-ray diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), Bruanauer-Emmett-Teller (BET) and Field Emission Scanning Electron Microscopy (FESEM). From the XRD analysis, SBA-15 obtained shows the characteristic of 2-D hexagonal mesoporous material at peak (100), (110), and (200) reflections associated to 2-D hexagonal with p6mm symmetry which indicate the mesoporous structure. The clear formed of mesoporous pore aligned uniformly. The pore dimensions estimated around 2.3 um to 781 nm with particle diameter approximately 80 nm to 251 nm, also with the large surface area, 466 m2/g. Therefore, mesoporous SBA-15 synthesised exhibited the similar morphology as commercial SBA-15.
format	Thesis
qualification_level	Master's degree
author	Sahiron, Norsuraya
author_facet	Sahiron, Norsuraya
author_sort	Sahiron, Norsuraya
title	Sodium silicate extraction from sugarcane bagasse ash (SCBA) via thermo chemical treatment for synthesis of Santa Barbara Amorphous-15 (SBA-15) / Norsuraya Sahiron
title_short	Sodium silicate extraction from sugarcane bagasse ash (SCBA) via thermo chemical treatment for synthesis of Santa Barbara Amorphous-15 (SBA-15) / Norsuraya Sahiron
title_full	Sodium silicate extraction from sugarcane bagasse ash (SCBA) via thermo chemical treatment for synthesis of Santa Barbara Amorphous-15 (SBA-15) / Norsuraya Sahiron
title_fullStr	Sodium silicate extraction from sugarcane bagasse ash (SCBA) via thermo chemical treatment for synthesis of Santa Barbara Amorphous-15 (SBA-15) / Norsuraya Sahiron
title_full_unstemmed	Sodium silicate extraction from sugarcane bagasse ash (SCBA) via thermo chemical treatment for synthesis of Santa Barbara Amorphous-15 (SBA-15) / Norsuraya Sahiron
title_sort	sodium silicate extraction from sugarcane bagasse ash (scba) via thermo chemical treatment for synthesis of santa barbara amorphous-15 (sba-15) / norsuraya sahiron
granting_institution	Universiti Teknologi MARA (UiTM)
granting_department	Faculty of Chemical Engineering
publishDate	2018
url	https://ir.uitm.edu.my/id/eprint/67509/1/67509.pdf
_version_	1783735692796362752

Sodium silicate extraction from sugarcane bagasse ash (SCBA) via thermo chemical treatment for synthesis of Santa Barbara Amorphous-15 (SBA-15) / Norsuraya Sahiron

Similar Items