Crystal clear thermal barrier coating of inorganic polysiloxane resin filled with titanium dioxide for glass coating application / Syahmina Athirah Saudi
This research develops transparent inorganic polysiloxane resin with Ti02 to allow certain light wavelength to transmit through coated glass. Epoxy silane and amino silane hardener were synthesised in different molar ratios. Each was tested for their viscosity using Brookfield Viscometer. Different...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English |
Published: |
2022
|
Subjects: | |
Online Access: | https://ir.uitm.edu.my/id/eprint/75758/1/75758.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my-uitm-ir.75758 |
---|---|
record_format |
uketd_dc |
spelling |
my-uitm-ir.757582023-03-31T01:52:32Z Crystal clear thermal barrier coating of inorganic polysiloxane resin filled with titanium dioxide for glass coating application / Syahmina Athirah Saudi 2022 Saudi, Syahmina Athirah Titanium dioxide This research develops transparent inorganic polysiloxane resin with Ti02 to allow certain light wavelength to transmit through coated glass. Epoxy silane and amino silane hardener were synthesised in different molar ratios. Each was tested for their viscosity using Brookfield Viscometer. Different viscosities were observed before reaching constant values which designates complete formations of amide linkages. Highest viscosity of 30.5 mPa/s was recorded. FTIR supported the viscosity result by proving the presence of amide linkages. Ti02 concentrations of 10%, 20% and 30% (w/v) in dehydrated ethanol were successfully dispersed using high-speed disperser. Dispersed Ti02 were characterized for size distribution and recorded 87 nm with value of 1 PDI. UV absorber of 2-hydroxybenzophenone (HBP) with boron (BF3) catalyst was formulated to aid in coating performance. The combined formulation of polysiloxane resin, HBP and BF3 gives fastest curing time of 60 minutes and was chosen as an ideal coating binder. Surface tension test supported the curing results. Smart coating (SC) formulations consist of ideal coating binder and Ti02 dispersion was coated on glass for pencil hardness analysis. 6H pencil grade was quoted as the hardest. SC's real-time measurement for UV, IR and daylight transmissions using WEP gives 0%, 10% and 61% of respectively. 2022 Thesis https://ir.uitm.edu.my/id/eprint/75758/ https://ir.uitm.edu.my/id/eprint/75758/1/75758.pdf text en public masters Universiti Teknologi MARA (UiTM) Faculty of Applied Sciences Mohd, Ahmad Faiza |
institution |
Universiti Teknologi MARA |
collection |
UiTM Institutional Repository |
language |
English |
advisor |
Mohd, Ahmad Faiza |
topic |
Titanium dioxide |
spellingShingle |
Titanium dioxide Saudi, Syahmina Athirah Crystal clear thermal barrier coating of inorganic polysiloxane resin filled with titanium dioxide for glass coating application / Syahmina Athirah Saudi |
description |
This research develops transparent inorganic polysiloxane resin with Ti02 to allow certain light wavelength to transmit through coated glass. Epoxy silane and amino silane hardener were synthesised in different molar ratios. Each was tested for their viscosity using Brookfield Viscometer. Different viscosities were observed before reaching constant values which designates complete formations of amide linkages. Highest viscosity of 30.5 mPa/s was recorded. FTIR supported the viscosity result by proving the presence of amide linkages. Ti02 concentrations of 10%, 20% and 30% (w/v) in dehydrated ethanol were successfully dispersed using high-speed disperser. Dispersed Ti02 were characterized for size distribution and recorded 87 nm with value of 1 PDI. UV absorber of 2-hydroxybenzophenone (HBP) with boron (BF3) catalyst was formulated to aid in coating performance. The combined formulation of polysiloxane resin, HBP and BF3 gives fastest curing time of 60 minutes and was chosen as an ideal coating binder. Surface tension test supported the curing results. Smart coating (SC) formulations consist of ideal coating binder and Ti02 dispersion was coated on glass for pencil hardness analysis. 6H pencil grade was quoted as the hardest. SC's real-time measurement for UV, IR and daylight transmissions using WEP gives 0%, 10% and 61% of respectively. |
format |
Thesis |
qualification_level |
Master's degree |
author |
Saudi, Syahmina Athirah |
author_facet |
Saudi, Syahmina Athirah |
author_sort |
Saudi, Syahmina Athirah |
title |
Crystal clear thermal barrier coating of inorganic polysiloxane resin filled with titanium dioxide for glass coating application / Syahmina Athirah Saudi |
title_short |
Crystal clear thermal barrier coating of inorganic polysiloxane resin filled with titanium dioxide for glass coating application / Syahmina Athirah Saudi |
title_full |
Crystal clear thermal barrier coating of inorganic polysiloxane resin filled with titanium dioxide for glass coating application / Syahmina Athirah Saudi |
title_fullStr |
Crystal clear thermal barrier coating of inorganic polysiloxane resin filled with titanium dioxide for glass coating application / Syahmina Athirah Saudi |
title_full_unstemmed |
Crystal clear thermal barrier coating of inorganic polysiloxane resin filled with titanium dioxide for glass coating application / Syahmina Athirah Saudi |
title_sort |
crystal clear thermal barrier coating of inorganic polysiloxane resin filled with titanium dioxide for glass coating application / syahmina athirah saudi |
granting_institution |
Universiti Teknologi MARA (UiTM) |
granting_department |
Faculty of Applied Sciences |
publishDate |
2022 |
url |
https://ir.uitm.edu.my/id/eprint/75758/1/75758.pdf |
_version_ |
1783736081417502720 |