Constant load effect on fracture of polymer concrete (PC) due to environment / Alia Ibrahim

Constant load effect on fracture of polymer concrete (PC) due to environment / Alia Ibrahim

The behavior of compact tension (CT) polymer concrete (PC) when exposed to air, water (pH=7) and sulfuric acid (pH=4) were investigated over a period of one and three weeks, respectively. In this study, CT specimen exposed to air will be considered as optimum condition. Also the effect of environmen...

Full description

Saved in:
Bibliographic Details
Main Author: Ibrahim, Alia
Format: Thesis
Language:English
Published: 2005
Online Access:https://ir.uitm.edu.my/id/eprint/77234/1/77234.pdf
Tags: Add Tag
No Tags, Be the first to tag this record!
id my-uitm-ir.77234
record_format uketd_dc
spelling my-uitm-ir.772342023-08-23T04:00:27Z Constant load effect on fracture of polymer concrete (PC) due to environment / Alia Ibrahim 2005 Ibrahim, Alia The behavior of compact tension (CT) polymer concrete (PC) when exposed to air, water (pH=7) and sulfuric acid (pH=4) were investigated over a period of one and three weeks, respectively. In this study, CT specimen exposed to air will be considered as optimum condition. Also the effect of environment to PC on the fracture toughness was studied. The decrease in fracture toughness was dependent on the type, concentration and pH of the corrosive solutions. In water and sulfuric acid exposure, PC did show reduced the fracture toughness compared to optimum specimen. Water was the most corrosive media compared to others as it reduced about 15.71% of the fracture toughness. The reduced fracture toughness corresponded to the increasing in pH value. There was linear correlation between the fracture toughness and stiffness. The highest fracture toughness was air at 1.89MPaVm having stiffness 0.3875kN/mm while the lowest fracture toughness was three weeks immersed in water at 1.59MPaVm having stiffness 0.3000kN/mm. A fixture was fabricated to conduct constant load test at 90%, 80% and 70% of fracture toughness. PC immersed in sulfuric acid for a week and three weeks show increasing percentage of life time to failure due to fracture at all loading rate. For 80% of fracture toughness loading, there was slightly different in large decreasing percentage of life time to failure for PC immersed in a week (94.95%) compared to three weeks immersed in water (86.77%). The reduced of percentage life time corresponded to suddenly increase uptake of water for the first week immersed. From the observation, decreasing life time to failure due to fracture for PC in all condition had no correlation with increasing load conducted for constant load test. 2005 Thesis https://ir.uitm.edu.my/id/eprint/77234/ https://ir.uitm.edu.my/id/eprint/77234/1/77234.pdf text en public degree Universiti Teknologi MARA (UiTM) Faculty of Mechanical Engineering Md Taib, Yakub
institution Universiti Teknologi MARA
collection UiTM Institutional Repository
language English
advisor Md Taib, Yakub
description The behavior of compact tension (CT) polymer concrete (PC) when exposed to air, water (pH=7) and sulfuric acid (pH=4) were investigated over a period of one and three weeks, respectively. In this study, CT specimen exposed to air will be considered as optimum condition. Also the effect of environment to PC on the fracture toughness was studied. The decrease in fracture toughness was dependent on the type, concentration and pH of the corrosive solutions. In water and sulfuric acid exposure, PC did show reduced the fracture toughness compared to optimum specimen. Water was the most corrosive media compared to others as it reduced about 15.71% of the fracture toughness. The reduced fracture toughness corresponded to the increasing in pH value. There was linear correlation between the fracture toughness and stiffness. The highest fracture toughness was air at 1.89MPaVm having stiffness 0.3875kN/mm while the lowest fracture toughness was three weeks immersed in water at 1.59MPaVm having stiffness 0.3000kN/mm. A fixture was fabricated to conduct constant load test at 90%, 80% and 70% of fracture toughness. PC immersed in sulfuric acid for a week and three weeks show increasing percentage of life time to failure due to fracture at all loading rate. For 80% of fracture toughness loading, there was slightly different in large decreasing percentage of life time to failure for PC immersed in a week (94.95%) compared to three weeks immersed in water (86.77%). The reduced of percentage life time corresponded to suddenly increase uptake of water for the first week immersed. From the observation, decreasing life time to failure due to fracture for PC in all condition had no correlation with increasing load conducted for constant load test.
format Thesis
qualification_level Bachelor degree
author Ibrahim, Alia
spellingShingle Ibrahim, Alia
Constant load effect on fracture of polymer concrete (PC) due to environment / Alia Ibrahim
author_facet Ibrahim, Alia
author_sort Ibrahim, Alia
title Constant load effect on fracture of polymer concrete (PC) due to environment / Alia Ibrahim
title_short Constant load effect on fracture of polymer concrete (PC) due to environment / Alia Ibrahim
title_full Constant load effect on fracture of polymer concrete (PC) due to environment / Alia Ibrahim
title_fullStr Constant load effect on fracture of polymer concrete (PC) due to environment / Alia Ibrahim
title_full_unstemmed Constant load effect on fracture of polymer concrete (PC) due to environment / Alia Ibrahim
title_sort constant load effect on fracture of polymer concrete (pc) due to environment / alia ibrahim
granting_institution Universiti Teknologi MARA (UiTM)
granting_department Faculty of Mechanical Engineering
publishDate 2005
url https://ir.uitm.edu.my/id/eprint/77234/1/77234.pdf
_version_ 1783736145689968640

Similar Items