Spin coated TiO2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / Muhammad Alhadi Zulkefle

Low cost sol-gel spin coating is indeed a popular method for producing thin films but suitable ways of controlling the process for fabrication of a high pH sensitivity TiO2 sensing membrane that obey Nernstian theoretical response (59.2 mV/pH) are limitedly available and explained. Hence this thesis...

Full description

Saved in:

Bibliographic Details
Main Author:	Zulkefle, Muhammad Alhadi
Format:	Thesis
Language:	English
Published:	2017
Subjects:	Surface effects and tests
Online Access:	https://ir.uitm.edu.my/id/eprint/89100/2/89100.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-uitm-ir.89100
record_format	uketd_dc
spelling	my-uitm-ir.891002024-04-16T14:20:47Z Spin coated TiO2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / Muhammad Alhadi Zulkefle 2017 Zulkefle, Muhammad Alhadi Surface effects and tests Low cost sol-gel spin coating is indeed a popular method for producing thin films but suitable ways of controlling the process for fabrication of a high pH sensitivity TiO2 sensing membrane that obey Nernstian theoretical response (59.2 mV/pH) are limitedly available and explained. Hence this thesis presents extensive works on studying the condition in sol-gel spin coating so that optimum condition would be identified. Sol-gel TiO2 is deposited on a conductive ITO coated glass substrate and then spun using spin coater. The solid TiO2 films produced are later dried and annealed and then measured for their pH response. Characterization of each film for its thickness and roughness was also performed using surface profiler and atomic force microscope. Comparing pH sensing performance of TiO2 and ZnO thin films, it was determined that TiO2 is a better sensing membrane for EGFET pH sensor than ZnO. This is because TiO2 sample shows greater sensitivity and linearity values than ZnO sample. Several parameters in sol-gel spin coating had been studied and the optimum condition was successfully identified. The overall findings in studies of deposition condition is that sol-gel spin TiO2 thin films ability to sense hydrogen ions can be improved by; fabricating it using a single layer structure as opposed to multiple layer, spun at the speed of 3000 rpm for duration of 75 seconds and annealed at 400 °C for 45 minutes. Based on the data, it was found that thickness of TiO2 thin films plays vital role in determining capabilities of the film to act as a good hydrogen sensing membrane for EGFET pH sensor. Thinner film has better sensitivity while thicker film shows deteriorating performance in sensing hydrogen ions and suitable TiO2 film thickness so that it would give high pH sensitivity is between 20 nm to 29 nm. The identified optimum condition is then applied to fabricate an optimized sample and the sample possesses sensitivity of 59.3 mV/pH and linearity of 0.9818. This value of pH sensitivity is high and follows Nernstian theoretical value. Besides that, the reliability and capabilities of the optimized sample to act as a good sensing membrane was further proved from the low drift and hysteresis values measured. 2017 Thesis https://ir.uitm.edu.my/id/eprint/89100/ https://ir.uitm.edu.my/id/eprint/89100/2/89100.pdf text en public masters Universiti Teknologi MARA (UiTM) Faculty of Electrical Engineering Herman, Sukreen Hana
institution	Universiti Teknologi MARA
collection	UiTM Institutional Repository
language	English
advisor	Herman, Sukreen Hana
topic	Surface effects and tests
spellingShingle	Surface effects and tests Zulkefle, Muhammad Alhadi Spin coated TiO2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / Muhammad Alhadi Zulkefle
description	Low cost sol-gel spin coating is indeed a popular method for producing thin films but suitable ways of controlling the process for fabrication of a high pH sensitivity TiO2 sensing membrane that obey Nernstian theoretical response (59.2 mV/pH) are limitedly available and explained. Hence this thesis presents extensive works on studying the condition in sol-gel spin coating so that optimum condition would be identified. Sol-gel TiO2 is deposited on a conductive ITO coated glass substrate and then spun using spin coater. The solid TiO2 films produced are later dried and annealed and then measured for their pH response. Characterization of each film for its thickness and roughness was also performed using surface profiler and atomic force microscope. Comparing pH sensing performance of TiO2 and ZnO thin films, it was determined that TiO2 is a better sensing membrane for EGFET pH sensor than ZnO. This is because TiO2 sample shows greater sensitivity and linearity values than ZnO sample. Several parameters in sol-gel spin coating had been studied and the optimum condition was successfully identified. The overall findings in studies of deposition condition is that sol-gel spin TiO2 thin films ability to sense hydrogen ions can be improved by; fabricating it using a single layer structure as opposed to multiple layer, spun at the speed of 3000 rpm for duration of 75 seconds and annealed at 400 °C for 45 minutes. Based on the data, it was found that thickness of TiO2 thin films plays vital role in determining capabilities of the film to act as a good hydrogen sensing membrane for EGFET pH sensor. Thinner film has better sensitivity while thicker film shows deteriorating performance in sensing hydrogen ions and suitable TiO2 film thickness so that it would give high pH sensitivity is between 20 nm to 29 nm. The identified optimum condition is then applied to fabricate an optimized sample and the sample possesses sensitivity of 59.3 mV/pH and linearity of 0.9818. This value of pH sensitivity is high and follows Nernstian theoretical value. Besides that, the reliability and capabilities of the optimized sample to act as a good sensing membrane was further proved from the low drift and hysteresis values measured.
format	Thesis
qualification_level	Master's degree
author	Zulkefle, Muhammad Alhadi
author_facet	Zulkefle, Muhammad Alhadi
author_sort	Zulkefle, Muhammad Alhadi
title	Spin coated TiO2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / Muhammad Alhadi Zulkefle
title_short	Spin coated TiO2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / Muhammad Alhadi Zulkefle
title_full	Spin coated TiO2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / Muhammad Alhadi Zulkefle
title_fullStr	Spin coated TiO2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / Muhammad Alhadi Zulkefle
title_full_unstemmed	Spin coated TiO2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / Muhammad Alhadi Zulkefle
title_sort	spin coated tio2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / muhammad alhadi zulkefle
granting_institution	Universiti Teknologi MARA (UiTM)
granting_department	Faculty of Electrical Engineering
publishDate	2017
url	https://ir.uitm.edu.my/id/eprint/89100/2/89100.pdf
_version_	1804889799293665280

Spin coated TiO2-based egfet ph sensor: fabrication of sensing membrane and sensor characterization / Muhammad Alhadi Zulkefle

Similar Items