Preparation and characterizations of sodium iodide-sodium dicyanamide solid electrolyte / Mohd Khairul Hazwan Mohd Yusof
This study sets out to investigate the possibility of using sodium based salt and inorganic ligand compound as solid electrolyte. Binary solid electrolyte system of NaI-NaN(CN)2 was successfully prepared by Ball Milling method with two hours of optimized milling time. The prepared samples were chara...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English |
Published: |
2018
|
Online Access: | https://ir.uitm.edu.my/id/eprint/89612/1/89612.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my-uitm-ir.89612 |
---|---|
record_format |
uketd_dc |
spelling |
my-uitm-ir.896122024-04-15T08:29:02Z Preparation and characterizations of sodium iodide-sodium dicyanamide solid electrolyte / Mohd Khairul Hazwan Mohd Yusof 2018 Mohd Yusof, Mohd Khairul Hazwan This study sets out to investigate the possibility of using sodium based salt and inorganic ligand compound as solid electrolyte. Binary solid electrolyte system of NaI-NaN(CN)2 was successfully prepared by Ball Milling method with two hours of optimized milling time. The prepared samples were characterized by Electrochemical Impedance Spectroscopy (EIS), Transference Number Measurement (TNM), Fourier Transform Infrared Spectroscopy (FTIR), X-Ray Diffraction (XRD) and Field Emission Scanning Electron Microscopy (FE-SEM). Highest conducting sample was obtained for 10NaI- 90NaN(CN)2 system where the room temperature conductivity was (5.67 ± 1.26) x 10-4 S cm-1 and it was confirmed an ionic conductor as the ionic transference number was 0.96. Temperature dependent conductivity analysis had revealed that the highest conducting sample obeys Arrhenius rule as the ionic charge carrier species conduction was through some hopping mechanism with lowest activation energy of 0.133 eV. Apart from that, conduction mechanism was found to follow Quantum Mechanical Tunneling (QMT) model. FTIR analysis had suggested some interaction had occurred between NaI charge carrier as the salt component in the binary system with the sodium dicyanamide host material as the duplet C≡ N spectra emerged into single broader peak at around 2100 cm-1 wavenumber region. Binary sample had showed to be less crystalline in nature due to decrease in overall intensity and disappearing of several sharp peaks from XRD diffractogram obtained. Finally, FE-SEM micrograph revealed significant difference between unmilled and milled pelletised sample as milled material particles was broken down into smaller size apart from homogenous of powder mixture was achieved. 2018 Thesis https://ir.uitm.edu.my/id/eprint/89612/ https://ir.uitm.edu.my/id/eprint/89612/1/89612.pdf text en public masters Universiti Teknologi MARA (UiTM) Faculty of Applied Science Ahmad, Azizah Hanom |
institution |
Universiti Teknologi MARA |
collection |
UiTM Institutional Repository |
language |
English |
advisor |
Ahmad, Azizah Hanom |
description |
This study sets out to investigate the possibility of using sodium based salt and inorganic ligand compound as solid electrolyte. Binary solid electrolyte system of NaI-NaN(CN)2 was successfully prepared by Ball Milling method with two hours of optimized milling time. The prepared samples were characterized by Electrochemical Impedance Spectroscopy (EIS), Transference Number Measurement (TNM), Fourier Transform Infrared Spectroscopy (FTIR), X-Ray Diffraction (XRD) and Field Emission Scanning Electron Microscopy (FE-SEM). Highest conducting sample was obtained for 10NaI- 90NaN(CN)2 system where the room temperature conductivity was (5.67 ± 1.26) x 10-4 S cm-1 and it was confirmed an ionic conductor as the ionic transference number was 0.96. Temperature dependent conductivity analysis had revealed that the highest conducting sample obeys Arrhenius rule as the ionic charge carrier species conduction was through some hopping mechanism with lowest activation energy of 0.133 eV. Apart from that, conduction mechanism was found to follow Quantum Mechanical Tunneling (QMT) model. FTIR analysis had suggested some interaction had occurred between NaI charge carrier as the salt component in the binary system with the sodium dicyanamide host material as the duplet C≡ N spectra emerged into single broader peak at around 2100 cm-1 wavenumber region. Binary sample had showed to be less crystalline in nature due to decrease in overall intensity and disappearing of several sharp peaks from XRD diffractogram obtained. Finally, FE-SEM micrograph revealed significant difference between unmilled and milled pelletised sample as milled material particles was broken down into smaller size apart from homogenous of powder mixture was achieved. |
format |
Thesis |
qualification_level |
Master's degree |
author |
Mohd Yusof, Mohd Khairul Hazwan |
spellingShingle |
Mohd Yusof, Mohd Khairul Hazwan Preparation and characterizations of sodium iodide-sodium dicyanamide solid electrolyte / Mohd Khairul Hazwan Mohd Yusof |
author_facet |
Mohd Yusof, Mohd Khairul Hazwan |
author_sort |
Mohd Yusof, Mohd Khairul Hazwan |
title |
Preparation and characterizations of sodium iodide-sodium dicyanamide solid electrolyte / Mohd Khairul Hazwan Mohd Yusof |
title_short |
Preparation and characterizations of sodium iodide-sodium dicyanamide solid electrolyte / Mohd Khairul Hazwan Mohd Yusof |
title_full |
Preparation and characterizations of sodium iodide-sodium dicyanamide solid electrolyte / Mohd Khairul Hazwan Mohd Yusof |
title_fullStr |
Preparation and characterizations of sodium iodide-sodium dicyanamide solid electrolyte / Mohd Khairul Hazwan Mohd Yusof |
title_full_unstemmed |
Preparation and characterizations of sodium iodide-sodium dicyanamide solid electrolyte / Mohd Khairul Hazwan Mohd Yusof |
title_sort |
preparation and characterizations of sodium iodide-sodium dicyanamide solid electrolyte / mohd khairul hazwan mohd yusof |
granting_institution |
Universiti Teknologi MARA (UiTM) |
granting_department |
Faculty of Applied Science |
publishDate |
2018 |
url |
https://ir.uitm.edu.my/id/eprint/89612/1/89612.pdf |
_version_ |
1804889815115628544 |