Barrier, thermal and mechanical properties of polyurethane-modified clay nanocomposites for thermal insulation material

In this thesis, the effect of modification through transition metal ions (TMI) on montmorillonite (MMT) clay that was incorporated into thermoplastic polyurethane (PU) was discussed. The TMI modification was intended to achieve a good dispersion of the clay into PU with fewer agglomerates. The modif...

Full description

Saved in:
Bibliographic Details
Main Author: Shamini, Gunaseelan
Format: Thesis
Language:English
Published: 2014
Subjects:
Online Access:http://umpir.ump.edu.my/id/eprint/12713/1/Barrier%2C%20thermal%20and%20mechanical%20properties%20of%20polyurethane-modified%20clay%20nanocomposites%20for%20thermal%20insulation%20material.pdf
Tags: Add Tag
No Tags, Be the first to tag this record!
id my-ump-ir.12713
record_format uketd_dc
spelling my-ump-ir.127132023-05-03T03:52:50Z Barrier, thermal and mechanical properties of polyurethane-modified clay nanocomposites for thermal insulation material 2014-09 Shamini, Gunaseelan TP Chemical technology In this thesis, the effect of modification through transition metal ions (TMI) on montmorillonite (MMT) clay that was incorporated into thermoplastic polyurethane (PU) was discussed. The TMI modification was intended to achieve a good dispersion of the clay into PU with fewer agglomerates. The modification of the MMT clay was carried out using Copper (II) Chloride and Iron (III) Chloride. The fabrication of the nanocomposites was done via solution intercalation method by employing chloroform as the solvent. The clay content was varied at three different clay loadings (1 to 3 weight percentage). The existences of the TMIs on the modified clay were confirmed through Inductive Couple Plasma Mass Spectrometry (ICP-MS) whereas its morphological structure was tested through Field Emission Scanning Electron Microscope (FESEM) and X-Ray Diffraction (XRD). The morphology of PU-MMT nanocomposites was determined through Fourier Transform Infrared Spectroscopy (FTIR), Scanning Electron Microscope (SEM), XRD and FESEM. The mechanical properties of the nanocomposites were studied through its tensile stress and elongation at break whereas its thermal properties were analysed using Thermogravimetric Analysis (TGA), Differential Scanning Calorimetry (DSC) and thermal conduction. Gas and water permeation through the nanocomposites was employed to investigate the nanocomposite’s barrier properties. The modification process was proved successful as high amount of copper and iron ions were detected in the ICP-MS and even distribution of the clay was obtained in FESEM. XRD data with higher d-spacing values was obtained for PU with modified clay which suggests that a good intercalated structure has been achieved. SEM micrographs illustrated lesser agglomerates in PU with modified clay nanocomposites due to the TMI modification that enables an even distribution of the clay into PU. The homogeneous dispersion of the clay strengthened the structure of PU which led to a remarkable improvement in its mechanical properties. The highest increase in tensile stress was obtained in 2% PU-MMT Cu which showed 148% hike in its 1% and 3% clay loading. The thermal stability was also improved in the modified nanocomposites due to its higher thermal degradation temperature however there were no significant effect of the clay on the melting temperature of the nanocomposites. Thermal conductivity of the PU nanocomposites decreased with increasing clay loading which makes it a suitable thermal insulation material. Both the gas and water permeability decreased in PU with modified clay nanocomposites due to the formation of the tortuous path in its matrix. The highest significant decrease in the gas permeation analysis amounted to 68% in 3% PU-MMT Fe and 40 times decrement in water permeation coefficients were obtianed in 1% PU-MMT Fe. The results obtained showed that the incorporation of modified clay into PU has brought significant improvements in its properties. 2014-09 Thesis http://umpir.ump.edu.my/id/eprint/12713/ http://umpir.ump.edu.my/id/eprint/12713/1/Barrier%2C%20thermal%20and%20mechanical%20properties%20of%20polyurethane-modified%20clay%20nanocomposites%20for%20thermal%20insulation%20material.pdf pdf en public masters Universiti Malaysia Pahang Faculty of Chemical & Natural Resources Engineering Yusoh, Kamal
institution Universiti Malaysia Pahang Al-Sultan Abdullah
collection UMPSA Institutional Repository
language English
advisor Yusoh, Kamal
topic TP Chemical technology
spellingShingle TP Chemical technology
Shamini, Gunaseelan
Barrier, thermal and mechanical properties of polyurethane-modified clay nanocomposites for thermal insulation material
description In this thesis, the effect of modification through transition metal ions (TMI) on montmorillonite (MMT) clay that was incorporated into thermoplastic polyurethane (PU) was discussed. The TMI modification was intended to achieve a good dispersion of the clay into PU with fewer agglomerates. The modification of the MMT clay was carried out using Copper (II) Chloride and Iron (III) Chloride. The fabrication of the nanocomposites was done via solution intercalation method by employing chloroform as the solvent. The clay content was varied at three different clay loadings (1 to 3 weight percentage). The existences of the TMIs on the modified clay were confirmed through Inductive Couple Plasma Mass Spectrometry (ICP-MS) whereas its morphological structure was tested through Field Emission Scanning Electron Microscope (FESEM) and X-Ray Diffraction (XRD). The morphology of PU-MMT nanocomposites was determined through Fourier Transform Infrared Spectroscopy (FTIR), Scanning Electron Microscope (SEM), XRD and FESEM. The mechanical properties of the nanocomposites were studied through its tensile stress and elongation at break whereas its thermal properties were analysed using Thermogravimetric Analysis (TGA), Differential Scanning Calorimetry (DSC) and thermal conduction. Gas and water permeation through the nanocomposites was employed to investigate the nanocomposite’s barrier properties. The modification process was proved successful as high amount of copper and iron ions were detected in the ICP-MS and even distribution of the clay was obtained in FESEM. XRD data with higher d-spacing values was obtained for PU with modified clay which suggests that a good intercalated structure has been achieved. SEM micrographs illustrated lesser agglomerates in PU with modified clay nanocomposites due to the TMI modification that enables an even distribution of the clay into PU. The homogeneous dispersion of the clay strengthened the structure of PU which led to a remarkable improvement in its mechanical properties. The highest increase in tensile stress was obtained in 2% PU-MMT Cu which showed 148% hike in its 1% and 3% clay loading. The thermal stability was also improved in the modified nanocomposites due to its higher thermal degradation temperature however there were no significant effect of the clay on the melting temperature of the nanocomposites. Thermal conductivity of the PU nanocomposites decreased with increasing clay loading which makes it a suitable thermal insulation material. Both the gas and water permeability decreased in PU with modified clay nanocomposites due to the formation of the tortuous path in its matrix. The highest significant decrease in the gas permeation analysis amounted to 68% in 3% PU-MMT Fe and 40 times decrement in water permeation coefficients were obtianed in 1% PU-MMT Fe. The results obtained showed that the incorporation of modified clay into PU has brought significant improvements in its properties.
format Thesis
qualification_level Master's degree
author Shamini, Gunaseelan
author_facet Shamini, Gunaseelan
author_sort Shamini, Gunaseelan
title Barrier, thermal and mechanical properties of polyurethane-modified clay nanocomposites for thermal insulation material
title_short Barrier, thermal and mechanical properties of polyurethane-modified clay nanocomposites for thermal insulation material
title_full Barrier, thermal and mechanical properties of polyurethane-modified clay nanocomposites for thermal insulation material
title_fullStr Barrier, thermal and mechanical properties of polyurethane-modified clay nanocomposites for thermal insulation material
title_full_unstemmed Barrier, thermal and mechanical properties of polyurethane-modified clay nanocomposites for thermal insulation material
title_sort barrier, thermal and mechanical properties of polyurethane-modified clay nanocomposites for thermal insulation material
granting_institution Universiti Malaysia Pahang
granting_department Faculty of Chemical & Natural Resources Engineering
publishDate 2014
url http://umpir.ump.edu.my/id/eprint/12713/1/Barrier%2C%20thermal%20and%20mechanical%20properties%20of%20polyurethane-modified%20clay%20nanocomposites%20for%20thermal%20insulation%20material.pdf
_version_ 1783731969669988352