Study of a palm slag-filled friction composite for brake pad
Since the use of asbestos was banned in all types of products and applications due to its carcinogenic nature, researchers worldwide has conducted extensive research and development activities with the goal of identifying alternative and safe materials. This research work was conducted with the ma...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Subjects: | |
| Online Access: | http://dspace.unimap.edu.my:80/xmlui/bitstream/123456789/42887/1/P.1-24.pdf http://dspace.unimap.edu.my:80/xmlui/bitstream/123456789/42887/2/Full%20Text.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Since the use of asbestos was banned in all types of products and applications due to its
carcinogenic nature, researchers worldwide has conducted extensive research and
development activities with the goal of identifying alternative and safe materials. This research work was conducted with the main objective of determining the potential and capability of using palm slag, an industrial solid waste that is abundant in Malaysia, as an alternative filler material in friction composites for brake pad applications. The
other main ingredient that were used to develop friction composites in this research
were, phenolic resin as a binder, graphite as a lubricant, alumina as an abrasive and
steel fibers to provide reinforcement. The mixture was hand press compacted to have
the 10 mm diameter cylindrical green body before being further compacted and cured
in a hot press at the 160 oC for five (5) minutes. Then the samples were post-cured in
the oven at 160 oC for four (4) hours before being tested for hardness, density,
compressive strength and resistance to wear. Characterization of the raw material,
especially the thermal behaviour of the palm slag, showed that it was thermally stable
and suitable for use as the filler material in brake pads. The processing parameters with
higher molding pressures had significant effects on the brake pad’s end properties, such
as density, hardness and compressive strength of the friction composite. The result of
this study also indicated that the mechanical properties of the composite material were
inversely related to the size of the palm slag particles that comprise the composite. The
wear rate of the friction composite was influenced by the type of filler, moulding
pressures and particle size of the filler. As a conclusion, this study was determined that,
palm slag could be one of the alternative fillers used in brake pad with a comparable
© This item is protected by original copyright
xix
wear properties to the commercial brake pad products in the market. It was also found
that, after a certain initial period of use, the trend of wear rate for various sliding
distances was essentially constant and linear. Lastly, on road brake test was
recommended to be performed for further study in the future to validate the formulation
or a real application in the vehicle. |
|---|