Kajian rintangan kakisan ke atas keluli bar tetulang dalam pes geopolimer
This study has been conducted to understand corrosion resistance on reinforcement bar in geopolymer. Geopolymer paste has been used as a substitute for ordinary Portland cement (OPC) concrete structures. Geopolymer paste in this study was made from a mixture of fly ash and an alkaline activator o...
Saved in:
| Summary: | This study has been conducted to understand corrosion resistance on reinforcement bar in
geopolymer. Geopolymer paste has been used as a substitute for ordinary Portland cement
(OPC) concrete structures. Geopolymer paste in this study was made from a mixture of fly
ash and an alkaline activator of sodium hydroxide (NaOH) solution and sodium silicate
(Na2SiO3) solution. For tests involving steel reinforcement bars, carbon steel is placed in
the middle of the mixture and allowed to harden for 24 hours. Next, geopolymer paste
placed in an oven for curing process for 24 hours. The temperature was 60˚C. Various tests
were conducted to study the respect of geopolymer paste and study of corrosion on steel
reinforcement bars in the paste. Among the tests conducted are phase analysis, type of
bonding analysis, morphology analysis, water absorption test, porosity test, compressive
strength test, pulse velocity test, immersion test, hardness test, electrical resistivity test,
open circuit potential (OCP) measurements test and Tafel extrapolation test. For water
absorption test, the percentage of water absorbed reduced from day 7 until day 90 which
4.65%, 4.27%, 4.16% and 3.81%. The percentage of porosity also reduced from 11.95%,
11.02%, 7.65% and 3.77% from day 7 until day 90. Vice versa, compressive strength value
increased from day 7 until day 90 with the readings were 25.18 MPa, 26.76 MPa, 34.99
MPa and 56.50 MPa. The geopolymer electrical resistivity value at day 28 with electrode
spacing 0.10 m and 0.01 mA current stated highest value of electrical resistivity with 61575
Ω.m however geopolymer at day 7 with electrode spacing 0.02 m and 0.95 mA current
shows the lowest electrical resistivity with 537 Ω.m. It shows that the corrosion rate of
geopolymer was low and too small. For OCP test before applying sacrificial anode
cathodic protection (SACP), geopolymer stated minimum and maximum potential value
with -0.120 V and 0.539 V respectively. From the tests, the corrosion rate of steel in
geopolymer paste is still under controlled and located in the passive region. In the passive
region, an oxide layer which is Iron (III) Oxide-Hydroxide (FeOOH) formed by the
reaction between the steel, minerals and the air and protect the steel from corrosion agents.
But this layer can only survive in the decades depends on the environment. The oxide layer
will be destroyed if the paste or concrete cracks. Thus, the SACP method was implemented
to protect the steel reinforcement bars in the geopolymer paste. Zinc anode is used as a
sacrificial anode as the zinc has a higher electronegativity than iron in the electrochemical
series. After running further analysis, it was found that the potential values located in the
immunity region where the minimum potential value was -0.942 V and the maximum value
was -0.704 V. In the immunity region, ferum (Fe) is stable and the reinforcement bar is not
attacked by the corrosion. |
|---|