Durability Study Of Precast Concrete Sandwich Panel Under Exposure To Sea Water
An experimental investigation was conducted to observe and study the behavior of precast concrete sandwich panels in corrosive environment of chloride ion in marine environment. Three different strengths of marine waters were prepared namely one time, three time and six times of the concentration...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English English |
| Published: |
2002
|
| Subjects: | |
| Online Access: | http://psasir.upm.edu.my/id/eprint/12065/1/FK_2002_31.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| id |
my-upm-ir.12065 |
|---|---|
| record_format |
uketd_dc |
| spelling |
my-upm-ir.120652024-06-27T08:50:33Z Durability Study Of Precast Concrete Sandwich Panel Under Exposure To Sea Water 2002-08 Ahmad, Aftab An experimental investigation was conducted to observe and study the behavior of precast concrete sandwich panels in corrosive environment of chloride ion in marine environment. Three different strengths of marine waters were prepared namely one time, three time and six times of the concentration of actual ocean water. Twenty-seven numbers of sandwich panels were casted and nine numbers were placed in each types of solution. Along with that one number of Panel was casted to use as control specimen and left in air for eight months .Two more sandwich panel were used for permeability tests. The study deals with the experimental investigation of panels for their ability to stand in corrosive environment and probability of corrosion in panel reinforcement. The results obtained were analyzed and observation was made to identify the corrosion probability, location of maximum corrosion and corrosion rate of the sandwich panel reinforcement. Comparative behaviors of the concrete strength variation in different chloride environment were observed. From the observation of the experimental results it was found that at higher chloride concentration in the environment causes higher corrosion and in the same environment highest corrosion was found along the edges of the precast concrete sandwich panel. There was no critical loss of concrete strength in sandwich panel due to submersion test. Reinforced concrete Concrete panels 2002-08 Thesis http://psasir.upm.edu.my/id/eprint/12065/ http://psasir.upm.edu.my/id/eprint/12065/1/FK_2002_31.pdf text en public masters Universiti Putra Malaysia Reinforced concrete Concrete panels Faculty of Engineering Abdul Samad, Abdul Aziz English |
| institution |
Universiti Putra Malaysia |
| collection |
PSAS Institutional Repository |
| language |
English English |
| advisor |
Abdul Samad, Abdul Aziz |
| topic |
Reinforced concrete Concrete panels |
| spellingShingle |
Reinforced concrete Concrete panels Ahmad, Aftab Durability Study Of Precast Concrete Sandwich Panel Under Exposure To Sea Water |
| description |
An experimental investigation was conducted to observe and study the behavior of
precast concrete sandwich panels in corrosive environment of chloride ion in marine
environment. Three different strengths of marine waters were prepared namely one time,
three time and six times of the concentration of actual ocean water. Twenty-seven
numbers of sandwich panels were casted and nine numbers were placed in each types of
solution. Along with that one number of Panel was casted to use as control specimen and
left in air for eight months .Two more sandwich panel were used for permeability tests.
The study deals with the experimental investigation of panels for their ability to stand in
corrosive environment and probability of corrosion in panel reinforcement.
The results obtained were analyzed and observation was made to identify the corrosion
probability, location of maximum corrosion and corrosion rate of the sandwich panel
reinforcement. Comparative behaviors of the concrete strength variation in different chloride environment were observed. From the observation of the experimental results it
was found that at higher chloride concentration in the environment causes higher
corrosion and in the same environment highest corrosion was found along the edges of
the precast concrete sandwich panel. There was no critical loss of concrete strength in
sandwich panel due to submersion test. |
| format |
Thesis |
| qualification_level |
Master's degree |
| author |
Ahmad, Aftab |
| author_facet |
Ahmad, Aftab |
| author_sort |
Ahmad, Aftab |
| title |
Durability Study Of Precast Concrete Sandwich Panel Under Exposure To Sea Water |
| title_short |
Durability Study Of Precast Concrete Sandwich Panel Under Exposure To Sea Water |
| title_full |
Durability Study Of Precast Concrete Sandwich Panel Under Exposure To Sea Water |
| title_fullStr |
Durability Study Of Precast Concrete Sandwich Panel Under Exposure To Sea Water |
| title_full_unstemmed |
Durability Study Of Precast Concrete Sandwich Panel Under Exposure To Sea Water |
| title_sort |
durability study of precast concrete sandwich panel under exposure to sea water |
| granting_institution |
Universiti Putra Malaysia |
| granting_department |
Faculty of Engineering |
| publishDate |
2002 |
| url |
http://psasir.upm.edu.my/id/eprint/12065/1/FK_2002_31.pdf |
| _version_ |
1804888671376113664 |