Preparation and Characterization of Natural Rubber/Polypropylene/Fatty Hyrazide-Octadecyl Ammonium Modified Clay Nanocomposites
Fatty hydrazides (FH) which were synthesized from palm oil were used as one of the organic compounds to modify a natural clay (sodium montmorillonite). The clay modification was carried out by stirring the clay particles in an aqueous solution of a mixture of FH and octadecylammonium (ODA) by whi...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English English |
Published: |
2008
|
Subjects: | |
Online Access: | http://psasir.upm.edu.my/id/eprint/5128/1/FS_2008_23.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my-upm-ir.5128 |
---|---|
record_format |
uketd_dc |
spelling |
my-upm-ir.51282013-05-27T07:20:35Z Preparation and Characterization of Natural Rubber/Polypropylene/Fatty Hyrazide-Octadecyl Ammonium Modified Clay Nanocomposites 2008 Alosime, Eid Moneer Fatty hydrazides (FH) which were synthesized from palm oil were used as one of the organic compounds to modify a natural clay (sodium montmorillonite). The clay modification was carried out by stirring the clay particles in an aqueous solution of a mixture of FH and octadecylammonium (ODA) by which the clay layer distance increases from 1.27 nm to 2.60 nm. The modified clay was then used in the preparation of the natural rubber/polypropylene (NR/PP) blend nanocomposites. The intercalation of the modifier in the clay layer was characterized by X-ray diffraction (XRD) and Fourier Transform Infrared (FT-IR). Elemental analysis was used to estimate the presence of FH and ODA in the clay. In the first part of the preparation, the nanocomposites were synthesized by melt mixing of the modified clay and a natural rubber (SMR CV60) using a two-roll-mill internal mixer. The compounded natural rubber was then mixed with organic peroxide-Luperox F-40P at 60 °C and cured at 130 °C using an electrical hydraulic hot press. Mechanical properties of the produced composites were then characterized. The results indicate that the presence of the modified clay has dramatically improved these properties. The crosslinked NR/clay nanocomposites were further characterized by XRD, Transmission Electron Microscopy (TEM) and Thermogravimetric Analysis (TGA). In the final part of the study, preparation of the nanocomposites was carried out by melt mixing of the modified clay with NR/PP in the ratio of 50:50 using the internal mixer. The study of mixing temperature, rotor speed and mixing time shows that under the following mixing conditions: temperature of 170 °C, 75 rpm of rotor speed and 10 minutes of mixing time, the composites with maximum tensile strength and elongation at break were obtained. The modified clay content to give maximum tensile strength is 1 php. The crosslinking of NR/PP, using Luperox F-40P to crosslink the rubber phase was also investigated. The compound was then cured in a hot press at 185 °C. The optimum concentration of Luperox F-40P to give maximum strength and elongation at break is 2.0 php. The tensile strength of Luperox F-40P crosslinked NR/PP/clay is higher compared to those of the unfilled crosslinked NR/PP/clay. The presence of 1 or 3 php of the modified clay into the Luperox F-40P crosslinked NR/PP increases its tensile strength. TGA study shows that crosslinked NR/PP/clay nanocomposites have higher decomposition temperatures in comparison with those of the crosslinked NR/PP/clay composites. Polypropylene Polymeric composites Clay - Analysis 2008 Thesis http://psasir.upm.edu.my/id/eprint/5128/ http://psasir.upm.edu.my/id/eprint/5128/1/FS_2008_23.pdf application/pdf en public masters Universiti Putra Malaysia Polypropylene Polymeric composites Clay - Analysis Science English |
institution |
Universiti Putra Malaysia |
collection |
PSAS Institutional Repository |
language |
English English |
topic |
Polypropylene Polymeric composites Clay - Analysis |
spellingShingle |
Polypropylene Polymeric composites Clay - Analysis Alosime, Eid Moneer Preparation and Characterization of Natural Rubber/Polypropylene/Fatty Hyrazide-Octadecyl Ammonium Modified Clay Nanocomposites |
description |
Fatty hydrazides (FH) which were synthesized from palm oil were used as one of the
organic compounds to modify a natural clay (sodium montmorillonite). The clay
modification was carried out by stirring the clay particles in an aqueous solution of a
mixture of FH and octadecylammonium (ODA) by which the clay layer distance
increases from 1.27 nm to 2.60 nm. The modified clay was then used in the
preparation of the natural rubber/polypropylene (NR/PP) blend nanocomposites. The
intercalation of the modifier in the clay layer was characterized by X-ray diffraction
(XRD) and Fourier Transform Infrared (FT-IR). Elemental analysis was used to
estimate the presence of FH and ODA in the clay.
In the first part of the preparation, the nanocomposites were synthesized by melt
mixing of the modified clay and a natural rubber (SMR CV60) using a two-roll-mill
internal mixer. The compounded natural rubber was then mixed with organic
peroxide-Luperox F-40P at 60 °C and cured at 130 °C using an electrical hydraulic
hot press. Mechanical properties of the produced composites were then characterized. The results indicate that the presence of the modified clay has
dramatically improved these properties. The crosslinked NR/clay nanocomposites
were further characterized by XRD, Transmission Electron Microscopy (TEM) and
Thermogravimetric Analysis (TGA).
In the final part of the study, preparation of the nanocomposites was carried out by
melt mixing of the modified clay with NR/PP in the ratio of 50:50 using the internal
mixer. The study of mixing temperature, rotor speed and mixing time shows that
under the following mixing conditions: temperature of 170 °C, 75 rpm of rotor speed
and 10 minutes of mixing time, the composites with maximum tensile strength and
elongation at break were obtained. The modified clay content to give maximum
tensile strength is 1 php. The crosslinking of NR/PP, using Luperox F-40P to
crosslink the rubber phase was also investigated. The compound was then cured in a
hot press at 185 °C. The optimum concentration of Luperox F-40P to give maximum
strength and elongation at break is 2.0 php. The tensile strength of Luperox F-40P
crosslinked NR/PP/clay is higher compared to those of the unfilled crosslinked
NR/PP/clay. The presence of 1 or 3 php of the modified clay into the Luperox F-40P
crosslinked NR/PP increases its tensile strength. TGA study shows that crosslinked
NR/PP/clay nanocomposites have higher decomposition temperatures in comparison
with those of the crosslinked NR/PP/clay composites. |
format |
Thesis |
qualification_level |
Master's degree |
author |
Alosime, Eid Moneer |
author_facet |
Alosime, Eid Moneer |
author_sort |
Alosime, Eid Moneer |
title |
Preparation and Characterization of Natural Rubber/Polypropylene/Fatty Hyrazide-Octadecyl Ammonium Modified Clay Nanocomposites |
title_short |
Preparation and Characterization of Natural Rubber/Polypropylene/Fatty Hyrazide-Octadecyl Ammonium Modified Clay Nanocomposites |
title_full |
Preparation and Characterization of Natural Rubber/Polypropylene/Fatty Hyrazide-Octadecyl Ammonium Modified Clay Nanocomposites |
title_fullStr |
Preparation and Characterization of Natural Rubber/Polypropylene/Fatty Hyrazide-Octadecyl Ammonium Modified Clay Nanocomposites |
title_full_unstemmed |
Preparation and Characterization of Natural Rubber/Polypropylene/Fatty Hyrazide-Octadecyl Ammonium Modified Clay Nanocomposites |
title_sort |
preparation and characterization of natural rubber/polypropylene/fatty hyrazide-octadecyl ammonium modified clay nanocomposites |
granting_institution |
Universiti Putra Malaysia |
granting_department |
Science |
publishDate |
2008 |
url |
http://psasir.upm.edu.my/id/eprint/5128/1/FS_2008_23.pdf |
_version_ |
1747810357173288960 |