Preparation of N-isopropyl acrylamide polymer gel dosimeters and their characterization by Raman spectroscopy
This present work aims to synthesise N-isopropyl acrylamide (NIPAM) polymer gel and study the effect of NIPAM monomer and N, N’-methylene-bisacrylamide (BIS) crosslinker concentrations on polymerization of NIPAM polymer and NIPAM and BIS consumptions in gelatin matrix induced by gamma rays at dose b...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2014
|
| Subjects: | |
| Online Access: | http://psasir.upm.edu.my/id/eprint/70511/1/FS%202014%2066%20-%20IR.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | This present work aims to synthesise N-isopropyl acrylamide (NIPAM) polymer gel and study the effect of NIPAM monomer and N, N’-methylene-bisacrylamide (BIS) crosslinker concentrations on polymerization of NIPAM polymer and NIPAM and BIS consumptions in gelatin matrix induced by gamma rays at dose between 0 and 21 Gy. The NIPAM polymer gels were synthesized from NIPAM (2 to 4% w/w) and BIS (2 to 4% w/w), gelatin (6% w/w), anti-oxidant tetrakis hydroxymethyl phosphonium chloride (THPC) (5 mM), and de-ionized water. The samples were irradiated with 60Co Gamma cell instrument at a constant dose rate, receiving doses from 3 Gy up to 21 Gy. The dose response of irradiated NIPAM polymer gel was determined using Raman spectroscopy. Raman peak intensities were identified in the samples at 815 cm-1 assigned bonding for C-C of NIPAM polymer gel, 1025 cm-1 assigned bonding for C=C of NIPAM and 2353 cm-1 bonding for C=C of BIS. The Raman intensity y that corresponds to the rate of polymer formation in NIPAM polymer gel increases with increasing dose D and fitted with the monoexponential equation y = y0 + A(1 – e –D/D0 ). The dose sensitivity D0 derived from the equation that was also found increasing with the increase of initial concentrations of NIPAM monomer and BIS crosslinker. The rate of co-monomer consumption decreases with increasing dose and was fitted with the monoexponential equation y = y0 – A(1 – e -D/ D0). The dose sensitivity D0
were also found to increase with the increase of initial concentrations of NIPAM monomer and BIS crosslinker. |
|---|