Preparation and characterization of zinc oxide and titanium oxide polyethersulfone hybrid film photocatalysts for degradation of methyl orange
Environmental issues and scarcity of water reserves have led to the development of photocatalyst technology to recycle the polluted water. The photocatalyst is usually applied in powder form but suffers several drawbacks; (i) agglomeration which led to a decrease in photoactivity and (ii) diff...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2018
|
| Subjects: | |
| Online Access: | http://psasir.upm.edu.my/id/eprint/76906/1/ITMA%202018%2021%20-%20IR.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Environmental issues and scarcity of water reserves have led to the development of
photocatalyst technology to recycle the polluted water. The photocatalyst is usually
applied in powder form but suffers several drawbacks; (i) agglomeration which led to a
decrease in photoactivity and (ii) difficult and costly recovery process. These problems
could be overcome by immobilizing the catalyst on a support. With the aim to provide
alternative solution to the solid–liquid separation problem, polyethersulfone (PES) was
chosen as the support due to its stability against radicals produced during photocatalytic
reaction. This work investigated the physicochemical characteristics of TiO2/PES,
ZnO/PES and reduced TiO2 (rTiO2)/PES hybrid film photocatalyst prepared via phase
inversion technique and reported, for the first time, its synergistic contribution in the
field of photocatalysis. The films were characterized using Scanning Electron
Microscopy (SEM), Energy Dispersive X-ray (EDX), X-ray Diffraction (XRD), X-ray
Photoelectron Spectroscopy (XPS), Atomic Force Microscopy (AFM) and UV-vis
Diffuse Reflectance Spectroscopy (UV-vis DRS) analyses. XRD, SEM and EDX
analyses revealed that the TiO2, ZnO and reduced TiO2 (rTiO2) were homogeneously
dispersed and embedded onto the PES film. XPS and UV-vis DRS results confirmed the
existence of interstitial site of TiO2 (458.2 and 463.9 eV), ZnO (1021.0 and 1043.8 eV)
and rTiO2 (456.1 and 461.8 eV) with their respective band gap energy of 3.00, 3.15 and
2.85 eV. The films exhibited higher surface roughness and enhance hydrophilicity
compared to PES film alone. The photoactivity of the films was evaluated with respect
to methyl orange (MO) degradation under both UV and visible light irradiation.
Emphasis was placed on the effect of catalyst loading, pH, concentration, number of
films and recyclability study. The best film photocatalysts displayed pseudo first-order
kinetics with almost 80% and 30% for PES–TiO2 (13 wt%), 100% and 56% for PES–
ZnO (17 wt%), 76% and 55% for PES–rTiO2 (13 wt%) of MO removal under original
condition against UV and visible light irradiation, respectively. A complete removal of
MO was achieved at pH 2.0 for both PES–TiO2 (13 wt%) and PES–rTiO2 (13 wt%) and
pH 5.8 for PES–ZnO (17 wt%). The degradation percentage decreased with increasing
initial concentration of MO (5–20 mg/L) but increased with increasing number of films.
The major active species were found to be •O2
– for both PES–TiO2 (13 wt%) and PES–
rTiO2 (13 wt%) and h+ for PES–ZnO (17 wt%). The best films can be recycled for up to five times while retaining its stability and degradation efficiency without being subjected
to any regeneration process. The degradation of palm oil mill effluent (POME) was
monitored through chemical oxygen demand (COD) analysis with degradation
percentage of 20%, 27%, 12% and 12%, 18%, 15% under UV and visible light
irradiation, respectively with some reduction in American Dye Manufacturers’ Institute
(ADMI) colour values. |
|---|