Microwave-Assisted Synthesis of Layered Double Hydroxides and Their Nanocomposites
A senes of hydrotalcite (HT) compounds of the type {Mg1_.rAl,(OH)2}[CO3]1.x12 mH2O had been synthesised using conventional co-precipitation method with Rd15 = Mg/ Al=1 to 10 m order to establish the relationship between composition and the basic properties it was found that pure HT compounds were...
محفوظ في:
| المؤلف الرئيسي: | |
|---|---|
| التنسيق: | أطروحة |
| اللغة: | English English |
| منشور في: |
1999
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | http://psasir.upm.edu.my/id/eprint/9472/1/FSAS_1999_19_A.pdf |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | A senes of hydrotalcite (HT) compounds of the type {Mg1_.rAl,(OH)2}[CO3]1.x12 mH2O
had been synthesised using conventional co-precipitation method with Rd15 = Mg/ Al=1 to 10
m order to establish the relationship between composition and the basic properties it was
found that pure HT compounds were obtained in the range of Rd15 =2 to 4. The materials
were also synthesised by microwave-assisted method using a home cooking microwave oven
at various ageing tunes, from 0 5 to 10.0 minutes.The discharged ratio of Rd15 = 3, 4, and 6
were chosen in this study. The resulting synthetic materials afford well-crystallised
hydrotalcite even at a very short microwave exposure tune of about 60 minutes as compared
With the conventional method that took about 18hrs. However, the conventional method gave
good crystallimty. On the other hand, the microwave-assisted method gave better pore size
distribution as compared to the conventional method. Better crystallImty was observed as the
exposure time mcreased for all Rd15 Structural charactensations were done by powder X-ray
diffraction (PXRD). The gram sizes and crystal stram of the materials using PXRD were
calculated.
Modification of hydrotalcite had also been done by replacing its among With
anthraqumone-2,6-disulfanate ions (AQ26), which were present in the mterlayer of brucitelike
([Mg1-,AI.,(OH)2]") and [Zn1-.,Alx(OH)2]")... |
|---|