Fracture Toughness Enhancement of Zirconia Toughened Alumina (ZTA) Through Additions Of Combination Of CaCO3 And CaO
Alumina yang diperkuat zirkonia (ZTA) merupakan sebatian seramik yang amat berguna dalam teknologi industri masa kini. Walau bagaimanapun, sifat keliatan patah ZTA yang rendah menghadkan penggunaan yang meluas dalam bidang kejuruteraan. Oleh itu, penambahbaikan bagi keliatan patah adalah pentin...
Saved in:
Main Author: | Ibrahm Sktani, Zhwan Dilshad |
---|---|
Format: | Thesis |
Language: | English |
Published: |
2016
|
Subjects: | |
Online Access: | http://eprints.usm.my/40777/1/Fracture_Toughness_Enhancement_of_Zirconia_Toughened_Alumina_%28ZTA%29_Through_Additions_Of_Combination_Of_CaCO3_And_CaO.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Similar Items
-
Toughness enhancement of zirconia-toughened alumina ceramic composite using multi-phasic additives and microwave heat treatment
by: Abdullah, Ezzat Chan
Published: (2017) -
Wear Resistance Performance Of Zirconia Toughened Alumina (ZTA) Cutting Tool Added With MgO and CeO2
by: Ali, Afifah Mohd.
Published: (2016) -
Y2O3 And CaO Zirconia as Reinforcement for Hydroxyapatite Biocomposite
by: Zaw , Linn Htun
Published: (2016) - Effect of niobium oxide (Nb2O5) addition to the physical and mechanical properties of cold isostatic press zirconia toughened alumina (ZTA)
-
Synthesis, Characterization And Co2 Adsorption Of Caco3, Ca(Oh)2 And Inert Materials Incorporated Ca(Oh)2
by: Hlaing, Nwe Ni
Published: (2016)