Preparation And Characterization Of Epoxy Particlefilled Thermosetting Composites
Water-based emulsion technique was used in this study to produce hollow epoxy particles (HEP) and solid epoxy particles (SEP). The HEP and SEP fillers were then chemically treated with hydrochloric acid solution to get rid of the excessive calcium carbonate on the surfaces of the fillers. It was fo...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2012
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/41978/1/LOW_LAY_FOON.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| id |
my-usm-ep.41978 |
|---|---|
| record_format |
uketd_dc |
| spelling |
my-usm-ep.419782019-04-12T05:26:23Z Preparation And Characterization Of Epoxy Particlefilled Thermosetting Composites 2012-03 Low, Lay Foon TN1-997 Mining engineering. Metallurgy Water-based emulsion technique was used in this study to produce hollow epoxy particles (HEP) and solid epoxy particles (SEP). The HEP and SEP fillers were then chemically treated with hydrochloric acid solution to get rid of the excessive calcium carbonate on the surfaces of the fillers. It was found that HEP and SEP fillers could be optimally prepared at the homogenizing time of 9 minutes and 7 minutes, respectively under the homogenizing speed of 15,000 rpm. HEP fillers were added into the epoxy, vinyl ester and polyester thermosetting matrices at different loading amounts (0-9 wt%) to strengthen and toughen the thermosetting matrices. 2012-03 Thesis http://eprints.usm.my/41978/ http://eprints.usm.my/41978/1/LOW_LAY_FOON.pdf application/pdf en public masters Universiti Sains Malaysia Pusat Pengajian Kejuteraan Bahan & Sumber Mineral |
| institution |
Universiti Sains Malaysia |
| collection |
USM Institutional Repository |
| language |
English |
| topic |
TN1-997 Mining engineering Metallurgy |
| spellingShingle |
TN1-997 Mining engineering Metallurgy Low, Lay Foon Preparation And Characterization Of Epoxy Particlefilled Thermosetting Composites |
| description |
Water-based emulsion technique was used in this study to produce hollow epoxy particles (HEP) and solid epoxy particles (SEP). The HEP and SEP fillers were then
chemically treated with hydrochloric acid solution to get rid of the excessive calcium carbonate on the surfaces of the fillers. It was found that HEP and SEP fillers could
be optimally prepared at the homogenizing time of 9 minutes and 7 minutes, respectively under the homogenizing speed of 15,000 rpm. HEP fillers were added into the epoxy, vinyl ester and polyester thermosetting matrices at different loading amounts (0-9 wt%) to strengthen and toughen the thermosetting matrices. |
| format |
Thesis |
| qualification_level |
Master's degree |
| author |
Low, Lay Foon |
| author_facet |
Low, Lay Foon |
| author_sort |
Low, Lay Foon |
| title |
Preparation And Characterization Of Epoxy Particlefilled
Thermosetting Composites
|
| title_short |
Preparation And Characterization Of Epoxy Particlefilled
Thermosetting Composites
|
| title_full |
Preparation And Characterization Of Epoxy Particlefilled
Thermosetting Composites
|
| title_fullStr |
Preparation And Characterization Of Epoxy Particlefilled
Thermosetting Composites
|
| title_full_unstemmed |
Preparation And Characterization Of Epoxy Particlefilled
Thermosetting Composites
|
| title_sort |
preparation and characterization of epoxy particlefilled
thermosetting composites |
| granting_institution |
Universiti Sains Malaysia |
| granting_department |
Pusat Pengajian Kejuteraan Bahan & Sumber Mineral |
| publishDate |
2012 |
| url |
http://eprints.usm.my/41978/1/LOW_LAY_FOON.pdf |
| _version_ |
1747821007618441216 |