The Effect Of Pre - Treatment Followed By Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Al 5052 Alloy

This research was aimed to study the effect of different pre-heat treatment on cryorolled Al 5052 alloy. Two types of pre-treatments; without pre-treatment, annealing (150°C, 200°C, 250°C, 300°C and 350°C) and solution treatment (480°C, 510°C and 540°C) were selected to study the effect of pre-heat...

Full description

Saved in:

Bibliographic Details
Main Author:	Norazman, Muhammad Anas
Format:	Thesis
Language:	English
Published:	2017
Subjects:	T Technology
Online Access:	http://eprints.usm.my/46356/1/The%20Effect%20Of%20Pre%20-%20Treatment%20Followed%20By%20Cryorolling%20On%20The%20Microstructures%2C%20Mechanical%20Properties%20And%20Corrosion%20Behaviour%20Of%20Al%205052%20Alloy.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-usm-ep.46356
record_format	uketd_dc
spelling	my-usm-ep.463562021-11-17T03:42:16Z The Effect Of Pre - Treatment Followed By Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Al 5052 Alloy 2017-03-01 Norazman, Muhammad Anas T Technology TA401-492 Materials of engineering and construction. Mechanics of materials This research was aimed to study the effect of different pre-heat treatment on cryorolled Al 5052 alloy. Two types of pre-treatments; without pre-treatment, annealing (150°C, 200°C, 250°C, 300°C and 350°C) and solution treatment (480°C, 510°C and 540°C) were selected to study the effect of pre-heat treatment on the properties of cryorolled Al 5052 alloy. Al 5052 alloys were heated at various pre-heat treatments process before cryorolling. Then, the Al 5052 alloys were dipped in liquid nitrogen and rolled at cryogenic temperature (cryorolling) at 30% thickness reduction. The Al 5052 alloy also was cold rolled at the 30% thickness reduction for comparison. The details of microstructural characteristics, physical properties, mechanical properties and corrosion behaviour of Al 5052 alloy were investigated using optical microscope (OM), scanning electron microscope (SEM), electron back scattered diffraction (EBSD), transmission electron microscope (TEM), X-ray diffraction (XRD), Vicker microhardness, Instron tensile test and potentiodynamic polarization test. The optical micrograph revealed that the grains are elongated along the rolling direction and the cryorolled samples showed higher grain aspect ratio compared to cold rolled. The grain aspect ratio increases with pre-heat treatment temperatures for both pre-heat treatment and achieved the highest aspect ratio at 300°C for pre-annealed and 540°C for pre-solution treated. The structure of cryorolled sample for both pre-heat treatment samples showed high density of dislocations and formation of submicron-sized grains. The mechanical properties showed that the cryorolled sample pre-annealed at 300°C exhibited the highest hardness, yield and ultimate tensile strength values with improvement of 17.3%, 13% and 15%, respectively, compared to non pre-treatment cryorolled sample. In contrast, the cryorolled sample pre-solution treated at 540°C exhibited the highest hardness, yield and ultimate tensile strength values with improvement of 13.6%, 7.1% and 4.8%, respectively, compared to non pre-treatment cryorolled sample. The cryorolled sample pre-annealed at 300°C and cryorolled sample pre-solution treated sample at 540°C exhibited the highest corrosion resistance due to lowest corrosion current, Icorr and corrosion rate values and more positive value of corrosion potential, Ecorr. The cryorolled sample pre-annealed at 300°C displayed an excellent physical, mechanical and corrosion properties compared to other samples. nano-composites are higher than UnF SiR/EPDM. 2017-03 Thesis http://eprints.usm.my/46356/ http://eprints.usm.my/46356/1/The%20Effect%20Of%20Pre%20-%20Treatment%20Followed%20By%20Cryorolling%20On%20The%20Microstructures%2C%20Mechanical%20Properties%20And%20Corrosion%20Behaviour%20Of%20Al%205052%20Alloy.pdf application/pdf en public masters Universiti Sains Malaysia Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral
institution	Universiti Sains Malaysia
collection	USM Institutional Repository
language	English
topic	T Technology T Technology
spellingShingle	T Technology T Technology Norazman, Muhammad Anas The Effect Of Pre - Treatment Followed By Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Al 5052 Alloy
description	This research was aimed to study the effect of different pre-heat treatment on cryorolled Al 5052 alloy. Two types of pre-treatments; without pre-treatment, annealing (150°C, 200°C, 250°C, 300°C and 350°C) and solution treatment (480°C, 510°C and 540°C) were selected to study the effect of pre-heat treatment on the properties of cryorolled Al 5052 alloy. Al 5052 alloys were heated at various pre-heat treatments process before cryorolling. Then, the Al 5052 alloys were dipped in liquid nitrogen and rolled at cryogenic temperature (cryorolling) at 30% thickness reduction. The Al 5052 alloy also was cold rolled at the 30% thickness reduction for comparison. The details of microstructural characteristics, physical properties, mechanical properties and corrosion behaviour of Al 5052 alloy were investigated using optical microscope (OM), scanning electron microscope (SEM), electron back scattered diffraction (EBSD), transmission electron microscope (TEM), X-ray diffraction (XRD), Vicker microhardness, Instron tensile test and potentiodynamic polarization test. The optical micrograph revealed that the grains are elongated along the rolling direction and the cryorolled samples showed higher grain aspect ratio compared to cold rolled. The grain aspect ratio increases with pre-heat treatment temperatures for both pre-heat treatment and achieved the highest aspect ratio at 300°C for pre-annealed and 540°C for pre-solution treated. The structure of cryorolled sample for both pre-heat treatment samples showed high density of dislocations and formation of submicron-sized grains. The mechanical properties showed that the cryorolled sample pre-annealed at 300°C exhibited the highest hardness, yield and ultimate tensile strength values with improvement of 17.3%, 13% and 15%, respectively, compared to non pre-treatment cryorolled sample. In contrast, the cryorolled sample pre-solution treated at 540°C exhibited the highest hardness, yield and ultimate tensile strength values with improvement of 13.6%, 7.1% and 4.8%, respectively, compared to non pre-treatment cryorolled sample. The cryorolled sample pre-annealed at 300°C and cryorolled sample pre-solution treated sample at 540°C exhibited the highest corrosion resistance due to lowest corrosion current, Icorr and corrosion rate values and more positive value of corrosion potential, Ecorr. The cryorolled sample pre-annealed at 300°C displayed an excellent physical, mechanical and corrosion properties compared to other samples. nano-composites are higher than UnF SiR/EPDM.
format	Thesis
qualification_level	Master's degree
author	Norazman, Muhammad Anas
author_facet	Norazman, Muhammad Anas
author_sort	Norazman, Muhammad Anas
title	The Effect Of Pre - Treatment Followed By Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Al 5052 Alloy
title_short	The Effect Of Pre - Treatment Followed By Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Al 5052 Alloy
title_full	The Effect Of Pre - Treatment Followed By Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Al 5052 Alloy
title_fullStr	The Effect Of Pre - Treatment Followed By Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Al 5052 Alloy
title_full_unstemmed	The Effect Of Pre - Treatment Followed By Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Al 5052 Alloy
title_sort	effect of pre - treatment followed by cryorolling on the microstructures, mechanical properties and corrosion behaviour of al 5052 alloy
granting_institution	Universiti Sains Malaysia
granting_department	Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral
publishDate	2017
url	http://eprints.usm.my/46356/1/The%20Effect%20Of%20Pre%20-%20Treatment%20Followed%20By%20Cryorolling%20On%20The%20Microstructures%2C%20Mechanical%20Properties%20And%20Corrosion%20Behaviour%20Of%20Al%205052%20Alloy.pdf
_version_	1747821657086492672

The Effect Of Pre - Treatment Followed By Cryorolling On The Microstructures, Mechanical Properties And Corrosion Behaviour Of Al 5052 Alloy

Similar Items