Effect Of Indium On Microstructure And Intermetallic Compound Formation During Isothermal Aging Of Sncu Solder Alloy

Solder is the interconnect material serving both electrical and mechanical connections between components and substrate in electronic devices. Concern over the toxicity of lead sparked intense focus on finding alternative lead-free solders to replace the traditional Sn-Pb solder. Among the lead-free...

Full description

Saved in:
Bibliographic Details
Main Author: Khusaini, Nur Nadirah Mohd
Format: Thesis
Language:English
Published: 2018
Subjects:
Online Access:http://eprints.usm.my/46688/1/Effect%20Of%20Indium%20On%20Microstructure%20And%20Intermetallic%20Compound%20Formation%20During%20Isothermal%20Aging%20Of%20Sncu%20Solder%20Alloy.pdf
Tags: Add Tag
No Tags, Be the first to tag this record!
id my-usm-ep.46688
record_format uketd_dc
spelling my-usm-ep.466882021-11-17T03:42:13Z Effect Of Indium On Microstructure And Intermetallic Compound Formation During Isothermal Aging Of Sncu Solder Alloy 2018-08-01 Khusaini, Nur Nadirah Mohd T Technology TA401-492 Materials of engineering and construction. Mechanics of materials Solder is the interconnect material serving both electrical and mechanical connections between components and substrate in electronic devices. Concern over the toxicity of lead sparked intense focus on finding alternative lead-free solders to replace the traditional Sn-Pb solder. Among the lead-free solder alloy, Sn-Cu alloy has relatively good physical and mechanical characteristics, low cost, and is currently being used in wave soldering. However, Sn-0.7Cu solder alloy has higher melting point (227°C) compared to SnPb (183°C). Indium was added into Sn-0.7Cu-0.05Ni-Ge (SN100C) solder alloy in this work to reduce the melting point, but the effect to IMC growth during thermal aging need to be evaluated. SN100C and indium added (0.5, 1, 1.5 and 2 wt%) solder was prepared via casting process. The solder alloys were reflowed onto Cu substrate at 270°C for 10 seconds. Elemental composition was determined using X-ray fluorescence (XRF) technique while melting point of solder alloys was determined using differential scanning calorimetry (DSC). Wetting balance test and spreading test were used to evaluate wettability. Meanwhile thermal aging was done for 100, 250 and 500 hours at 150°C and 180°C. Respectively, the microstructure of bulk solder and the IMC formed at interface between solder and Cu substrate were observed using scanning electron microscopy (SEM) equipped with electron dispersive x-ray (EDX). The wettability of solder alloys increased with increasing amount of In. Addition of In after aging resulted in the formation of (Cu,Ni)6Sn5 and Cu3Sn+Ni+In, seems to reduce formation of Cu6Sn5 and Cu3Sn IMC, and refined primary β-Sn dendrites. Further addition of 2 wt.% In resulted in formation of Sn-Cu-Ni-In IMC. The addition of 2 wt.% In gave the lowest growth rate of IMC which was 3.364 x 10-13 (cm2/s) while SN100C gave highest growth rate at 4.096 x 10-13 (cm2/s). The activation energy for SN100C-2In at 53 kJ/mol was the highest compared to SN100C 29.5 kJ/mol. From the result, it can be concluded that indium addition could lead to a finer β-Sn grain, increased hardness, improved wettability and supressed Cu3Sn IMC layer during isothermal aging which could increase the reliability of solder joint. 2018-08 Thesis http://eprints.usm.my/46688/ http://eprints.usm.my/46688/1/Effect%20Of%20Indium%20On%20Microstructure%20And%20Intermetallic%20Compound%20Formation%20During%20Isothermal%20Aging%20Of%20Sncu%20Solder%20Alloy.pdf application/pdf en public masters Universiti Sains Malaysia Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral
institution Universiti Sains Malaysia
collection USM Institutional Repository
language English
topic T Technology
T Technology
spellingShingle T Technology
T Technology
Khusaini, Nur Nadirah Mohd
Effect Of Indium On Microstructure And Intermetallic Compound Formation During Isothermal Aging Of Sncu Solder Alloy
description Solder is the interconnect material serving both electrical and mechanical connections between components and substrate in electronic devices. Concern over the toxicity of lead sparked intense focus on finding alternative lead-free solders to replace the traditional Sn-Pb solder. Among the lead-free solder alloy, Sn-Cu alloy has relatively good physical and mechanical characteristics, low cost, and is currently being used in wave soldering. However, Sn-0.7Cu solder alloy has higher melting point (227°C) compared to SnPb (183°C). Indium was added into Sn-0.7Cu-0.05Ni-Ge (SN100C) solder alloy in this work to reduce the melting point, but the effect to IMC growth during thermal aging need to be evaluated. SN100C and indium added (0.5, 1, 1.5 and 2 wt%) solder was prepared via casting process. The solder alloys were reflowed onto Cu substrate at 270°C for 10 seconds. Elemental composition was determined using X-ray fluorescence (XRF) technique while melting point of solder alloys was determined using differential scanning calorimetry (DSC). Wetting balance test and spreading test were used to evaluate wettability. Meanwhile thermal aging was done for 100, 250 and 500 hours at 150°C and 180°C. Respectively, the microstructure of bulk solder and the IMC formed at interface between solder and Cu substrate were observed using scanning electron microscopy (SEM) equipped with electron dispersive x-ray (EDX). The wettability of solder alloys increased with increasing amount of In. Addition of In after aging resulted in the formation of (Cu,Ni)6Sn5 and Cu3Sn+Ni+In, seems to reduce formation of Cu6Sn5 and Cu3Sn IMC, and refined primary β-Sn dendrites. Further addition of 2 wt.% In resulted in formation of Sn-Cu-Ni-In IMC. The addition of 2 wt.% In gave the lowest growth rate of IMC which was 3.364 x 10-13 (cm2/s) while SN100C gave highest growth rate at 4.096 x 10-13 (cm2/s). The activation energy for SN100C-2In at 53 kJ/mol was the highest compared to SN100C 29.5 kJ/mol. From the result, it can be concluded that indium addition could lead to a finer β-Sn grain, increased hardness, improved wettability and supressed Cu3Sn IMC layer during isothermal aging which could increase the reliability of solder joint.
format Thesis
qualification_level Master's degree
author Khusaini, Nur Nadirah Mohd
author_facet Khusaini, Nur Nadirah Mohd
author_sort Khusaini, Nur Nadirah Mohd
title Effect Of Indium On Microstructure And Intermetallic Compound Formation During Isothermal Aging Of Sncu Solder Alloy
title_short Effect Of Indium On Microstructure And Intermetallic Compound Formation During Isothermal Aging Of Sncu Solder Alloy
title_full Effect Of Indium On Microstructure And Intermetallic Compound Formation During Isothermal Aging Of Sncu Solder Alloy
title_fullStr Effect Of Indium On Microstructure And Intermetallic Compound Formation During Isothermal Aging Of Sncu Solder Alloy
title_full_unstemmed Effect Of Indium On Microstructure And Intermetallic Compound Formation During Isothermal Aging Of Sncu Solder Alloy
title_sort effect of indium on microstructure and intermetallic compound formation during isothermal aging of sncu solder alloy
granting_institution Universiti Sains Malaysia
granting_department Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral
publishDate 2018
url http://eprints.usm.my/46688/1/Effect%20Of%20Indium%20On%20Microstructure%20And%20Intermetallic%20Compound%20Formation%20During%20Isothermal%20Aging%20Of%20Sncu%20Solder%20Alloy.pdf
_version_ 1747821712831938560