Characterization and corrosion behaviour of 96.5Sn-3.0Ag-0.5Cu solder on Cu substrate at different reflow reactions

96.5Sn-3.0Ag-0.5Cu (SAC305) thin film solder exhibits different surface characteristics if compared to conventional bulk solder. In thin film solder, the actual surface is comprised of intermetallic layers whereas in the case of conventional solder, the intermetallic layers happened at the interfaci...

Full description

Saved in:

Bibliographic Details
Main Author:	Lee, Liu Mei
Format:	Thesis
Language:	English
Published:	2013
Subjects:	TN1-997 Mining engineering Metallurgy
Online Access:	http://eprints.usm.my/48025/1/characterization%20and%20corrosion%20behaviour24.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-usm-ep.48025
record_format	uketd_dc
spelling	my-usm-ep.480252020-12-28T04:22:03Z Characterization and corrosion behaviour of 96.5Sn-3.0Ag-0.5Cu solder on Cu substrate at different reflow reactions 2013 Lee, Liu Mei TN1-997 Mining engineering. Metallurgy 96.5Sn-3.0Ag-0.5Cu (SAC305) thin film solder exhibits different surface characteristics if compared to conventional bulk solder. In thin film solder, the actual surface is comprised of intermetallic layers whereas in the case of conventional solder, the intermetallic layers happened at the interfacial region of solder/base metal. This in turn, resulted in different surface microstructure and chemical composition. Moreover, a subtle and unstudied aspect of SAC305 in thin film characteristics was limited. Thus, the effect of solder reflow conditions at various temperatures and times were investigated. Structural and elemental characterizations indicated that Sn, Ag3Sn, and Cli6Sns were present in the as-deposited SAC305 thin film on Cu substrate. After solder reflow, SAC305 thin film was totally reacted and developed into Cu6Sns then Cu3Sn. Cu6Sn5 is located almost exclusively in the volume, whereas Cu3Sn appears as a thin uniform layer structure beneath Cu6Sn5• The Cu3Sn intermetallic layer consistent~y increases with increased temperature but remains within the thickness of Cu6Sn5• The corrosion behavior of bare Cu, as-deposited SAC305/Cu and as-reflowed SAC305/Cu at varying reflow temperatures was investigated by means of potentiodynamic polarization in a 6 M potassium hydroxide (KOH) solution. Bare Cu was found to possess the best corrosion resistance, whereas the as-deposited SAC305/Cu had the lowest corrosion resistance. 2013 Thesis http://eprints.usm.my/48025/ http://eprints.usm.my/48025/1/characterization%20and%20corrosion%20behaviour24.pdf application/pdf en public masters Universiti Sains Malaysia Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral
institution	Universiti Sains Malaysia
collection	USM Institutional Repository
language	English
topic	TN1-997 Mining engineering Metallurgy
spellingShingle	TN1-997 Mining engineering Metallurgy Lee, Liu Mei Characterization and corrosion behaviour of 96.5Sn-3.0Ag-0.5Cu solder on Cu substrate at different reflow reactions
description	96.5Sn-3.0Ag-0.5Cu (SAC305) thin film solder exhibits different surface characteristics if compared to conventional bulk solder. In thin film solder, the actual surface is comprised of intermetallic layers whereas in the case of conventional solder, the intermetallic layers happened at the interfacial region of solder/base metal. This in turn, resulted in different surface microstructure and chemical composition. Moreover, a subtle and unstudied aspect of SAC305 in thin film characteristics was limited. Thus, the effect of solder reflow conditions at various temperatures and times were investigated. Structural and elemental characterizations indicated that Sn, Ag3Sn, and Cli6Sns were present in the as-deposited SAC305 thin film on Cu substrate. After solder reflow, SAC305 thin film was totally reacted and developed into Cu6Sns then Cu3Sn. Cu6Sn5 is located almost exclusively in the volume, whereas Cu3Sn appears as a thin uniform layer structure beneath Cu6Sn5• The Cu3Sn intermetallic layer consistent~y increases with increased temperature but remains within the thickness of Cu6Sn5• The corrosion behavior of bare Cu, as-deposited SAC305/Cu and as-reflowed SAC305/Cu at varying reflow temperatures was investigated by means of potentiodynamic polarization in a 6 M potassium hydroxide (KOH) solution. Bare Cu was found to possess the best corrosion resistance, whereas the as-deposited SAC305/Cu had the lowest corrosion resistance.
format	Thesis
qualification_level	Master's degree
author	Lee, Liu Mei
author_facet	Lee, Liu Mei
author_sort	Lee, Liu Mei
title	Characterization and corrosion behaviour of 96.5Sn-3.0Ag-0.5Cu solder on Cu substrate at different reflow reactions
title_short	Characterization and corrosion behaviour of 96.5Sn-3.0Ag-0.5Cu solder on Cu substrate at different reflow reactions
title_full	Characterization and corrosion behaviour of 96.5Sn-3.0Ag-0.5Cu solder on Cu substrate at different reflow reactions
title_fullStr	Characterization and corrosion behaviour of 96.5Sn-3.0Ag-0.5Cu solder on Cu substrate at different reflow reactions
title_full_unstemmed	Characterization and corrosion behaviour of 96.5Sn-3.0Ag-0.5Cu solder on Cu substrate at different reflow reactions
title_sort	characterization and corrosion behaviour of 96.5sn-3.0ag-0.5cu solder on cu substrate at different reflow reactions
granting_institution	Universiti Sains Malaysia
granting_department	Pusat Pengajian Kejuruteraan Bahan dan Sumber Mineral
publishDate	2013
url	http://eprints.usm.my/48025/1/characterization%20and%20corrosion%20behaviour24.pdf
_version_	1747821868576931840

Characterization and corrosion behaviour of 96.5Sn-3.0Ag-0.5Cu solder on Cu substrate at different reflow reactions

Similar Items