Hydrothermal Process Route In The Synthesis Of Zinc Oxide Powder
In this work, zinc oxide powder is synthesized via the hydrothermal method. In the experimental procedure producing the ZnO powder, acetate buffer solution, sodium hydroxide, zinc nitrate hexahydrate solution (0.1 M and 1.0 M) and urea solution (0.2 M and 2.0M) are mixed under stirred condition i...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2009
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/48029/1/Hydrothermal%20Process%20Route%20In%20The%20Synthesis%20Of%20Zinc%20Oxide%20Powder.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| id |
my-usm-ep.48029 |
|---|---|
| record_format |
uketd_dc |
| spelling |
my-usm-ep.480292021-11-17T03:42:19Z Hydrothermal Process Route In The Synthesis Of Zinc Oxide Powder 2009-06-01 Ong, Pek Ling T Technology TA401-492 Materials of engineering and construction. Mechanics of materials In this work, zinc oxide powder is synthesized via the hydrothermal method. In the experimental procedure producing the ZnO powder, acetate buffer solution, sodium hydroxide, zinc nitrate hexahydrate solution (0.1 M and 1.0 M) and urea solution (0.2 M and 2.0M) are mixed under stirred condition in a pressure reactor. The molar concentration ratio of zinc nitrate hexahydrate to urea is 1 :2. The reaction time studied was at 3 hours and 5 hours at temperatures of 130°C and 150°C. The precipitates were dried after filtration and then calcination at 400°C. SEM analysis showed different types of morphology observed in the powders produced at varying reaction time and temperature. They were nano flakes-like shape, rod shape and hexagonal rod shape. The average thickness of the nano flakes structure obtained range from 7.49nm to 63.21nm. As for the rod shape particles, the width and length of the rod is 1. 724Jlm and 10.63 Jlm respectively. Overall EDX results, did not show the presence of other elemental peaks. From XRD analysis, the crystallite size of the samples produced range from 197.4A to 662.9A. The percentage of zinc oxide present in the sample from the XRF analysis is around 98.8 %. Results from thermal analysis (TGA/DT A) showed that the zinc oxide powder produced are stable with no significant change in mass. Zinc oxide powder with homogeneous distribution of nano flakes-like structure can be synthesized via hydrothermal process w1der low concentration of chemical precursors and at low reaction temperature and shorter reaction time. 2009-06 Thesis http://eprints.usm.my/48029/ http://eprints.usm.my/48029/1/Hydrothermal%20Process%20Route%20In%20The%20Synthesis%20Of%20Zinc%20Oxide%20Powder.pdf application/pdf en public masters Universiti Sains Malaysia Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral |
| institution |
Universiti Sains Malaysia |
| collection |
USM Institutional Repository |
| language |
English |
| topic |
T Technology T Technology |
| spellingShingle |
T Technology T Technology Ong, Pek Ling Hydrothermal Process Route In The Synthesis Of Zinc Oxide Powder |
| description |
In this work, zinc oxide powder is synthesized via the hydrothermal method.
In the experimental procedure producing the ZnO powder, acetate buffer solution,
sodium hydroxide, zinc nitrate hexahydrate solution (0.1 M and 1.0 M) and urea
solution (0.2 M and 2.0M) are mixed under stirred condition in a pressure reactor.
The molar concentration ratio of zinc nitrate hexahydrate to urea is 1 :2. The reaction
time studied was at 3 hours and 5 hours at temperatures of 130°C and 150°C. The
precipitates were dried after filtration and then calcination at 400°C. SEM analysis
showed different types of morphology observed in the powders produced at varying
reaction time and temperature. They were nano flakes-like shape, rod shape and
hexagonal rod shape. The average thickness of the nano flakes structure obtained
range from 7.49nm to 63.21nm. As for the rod shape particles, the width and length
of the rod is 1. 724Jlm and 10.63 Jlm respectively. Overall EDX results, did not show
the presence of other elemental peaks. From XRD analysis, the crystallite size of the
samples produced range from 197.4A to 662.9A. The percentage of zinc oxide
present in the sample from the XRF analysis is around 98.8 %. Results from thermal
analysis (TGA/DT A) showed that the zinc oxide powder produced are stable with no
significant change in mass. Zinc oxide powder with homogeneous distribution of
nano flakes-like structure can be synthesized via hydrothermal process w1der low
concentration of chemical precursors and at low reaction temperature and shorter
reaction time. |
| format |
Thesis |
| qualification_level |
Master's degree |
| author |
Ong, Pek Ling |
| author_facet |
Ong, Pek Ling |
| author_sort |
Ong, Pek Ling |
| title |
Hydrothermal Process Route In The Synthesis Of Zinc Oxide Powder |
| title_short |
Hydrothermal Process Route In The Synthesis Of Zinc Oxide Powder |
| title_full |
Hydrothermal Process Route In The Synthesis Of Zinc Oxide Powder |
| title_fullStr |
Hydrothermal Process Route In The Synthesis Of Zinc Oxide Powder |
| title_full_unstemmed |
Hydrothermal Process Route In The Synthesis Of Zinc Oxide Powder |
| title_sort |
hydrothermal process route in the synthesis of zinc oxide powder |
| granting_institution |
Universiti Sains Malaysia |
| granting_department |
Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral |
| publishDate |
2009 |
| url |
http://eprints.usm.my/48029/1/Hydrothermal%20Process%20Route%20In%20The%20Synthesis%20Of%20Zinc%20Oxide%20Powder.pdf |
| _version_ |
1747821869316177920 |