Influence Of Aluminium Doping On Random Lasing In Zno Nanorods
The purpose of this study is to investigate the structural, optical and random lasing characteristics from aluminium (Al) doped ZnO nanorods fabricated on ITO coated glass substrates using chemical bath deposition (CBD) technique. Different Al doping concentration 0 (ZnO), 0.25 (AZ1), 5 (AZ2), 10 (A...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English |
Published: |
2020
|
Subjects: | |
Online Access: | http://eprints.usm.my/52403/1/Pages%20from%20NUR%20FADZLIANA%20BINTI%20RAMLI%20-%20TESIS.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my-usm-ep.52403 |
---|---|
record_format |
uketd_dc |
spelling |
my-usm-ep.524032022-04-25T06:55:58Z Influence Of Aluminium Doping On Random Lasing In Zno Nanorods 2020-10 Ramli, Nur Fadzliana QC1 Physics (General) The purpose of this study is to investigate the structural, optical and random lasing characteristics from aluminium (Al) doped ZnO nanorods fabricated on ITO coated glass substrates using chemical bath deposition (CBD) technique. Different Al doping concentration 0 (ZnO), 0.25 (AZ1), 5 (AZ2), 10 (AZ3), 30 (AZ4) and 50 (AZ5) mM were explored. The majority of nanorods show a tapered structure with at the tip and voids between nanorods were more apparent with increasing Al concentration. Different doping concentration shows different average nanorod diameter between 29.22 nm and 33.80 nm. The formation of wurtzite ZnO phase with (002) as preferential orientation was confirmed by X-ray diffraction analysis. 2020-10 Thesis http://eprints.usm.my/52403/ http://eprints.usm.my/52403/1/Pages%20from%20NUR%20FADZLIANA%20BINTI%20RAMLI%20-%20TESIS.pdf application/pdf en public masters Universiti Sains Malaysia Pusat Pengajian Sains Fizik |
institution |
Universiti Sains Malaysia |
collection |
USM Institutional Repository |
language |
English |
topic |
QC1 Physics (General) |
spellingShingle |
QC1 Physics (General) Ramli, Nur Fadzliana Influence Of Aluminium Doping On Random Lasing In Zno Nanorods |
description |
The purpose of this study is to investigate the structural, optical and random lasing characteristics from aluminium (Al) doped ZnO nanorods fabricated on ITO coated glass substrates using chemical bath deposition (CBD) technique. Different Al doping concentration 0 (ZnO), 0.25 (AZ1), 5 (AZ2), 10 (AZ3), 30 (AZ4) and 50 (AZ5) mM were explored. The majority of nanorods show a tapered structure with at the tip and voids between nanorods were more apparent with increasing Al concentration. Different doping concentration shows different average nanorod diameter between 29.22 nm and 33.80 nm. The formation of wurtzite ZnO phase with (002) as preferential orientation was confirmed by X-ray diffraction analysis. |
format |
Thesis |
qualification_level |
Master's degree |
author |
Ramli, Nur Fadzliana |
author_facet |
Ramli, Nur Fadzliana |
author_sort |
Ramli, Nur Fadzliana |
title |
Influence Of Aluminium Doping On Random Lasing In Zno Nanorods |
title_short |
Influence Of Aluminium Doping On Random Lasing In Zno Nanorods |
title_full |
Influence Of Aluminium Doping On Random Lasing In Zno Nanorods |
title_fullStr |
Influence Of Aluminium Doping On Random Lasing In Zno Nanorods |
title_full_unstemmed |
Influence Of Aluminium Doping On Random Lasing In Zno Nanorods |
title_sort |
influence of aluminium doping on random lasing in zno nanorods |
granting_institution |
Universiti Sains Malaysia |
granting_department |
Pusat Pengajian Sains Fizik |
publishDate |
2020 |
url |
http://eprints.usm.my/52403/1/Pages%20from%20NUR%20FADZLIANA%20BINTI%20RAMLI%20-%20TESIS.pdf |
_version_ |
1747822175073599488 |