Effect Of Mechanical Activation On The Fluxing Properties Of Gua Musang Feldspar And Granite Quarry Dust
In the present study, mechanical activation was performed on samples of Gua Musang feldspar (GMF) and granite quarry dust (GQD). At first, GMF was milled for 10, 20 and 30 minutes, at 200, 300 and 400 rpm milling speeds. The powder obtained was then formed into pellets followed by firing at 1150,...
Saved in:
| Main Author: | |
|---|---|
| Format: | Thesis |
| Language: | English |
| Published: |
2013
|
| Subjects: | |
| Online Access: | http://eprints.usm.my/60805/1/24%20Pages%20from%2000001779610.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| id |
my-usm-ep.60805 |
|---|---|
| record_format |
uketd_dc |
| spelling |
my-usm-ep.608052024-07-10T01:23:17Z Effect Of Mechanical Activation On The Fluxing Properties Of Gua Musang Feldspar And Granite Quarry Dust 2013-03 Nordala, Phoumiphon TN1-997 Mining engineering. Metallurgy In the present study, mechanical activation was performed on samples of Gua Musang feldspar (GMF) and granite quarry dust (GQD). At first, GMF was milled for 10, 20 and 30 minutes, at 200, 300 and 400 rpm milling speeds. The powder obtained was then formed into pellets followed by firing at 1150, 1200 and 1250°C. From the milling and firing processes, 30 minutes was found to be the optimum time for milling. Therefore, in the milling process of GQD, 30 minutes was used at different milling speeds of200, 300 and 400 rpm. It was then fired at 1150, 1200 and 1250°C. At this stage, GQD was confirmed to be a suitable fluxing material as it can form a glassy phase and lower the firing temperature. Secondly, the process was followed by forming mixtures of GMF with ball clay (BC) and silica (SC) with a weight ratio of GMF 20 wt.%, 30 wt.% and 40 wt.%. These mixtures were fired at 1100, 1150 and 1200°C. In the final part, a mixture of GQD and BC without silica (SC) were prepared due to the high amount of silica in GQD. A weight ratio of GQD 40 wt.%, 50 wt.% and 60 wt.% were chosen. 2013-03 Thesis http://eprints.usm.my/60805/ http://eprints.usm.my/60805/1/24%20Pages%20from%2000001779610.pdf application/pdf en public masters Perpustakaan Hamzah Sendut Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral |
| institution |
Universiti Sains Malaysia |
| collection |
USM Institutional Repository |
| language |
English |
| topic |
TN1-997 Mining engineering Metallurgy |
| spellingShingle |
TN1-997 Mining engineering Metallurgy Nordala, Phoumiphon Effect Of Mechanical Activation On The Fluxing Properties Of Gua Musang Feldspar And Granite Quarry Dust |
| description |
In the present study, mechanical activation was performed on samples of Gua
Musang feldspar (GMF) and granite quarry dust (GQD). At first, GMF was milled
for 10, 20 and 30 minutes, at 200, 300 and 400 rpm milling speeds. The powder
obtained was then formed into pellets followed by firing at 1150, 1200 and 1250°C.
From the milling and firing processes, 30 minutes was found to be the optimum time
for milling. Therefore, in the milling process of GQD, 30 minutes was used at
different milling speeds of200, 300 and 400 rpm. It was then fired at 1150, 1200 and
1250°C. At this stage, GQD was confirmed to be a suitable fluxing material as it can
form a glassy phase and lower the firing temperature. Secondly, the process was
followed by forming mixtures of GMF with ball clay (BC) and silica (SC) with a
weight ratio of GMF 20 wt.%, 30 wt.% and 40 wt.%. These mixtures were fired at
1100, 1150 and 1200°C. In the final part, a mixture of GQD and BC without silica
(SC) were prepared due to the high amount of silica in GQD. A weight ratio of GQD
40 wt.%, 50 wt.% and 60 wt.% were chosen. |
| format |
Thesis |
| qualification_level |
Master's degree |
| author |
Nordala, Phoumiphon |
| author_facet |
Nordala, Phoumiphon |
| author_sort |
Nordala, Phoumiphon |
| title |
Effect Of Mechanical Activation On The Fluxing Properties Of Gua Musang Feldspar And Granite Quarry Dust |
| title_short |
Effect Of Mechanical Activation On The Fluxing Properties Of Gua Musang Feldspar And Granite Quarry Dust |
| title_full |
Effect Of Mechanical Activation On The Fluxing Properties Of Gua Musang Feldspar And Granite Quarry Dust |
| title_fullStr |
Effect Of Mechanical Activation On The Fluxing Properties Of Gua Musang Feldspar And Granite Quarry Dust |
| title_full_unstemmed |
Effect Of Mechanical Activation On The Fluxing Properties Of Gua Musang Feldspar And Granite Quarry Dust |
| title_sort |
effect of mechanical activation on the fluxing properties of gua musang feldspar and granite quarry dust |
| granting_institution |
Perpustakaan Hamzah Sendut |
| granting_department |
Pusat Pengajian Kejuruteraan Bahan & Sumber Mineral |
| publishDate |
2013 |
| url |
http://eprints.usm.my/60805/1/24%20Pages%20from%2000001779610.pdf |
| _version_ |
1804889000481128448 |