Modelling Of Wire Bonding Cu-Al Intermetallic Formation Growth Towards Interfacial Stress

Quality requirement in the semiconductor industry is getting more stringent due to the application of semiconductor components that are widely used in automotive. Furthermore different materials combination is being introduced to semiconductor packages to improve their package performance and reduce...

Full description

Saved in:

Bibliographic Details
Main Author:	Lee, Cher Chia
Format:	Thesis
Language:	English English
Published:	2017
Subjects:	T Technology (General) TS Manufactures
Online Access:	http://eprints.utem.edu.my/id/eprint/23786/1/Modelling%20Of%20Wire%20Bonding%20Cu-Al%20Intermetallic%20Formation%20Growth%20Towards%20Interfacial%20Stress%20-%20Lee%20Cher%20Chia%20-%2024%20Pages.pdf http://eprints.utem.edu.my/id/eprint/23786/2/Modelling%20Of%20Wire%20Bonding%20Cu-Al%20Intermetallic%20Formation%20Growth%20Towards%20Interfacial%20Stress.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-utem-ep.23786
record_format	uketd_dc
spelling	my-utem-ep.237862022-03-14T14:56:04Z Modelling Of Wire Bonding Cu-Al Intermetallic Formation Growth Towards Interfacial Stress 2017 Lee, Cher Chia T Technology (General) TS Manufactures Quality requirement in the semiconductor industry is getting more stringent due to the application of semiconductor components that are widely used in automotive. Furthermore different materials combination is being introduced to semiconductor packages to improve their package performance and reduce cost. The new materials combination can increase the packages functionality adversely mismatch of different materials properties induced higher interconnection and package stress. With such scenatio, quality of interconnects in the semiconductor products need more robust in order to withstand more severe condition and longer life. In this study the interfacial stress of Copper (Cu) Aluminium (Al) intermetallic compound (fMC) structure during high thermal stress condjtion is focused. Cu wire has been widely accepted as a main-stream interconnects to replace Au wire. Whereas AI bond pad is always the mostly used material for si licon semiconductor bond pad. According to Arrhenius equation, intermetallic growth is proportional to temperature. The Cu-Al IMC is complex due to the nanoscale and multiple phases exist. The Cu-Al IMC layer formed are normally in nanometer thickness, whereas Au-Al IMC is more thicker in micrometer. Analysis performed on Cu-AI IMC required more sophisticated and advanced tools. This is a big challenge for Cu-AI JMC studies. Thus the formation homogenous of Cu-Al fMC is more difficult to form compare to gold (Au) and AI IMC. Therefore using fuli te elements analysis (FEA) simulations of 3D models of various Cu-Al IMC compounds with different thickness is conducted to understand the stress and strain distribution at IMC layer. The numerical simulation is linear in nature and is based on linear isotropic material properties. Hence the equivalent stress is linear against increment of temperature. The modelling is using thermal-mechanical structure as the loading system. The effect of different fMC compound material properties is examined. From the numerical analysis once the IMC formed between Cu-AJ interconnect the interfacial stress increased 22%. The stress reduced - 3% when IMC grow1h thicker. The equivalent stress saturated when IMC growth more than 50% of the total AI bond pad thickness. Comparing different Cu-Al IMC compound Cu9A14 showed the most dominant impact towards the interfacial stress. Max equivalent stress and max elastic strain point occurred at the edge of Cu bond ball. UTeM 2017 Thesis http://eprints.utem.edu.my/id/eprint/23786/ http://eprints.utem.edu.my/id/eprint/23786/1/Modelling%20Of%20Wire%20Bonding%20Cu-Al%20Intermetallic%20Formation%20Growth%20Towards%20Interfacial%20Stress%20-%20Lee%20Cher%20Chia%20-%2024%20Pages.pdf text en public http://eprints.utem.edu.my/id/eprint/23786/2/Modelling%20Of%20Wire%20Bonding%20Cu-Al%20Intermetallic%20Formation%20Growth%20Towards%20Interfacial%20Stress.pdf text en validuser http://plh.utem.edu.my/cgi-bin/koha/opac-detail.pl?biblionumber=109161 mphil masters Universiti Teknikal Malaysia Melaka Faculty of Manufacturing Engineering
institution	Universiti Teknikal Malaysia Melaka
collection	UTeM Repository
language	English English
topic	T Technology (General) TS Manufactures
spellingShingle	T Technology (General) TS Manufactures Lee, Cher Chia Modelling Of Wire Bonding Cu-Al Intermetallic Formation Growth Towards Interfacial Stress
description	Quality requirement in the semiconductor industry is getting more stringent due to the application of semiconductor components that are widely used in automotive. Furthermore different materials combination is being introduced to semiconductor packages to improve their package performance and reduce cost. The new materials combination can increase the packages functionality adversely mismatch of different materials properties induced higher interconnection and package stress. With such scenatio, quality of interconnects in the semiconductor products need more robust in order to withstand more severe condition and longer life. In this study the interfacial stress of Copper (Cu) Aluminium (Al) intermetallic compound (fMC) structure during high thermal stress condjtion is focused. Cu wire has been widely accepted as a main-stream interconnects to replace Au wire. Whereas AI bond pad is always the mostly used material for si licon semiconductor bond pad. According to Arrhenius equation, intermetallic growth is proportional to temperature. The Cu-Al IMC is complex due to the nanoscale and multiple phases exist. The Cu-Al IMC layer formed are normally in nanometer thickness, whereas Au-Al IMC is more thicker in micrometer. Analysis performed on Cu-AI IMC required more sophisticated and advanced tools. This is a big challenge for Cu-AI JMC studies. Thus the formation homogenous of Cu-Al fMC is more difficult to form compare to gold (Au) and AI IMC. Therefore using fuli te elements analysis (FEA) simulations of 3D models of various Cu-Al IMC compounds with different thickness is conducted to understand the stress and strain distribution at IMC layer. The numerical simulation is linear in nature and is based on linear isotropic material properties. Hence the equivalent stress is linear against increment of temperature. The modelling is using thermal-mechanical structure as the loading system. The effect of different fMC compound material properties is examined. From the numerical analysis once the IMC formed between Cu-AJ interconnect the interfacial stress increased 22%. The stress reduced - 3% when IMC grow1h thicker. The equivalent stress saturated when IMC growth more than 50% of the total AI bond pad thickness. Comparing different Cu-Al IMC compound Cu9A14 showed the most dominant impact towards the interfacial stress. Max equivalent stress and max elastic strain point occurred at the edge of Cu bond ball.
format	Thesis
qualification_name	Master of Philosophy (M.Phil.)
qualification_level	Master's degree
author	Lee, Cher Chia
author_facet	Lee, Cher Chia
author_sort	Lee, Cher Chia
title	Modelling Of Wire Bonding Cu-Al Intermetallic Formation Growth Towards Interfacial Stress
title_short	Modelling Of Wire Bonding Cu-Al Intermetallic Formation Growth Towards Interfacial Stress
title_full	Modelling Of Wire Bonding Cu-Al Intermetallic Formation Growth Towards Interfacial Stress
title_fullStr	Modelling Of Wire Bonding Cu-Al Intermetallic Formation Growth Towards Interfacial Stress
title_full_unstemmed	Modelling Of Wire Bonding Cu-Al Intermetallic Formation Growth Towards Interfacial Stress
title_sort	modelling of wire bonding cu-al intermetallic formation growth towards interfacial stress
granting_institution	Universiti Teknikal Malaysia Melaka
granting_department	Faculty of Manufacturing Engineering
publishDate	2017
url	http://eprints.utem.edu.my/id/eprint/23786/1/Modelling%20Of%20Wire%20Bonding%20Cu-Al%20Intermetallic%20Formation%20Growth%20Towards%20Interfacial%20Stress%20-%20Lee%20Cher%20Chia%20-%2024%20Pages.pdf http://eprints.utem.edu.my/id/eprint/23786/2/Modelling%20Of%20Wire%20Bonding%20Cu-Al%20Intermetallic%20Formation%20Growth%20Towards%20Interfacial%20Stress.pdf
_version_	1747834055292878848

Modelling Of Wire Bonding Cu-Al Intermetallic Formation Growth Towards Interfacial Stress

Similar Items