Characterization and treatment of titanium dioxide, TiO2 via ultrasonic process with melastoma malabathricum as sustainable sensitizer for photovoltaic slar cell
Dye-sensitized solar cells (DSSCs) have been fabricated with doped Titanium Dioxide, TiO2 which are based on natural dyes from Malaysia tropical fruits, wherein contain interlocking groups; the carbonyl and hydroxyl groups of the anthocyanin molecule which enhance the photosensitization effect...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Thesis |
| 语言: | English English English |
| 出版: |
2012
|
| 主题: | |
| 在线阅读: | http://eprints.uthm.edu.my/2047/1/24p%20NUR%20MUNIRAH%20ABDULLAH.pdf http://eprints.uthm.edu.my/2047/2/NUR%20MUNIRAH%20ABDULLAH%20COPYRIGHT%20DECLARATION.pdf http://eprints.uthm.edu.my/2047/3/NUR%20MUNIRAH%20BINTI%20ABDULLAH%20WATERMARK.pdf |
| 标签: |
添加标签
没有标签, 成为第一个标记此记录!
|
| 总结: | Dye-sensitized solar cells (DSSCs) have been fabricated with doped Titanium Dioxide,
TiO2 which are based on natural dyes from Malaysia tropical fruits, wherein contain
interlocking groups; the carbonyl and hydroxyl groups of the anthocyanin molecule
which enhance the photosensitization effect due to the high interaction on the surface of
the film. Such a natural dye extracted from Melastoma Malabathricum can be subjected
to molecular tailoring to give a superior dye preparation, offering a wide range of
spectral absorption; covering the entire visible region (400 – 700 nm). This study is
based on a series of TiO2 preparations designated U1 and U2 (without and with additive
respectively), and those treated with ultrasonic energy, namely U3 and U4 (without and
with additive respectively). 10 minutes of sonication of the metal oxide led to its
breakdown from agglomeration at the micro to the nano scale. Furthermore the additive
(4-tert-butylpyridine) in potassium iodide, KI3 electrolyte, effects the rate of electron
injection into the oxidized dye sensitizer. Sonication of TiO2 reduced the particle size
agglomerates from 0.37 µm down to 0.15 µm; this treatment led to a more consistency
with high porosity, enabling enhance absorption and anchorage of the dye sensitizer.
Sonicated sample U4, with addition of electrolyte additive gives, open circuit voltage,
Voc= 0.742 V, short circuit current, Isc= 0.36 mA, fill factor, FF= 57.012 and 0.039 %
of cell’s efficiency. Evidently, sonication and addition of additive for KI3 electrolyte
offer enhanced capability for further application. |
|---|