Electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage

Articular cartilage is a soft tissue that covers bone joint surface. It has very low self-regenerative potential after injury, owing to its avascular nature. In recent years, hydrogels have been extensively studied as tissue engineering scaffolds for damaged articular cartilage. However, the use of...

全面介紹

Saved in:

書目詳細資料
主要作者:	Khoo, Weily
格式:	Thesis
語言:	English English English
出版:	2021
主題:	T Technology (General)
在線閱讀:	http://eprints.uthm.edu.my/8431/1/24p%20KHOO%20WEILY.pdf http://eprints.uthm.edu.my/8431/2/KHOO%20WEILY%20COPYRIGHT%20DECLARATION.pdf http://eprints.uthm.edu.my/8431/3/KHOO%20WEILY%20WATERMARK.pdf
標簽:	添加標簽沒有標簽, 成為第一個標記此記錄!

id	my-uthm-ep.8431
record_format	uketd_dc
spelling	my-uthm-ep.84312023-02-26T07:26:23Z Electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage 2021-11 Khoo, Weily T Technology (General) Articular cartilage is a soft tissue that covers bone joint surface. It has very low self-regenerative potential after injury, owing to its avascular nature. In recent years, hydrogels have been extensively studied as tissue engineering scaffolds for damaged articular cartilage. However, the use of fish skin gelatin as articular cartilage tissue engineering scaffold is remained unclear. Accordingly, the ultimate goal of this project is to investigate the feasibility of fish skin gelatin scaffold for articular cartilage tissue engineering application. Fish skin gelatin solution was first electrospun into fibrous scaffold under different solution feed rate (0.15 ml/h to 0.60 ml/h), applied voltage (9 kV to 18 kV) and spinning distance (10 cm to 25 cm). The scaffolds were visualized under SEM and mechanically tested in uniaxial tension and fracture mode I at displacement rate of 3 mm/min. Results revealed that scaffolds with fiber diameters ranged from 199 ± 15.75 nm to 795 ± 89.91 nm have been produced at different process parameters. After crosslinking with GA vapor, scaffolds were found to maintain their fibrous structure with improved aqueous stability and mechanical properties. The elastic modulus and fracture toughness of crosslinked scaffolds was found to achieve up to 363.50 ± 61.83 MPa and 8.81 ± 1.91 kJ/m2 respectively. The crosslinked electrospun scaffolds were stiffer and tougher than that of articular cartilage. Moreover, in vitro culture of human chondrocytes on scaffold revealed that fish skin gelatin scaffolds supported cell proliferation and attachment as well as ECM production. Besides that, in an attempt to mimic the layered structure and function of articular cartilage, graded electrospun scaffold was produced using sequential electrospinning process. Such scaffold presented gradually change in fiber diameter and packing density over the thickness. Overall, electrospun fish skin gelatin scaffolds produced in present work showed great promise for articular cartilage tissue engineering since they were mechanically stiff yet tough scaffolds which supported cell proliferation and GAGs accumulation. 2021-11 Thesis http://eprints.uthm.edu.my/8431/ http://eprints.uthm.edu.my/8431/1/24p%20KHOO%20WEILY.pdf text en public http://eprints.uthm.edu.my/8431/2/KHOO%20WEILY%20COPYRIGHT%20DECLARATION.pdf text en staffonly http://eprints.uthm.edu.my/8431/3/KHOO%20WEILY%20WATERMARK.pdf text en validuser phd doctoral Universiti Tun Hussein Onn Malaysia Fakulti Kejuruteraan Mekanikal dan Pembuatan
institution	Universiti Tun Hussein Onn Malaysia
collection	UTHM Institutional Repository
language	English English English
topic	T Technology (General)
spellingShingle	T Technology (General) Khoo, Weily Electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage
description	Articular cartilage is a soft tissue that covers bone joint surface. It has very low self-regenerative potential after injury, owing to its avascular nature. In recent years, hydrogels have been extensively studied as tissue engineering scaffolds for damaged articular cartilage. However, the use of fish skin gelatin as articular cartilage tissue engineering scaffold is remained unclear. Accordingly, the ultimate goal of this project is to investigate the feasibility of fish skin gelatin scaffold for articular cartilage tissue engineering application. Fish skin gelatin solution was first electrospun into fibrous scaffold under different solution feed rate (0.15 ml/h to 0.60 ml/h), applied voltage (9 kV to 18 kV) and spinning distance (10 cm to 25 cm). The scaffolds were visualized under SEM and mechanically tested in uniaxial tension and fracture mode I at displacement rate of 3 mm/min. Results revealed that scaffolds with fiber diameters ranged from 199 ± 15.75 nm to 795 ± 89.91 nm have been produced at different process parameters. After crosslinking with GA vapor, scaffolds were found to maintain their fibrous structure with improved aqueous stability and mechanical properties. The elastic modulus and fracture toughness of crosslinked scaffolds was found to achieve up to 363.50 ± 61.83 MPa and 8.81 ± 1.91 kJ/m2 respectively. The crosslinked electrospun scaffolds were stiffer and tougher than that of articular cartilage. Moreover, in vitro culture of human chondrocytes on scaffold revealed that fish skin gelatin scaffolds supported cell proliferation and attachment as well as ECM production. Besides that, in an attempt to mimic the layered structure and function of articular cartilage, graded electrospun scaffold was produced using sequential electrospinning process. Such scaffold presented gradually change in fiber diameter and packing density over the thickness. Overall, electrospun fish skin gelatin scaffolds produced in present work showed great promise for articular cartilage tissue engineering since they were mechanically stiff yet tough scaffolds which supported cell proliferation and GAGs accumulation.
format	Thesis
qualification_name	Doctor of Philosophy (PhD.)
qualification_level	Doctorate
author	Khoo, Weily
author_facet	Khoo, Weily
author_sort	Khoo, Weily
title	Electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage
title_short	Electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage
title_full	Electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage
title_fullStr	Electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage
title_full_unstemmed	Electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage
title_sort	electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage
granting_institution	Universiti Tun Hussein Onn Malaysia
granting_department	Fakulti Kejuruteraan Mekanikal dan Pembuatan
publishDate	2021
url	http://eprints.uthm.edu.my/8431/1/24p%20KHOO%20WEILY.pdf http://eprints.uthm.edu.my/8431/2/KHOO%20WEILY%20COPYRIGHT%20DECLARATION.pdf http://eprints.uthm.edu.my/8431/3/KHOO%20WEILY%20WATERMARK.pdf
_version_	1776103344153034752

Electrospun fish skin gelatin scaffolds for functional tissue engineering of articular cartilage

相似書籍