Microstructural studies of strontium titanate ceramic pressed at varying pressure
The purpose of this study is to fabricate the Strontium Titanate (SrTiO3) ceramics by using the High Energy Ball Milling Method (HEBM) for 9 hours at varying pressure between 60 MPa to 160 MPa at an interval 20 MPa. The samples were sintered at 1100 °C. The microstructures and morphology the samples...
Saved in:
Main Author: | |
---|---|
Format: | Thesis |
Language: | English |
Published: |
2014
|
Subjects: | |
Online Access: | http://eprints.utm.my/id/eprint/48052/25/NadiahMatSynedMFS2014.pdf |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
id |
my-utm-ep.48052 |
---|---|
record_format |
uketd_dc |
spelling |
my-utm-ep.480522017-08-06T04:41:28Z Microstructural studies of strontium titanate ceramic pressed at varying pressure 2014-06 Mat Syned, Nadiah QC Physics The purpose of this study is to fabricate the Strontium Titanate (SrTiO3) ceramics by using the High Energy Ball Milling Method (HEBM) for 9 hours at varying pressure between 60 MPa to 160 MPa at an interval 20 MPa. The samples were sintered at 1100 °C. The microstructures and morphology the samples were investigated by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) respectively. Meanwhile, the densities and porosities of the ceramics were determined via Archimedes’ method. The smallest crystallite size, 40.8 nm at 140 MPa and particle size, 0.58 ?m were found at the pressure 160 MPa this is due to the decreased of large voids by reorganization of granules. The maximum density of the samples was found to be 4.99 gcm-3 at 140 MPa while the porosity was 22.35 % at 60 MPa. 2014-06 Thesis http://eprints.utm.my/id/eprint/48052/ http://eprints.utm.my/id/eprint/48052/25/NadiahMatSynedMFS2014.pdf application/pdf en public masters Universiti Teknologi Malaysia, Faculty of Science Faculty of Science |
institution |
Universiti Teknologi Malaysia |
collection |
UTM Institutional Repository |
language |
English |
topic |
QC Physics |
spellingShingle |
QC Physics Mat Syned, Nadiah Microstructural studies of strontium titanate ceramic pressed at varying pressure |
description |
The purpose of this study is to fabricate the Strontium Titanate (SrTiO3) ceramics by using the High Energy Ball Milling Method (HEBM) for 9 hours at varying pressure between 60 MPa to 160 MPa at an interval 20 MPa. The samples were sintered at 1100 °C. The microstructures and morphology the samples were investigated by X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) respectively. Meanwhile, the densities and porosities of the ceramics were determined via Archimedes’ method. The smallest crystallite size, 40.8 nm at 140 MPa and particle size, 0.58 ?m were found at the pressure 160 MPa this is due to the decreased of large voids by reorganization of granules. The maximum density of the samples was found to be 4.99 gcm-3 at 140 MPa while the porosity was 22.35 % at 60 MPa. |
format |
Thesis |
qualification_level |
Master's degree |
author |
Mat Syned, Nadiah |
author_facet |
Mat Syned, Nadiah |
author_sort |
Mat Syned, Nadiah |
title |
Microstructural studies of strontium titanate ceramic pressed at varying pressure |
title_short |
Microstructural studies of strontium titanate ceramic pressed at varying pressure |
title_full |
Microstructural studies of strontium titanate ceramic pressed at varying pressure |
title_fullStr |
Microstructural studies of strontium titanate ceramic pressed at varying pressure |
title_full_unstemmed |
Microstructural studies of strontium titanate ceramic pressed at varying pressure |
title_sort |
microstructural studies of strontium titanate ceramic pressed at varying pressure |
granting_institution |
Universiti Teknologi Malaysia, Faculty of Science |
granting_department |
Faculty of Science |
publishDate |
2014 |
url |
http://eprints.utm.my/id/eprint/48052/25/NadiahMatSynedMFS2014.pdf |
_version_ |
1747817296099803136 |