Synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation

Platinum (Pt) is a noble metal catalyst that is most frequently used as the anode catalyst in direct methanol fuel cell (DMFC) because of its superior catalytic activity performance as compared to other metal catalysts. Besides the merit, Pt catalyst is expensive and also contributes to the problem...

Full description

Saved in:

Bibliographic Details
Main Author:	Hanifah, Mohamad Fahrul Radzi
Format:	Thesis
Language:	English
Published:	2015
Subjects:	QD Chemistry
Online Access:	http://eprints.utm.my/id/eprint/81130/1/MohamadFahrulRadziMFS2015.pdf
Tags:	Add Tag No Tags, Be the first to tag this record!

id	my-utm-ep.81130
record_format	uketd_dc
spelling	my-utm-ep.811302019-07-24T03:34:37Z Synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation 2015-10 Hanifah, Mohamad Fahrul Radzi QD Chemistry Platinum (Pt) is a noble metal catalyst that is most frequently used as the anode catalyst in direct methanol fuel cell (DMFC) because of its superior catalytic activity performance as compared to other metal catalysts. Besides the merit, Pt catalyst is expensive and also contributes to the problem of Pt poisoning by carbon monoxide (CO) during the methanol oxidation which can reduce the performance of DMFC. The use of carbonaceous material which is graphene nanosheets (GNS) as catalyst support for Pt catalyst can reduce the cost and enhance the catalytic property. Since the GNS have large surface area, the Pt nanoparticles can be dispersed uniformly onto the surface of GNS. Therefore, the main objective of this research is to synthesis and characterize the GNS supported Pt catalyst nanocomposite for methanol oxidation in DMFC. The nanocomposite from GNS and Pt catalyst precursor was fabricated by chemical reduction method using sodium borohydride as reducing agent. The physiochemical properties of the prepared graphene oxide nanosheets, GNS and the catalytic activity performance of GNS/Pt nanocomposite catalyst were successfully studied. Extensive characterization of the produced GNS as catalyst support in terms of morphology, structure, thermal stability and electrical conductivity property were conducted. The results showed that the prepared GNS possess high electrical conductivity of 7.65 S cm-1 thus indicated a highly potential catalyst support. HRTEM and FESEM analysis showed well-dispersed Pt nanoparticles on the surface of GNS with small average particle size around 3.33 nm obtained. The findings were consistent with the XRD data (~4.47 nm) obtained. The catalytic activities of GNS/Pt nanocomposites were measured by cyclic voltammogram. The electrochemical surface area (ECSA) of GNS/Pt nanocomposite catalyst was 0.36 cm2 larger than Vulcan XC-72/Pt (0.25 cm2) and graphite/Pt (0.14 cm2) catalysts. It has been found that GNS/Pt nanocomposite catalyst has better catalytic activity and high stability than Vulcan XC-72/Pt and graphite/Pt catalysts for methanol oxidation reaction. As a conclusion, the GNS/Pt nanocomposite catalyst fabricated in this study possesses appropriate characteristics to be used as anode catalyst in DMFC system. 2015-10 Thesis http://eprints.utm.my/id/eprint/81130/ http://eprints.utm.my/id/eprint/81130/1/MohamadFahrulRadziMFS2015.pdf application/pdf en public http://dms.library.utm.my:8080/vital/access/manager/Repository/vital:120176 masters Universiti Teknologi Malaysia, Faculty of Science Faculty of Science
institution	Universiti Teknologi Malaysia
collection	UTM Institutional Repository
language	English
topic	QD Chemistry
spellingShingle	QD Chemistry Hanifah, Mohamad Fahrul Radzi Synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation
description	Platinum (Pt) is a noble metal catalyst that is most frequently used as the anode catalyst in direct methanol fuel cell (DMFC) because of its superior catalytic activity performance as compared to other metal catalysts. Besides the merit, Pt catalyst is expensive and also contributes to the problem of Pt poisoning by carbon monoxide (CO) during the methanol oxidation which can reduce the performance of DMFC. The use of carbonaceous material which is graphene nanosheets (GNS) as catalyst support for Pt catalyst can reduce the cost and enhance the catalytic property. Since the GNS have large surface area, the Pt nanoparticles can be dispersed uniformly onto the surface of GNS. Therefore, the main objective of this research is to synthesis and characterize the GNS supported Pt catalyst nanocomposite for methanol oxidation in DMFC. The nanocomposite from GNS and Pt catalyst precursor was fabricated by chemical reduction method using sodium borohydride as reducing agent. The physiochemical properties of the prepared graphene oxide nanosheets, GNS and the catalytic activity performance of GNS/Pt nanocomposite catalyst were successfully studied. Extensive characterization of the produced GNS as catalyst support in terms of morphology, structure, thermal stability and electrical conductivity property were conducted. The results showed that the prepared GNS possess high electrical conductivity of 7.65 S cm-1 thus indicated a highly potential catalyst support. HRTEM and FESEM analysis showed well-dispersed Pt nanoparticles on the surface of GNS with small average particle size around 3.33 nm obtained. The findings were consistent with the XRD data (~4.47 nm) obtained. The catalytic activities of GNS/Pt nanocomposites were measured by cyclic voltammogram. The electrochemical surface area (ECSA) of GNS/Pt nanocomposite catalyst was 0.36 cm2 larger than Vulcan XC-72/Pt (0.25 cm2) and graphite/Pt (0.14 cm2) catalysts. It has been found that GNS/Pt nanocomposite catalyst has better catalytic activity and high stability than Vulcan XC-72/Pt and graphite/Pt catalysts for methanol oxidation reaction. As a conclusion, the GNS/Pt nanocomposite catalyst fabricated in this study possesses appropriate characteristics to be used as anode catalyst in DMFC system.
format	Thesis
qualification_level	Master's degree
author	Hanifah, Mohamad Fahrul Radzi
author_facet	Hanifah, Mohamad Fahrul Radzi
author_sort	Hanifah, Mohamad Fahrul Radzi
title	Synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation
title_short	Synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation
title_full	Synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation
title_fullStr	Synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation
title_full_unstemmed	Synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation
title_sort	synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation
granting_institution	Universiti Teknologi Malaysia, Faculty of Science
granting_department	Faculty of Science
publishDate	2015
url	http://eprints.utm.my/id/eprint/81130/1/MohamadFahrulRadziMFS2015.pdf
_version_	1747818308904681472

Synthesis and characterization of graphene nanosheets supported platinum nanocomposite as catalyst for methanol oxidation

Similar Items