Effects of oxidant and dopant loadings on direct ultrasonic irradiated polyaniline with nanostructure

Polyaniline (PANI) has been applied in many fields nowadays. In this study, di-rect ultrasonic irradiation, which means immersing the ultrasonic horn directly into the reaction solution, was used to polymerize polyaniline at frequency of 20 kHz, power of 600W. The overall objective of this study was...

Full description

Saved in:
Bibliographic Details
Main Author: Zheng, Xuefeng
Format: Thesis
Language:English
Published: 2020
Subjects:
Online Access:http://eprints.utm.my/id/eprint/92046/1/ZhengXuefengMSChE2020_valet-20210301-085854.pdf.pdf
Tags: Add Tag
No Tags, Be the first to tag this record!
id my-utm-ep.92046
record_format uketd_dc
spelling my-utm-ep.920462021-08-30T04:17:34Z Effects of oxidant and dopant loadings on direct ultrasonic irradiated polyaniline with nanostructure 2020 Zheng, Xuefeng TP Chemical technology Polyaniline (PANI) has been applied in many fields nowadays. In this study, di-rect ultrasonic irradiation, which means immersing the ultrasonic horn directly into the reaction solution, was used to polymerize polyaniline at frequency of 20 kHz, power of 600W. The overall objective of this study was to synthesize PANI with nanostructure and high conductivity under direct ultrasonic irradiation. The effects of oxidant, viz., ammonium persulfate (APS) and dopant, viz., hydrochloric acid (HCl) concentration on the structure integrity, morphology, and electrical conductivity properties of the pre-pared polyaniline were examined. As the molar ratio of APS to aniline varied from 0.1 to 1.25, the conductivity of PANI samples reached a maximum of 0.24 S/cm at the ratio of 1. Characteristic peaks at 1558, 1477, 1296, and 1226 cm-1 corresponded to quinonoid ring stretching, benzenoid ring (B) stretching, C-N stretching of secondary aromatic amine, and C-N stretching in B-NH-B-NH-B unit showed in the Fourier transform in-frared (FTIR) spectra, respectively. In the ultra violet-visible (UV-vis) spectra, the in-tensity ratio of absorbance bands at 570-670 nm and 330-400, denoted as p-p* excitation of quinonoid segment and p-p* excitation of benzenoid part respectively, attained a zen-ith at APS/aniline molar ratio of 1. The area percentage of three sharp, equal intensity, equal distant peaks at 7.02, 7.14, 7.27 assigned to ammonium protons reached a maxi-mum at APS/aniline molar ratio of 1 in the nuclear magnetic resonance (NMR) spec-troscopy. As the molar ratio of APS/aniline increased, four peaks at 2?=8.7°, 14.8°, 19.9° and 25.2° appeared in the X-ray diffraction (XRD) spectroscopy, and the crystallinity achieved a maximum at the molar ratio of 1. Field emission scanning electron micros-copy (FESEM) and high-resolution transmission electron microscopy (HRTEM) images showed vein-like structure, nanorods, nanofiber, bridge like structure and plate when APS/aniline molar ratio increased. Subsequently, the concentration of HCl was changed from 0.01 M to 2 M under the same preparation method with the optimized molar ratio of APS/aniline of 1. The conductivity of PANI samples increased with the increase of HCl concentration and reached a maximum of 0.5 S/cm at HCl concentration of 2 M. Characteristic peaks at 1554, 1480, 1287, and 1246 cm-1 corresponded to quinonoid ring stretching, benzenoid ring (B) stretching, C-N stretching of secondary aromatic amine, and C-N stretching in B-NH-B-NH-B unit showed in the FTIR spectra, respectively. In the UV-vis spectra, the intensity ratio of absorbance bands at 590-620 nm and 330-360, denoted as p-p* excitation of quinonoid segment and p-p* excitation of benzenoid part respectively, attained a zenith at HCl concentration of 2 M. The area percentage of three sharp, equal intensity, equal distant peaks at 7, 7.13, 7.26 assigned to ammonium protons reached a maximum at HCl concentration of 2 M in the NMR spectroscopy. As the HCl concentration increased, four peaks at 2?=8.6°, 14.9°, 19.9° and 25.2° appeared in the XRD spectroscopy, and the crystallinity achieved a maximum at the concentration of 2 M. FESEM images showed nanorods, nanostick, and petal-like structures when HCl concentration increased. 2020 Thesis http://eprints.utm.my/id/eprint/92046/ http://eprints.utm.my/id/eprint/92046/1/ZhengXuefengMSChE2020_valet-20210301-085854.pdf.pdf application/pdf en public http://dms.library.utm.my:8080/vital/access/manager/Repository/vital:139024 masters Universiti Teknologi Malaysia Faculty of Engineering - School of Chemical & Energy Engineering
institution Universiti Teknologi Malaysia
collection UTM Institutional Repository
language English
topic TP Chemical technology
spellingShingle TP Chemical technology
Zheng, Xuefeng
Effects of oxidant and dopant loadings on direct ultrasonic irradiated polyaniline with nanostructure
description Polyaniline (PANI) has been applied in many fields nowadays. In this study, di-rect ultrasonic irradiation, which means immersing the ultrasonic horn directly into the reaction solution, was used to polymerize polyaniline at frequency of 20 kHz, power of 600W. The overall objective of this study was to synthesize PANI with nanostructure and high conductivity under direct ultrasonic irradiation. The effects of oxidant, viz., ammonium persulfate (APS) and dopant, viz., hydrochloric acid (HCl) concentration on the structure integrity, morphology, and electrical conductivity properties of the pre-pared polyaniline were examined. As the molar ratio of APS to aniline varied from 0.1 to 1.25, the conductivity of PANI samples reached a maximum of 0.24 S/cm at the ratio of 1. Characteristic peaks at 1558, 1477, 1296, and 1226 cm-1 corresponded to quinonoid ring stretching, benzenoid ring (B) stretching, C-N stretching of secondary aromatic amine, and C-N stretching in B-NH-B-NH-B unit showed in the Fourier transform in-frared (FTIR) spectra, respectively. In the ultra violet-visible (UV-vis) spectra, the in-tensity ratio of absorbance bands at 570-670 nm and 330-400, denoted as p-p* excitation of quinonoid segment and p-p* excitation of benzenoid part respectively, attained a zen-ith at APS/aniline molar ratio of 1. The area percentage of three sharp, equal intensity, equal distant peaks at 7.02, 7.14, 7.27 assigned to ammonium protons reached a maxi-mum at APS/aniline molar ratio of 1 in the nuclear magnetic resonance (NMR) spec-troscopy. As the molar ratio of APS/aniline increased, four peaks at 2?=8.7°, 14.8°, 19.9° and 25.2° appeared in the X-ray diffraction (XRD) spectroscopy, and the crystallinity achieved a maximum at the molar ratio of 1. Field emission scanning electron micros-copy (FESEM) and high-resolution transmission electron microscopy (HRTEM) images showed vein-like structure, nanorods, nanofiber, bridge like structure and plate when APS/aniline molar ratio increased. Subsequently, the concentration of HCl was changed from 0.01 M to 2 M under the same preparation method with the optimized molar ratio of APS/aniline of 1. The conductivity of PANI samples increased with the increase of HCl concentration and reached a maximum of 0.5 S/cm at HCl concentration of 2 M. Characteristic peaks at 1554, 1480, 1287, and 1246 cm-1 corresponded to quinonoid ring stretching, benzenoid ring (B) stretching, C-N stretching of secondary aromatic amine, and C-N stretching in B-NH-B-NH-B unit showed in the FTIR spectra, respectively. In the UV-vis spectra, the intensity ratio of absorbance bands at 590-620 nm and 330-360, denoted as p-p* excitation of quinonoid segment and p-p* excitation of benzenoid part respectively, attained a zenith at HCl concentration of 2 M. The area percentage of three sharp, equal intensity, equal distant peaks at 7, 7.13, 7.26 assigned to ammonium protons reached a maximum at HCl concentration of 2 M in the NMR spectroscopy. As the HCl concentration increased, four peaks at 2?=8.6°, 14.9°, 19.9° and 25.2° appeared in the XRD spectroscopy, and the crystallinity achieved a maximum at the concentration of 2 M. FESEM images showed nanorods, nanostick, and petal-like structures when HCl concentration increased.
format Thesis
qualification_level Master's degree
author Zheng, Xuefeng
author_facet Zheng, Xuefeng
author_sort Zheng, Xuefeng
title Effects of oxidant and dopant loadings on direct ultrasonic irradiated polyaniline with nanostructure
title_short Effects of oxidant and dopant loadings on direct ultrasonic irradiated polyaniline with nanostructure
title_full Effects of oxidant and dopant loadings on direct ultrasonic irradiated polyaniline with nanostructure
title_fullStr Effects of oxidant and dopant loadings on direct ultrasonic irradiated polyaniline with nanostructure
title_full_unstemmed Effects of oxidant and dopant loadings on direct ultrasonic irradiated polyaniline with nanostructure
title_sort effects of oxidant and dopant loadings on direct ultrasonic irradiated polyaniline with nanostructure
granting_institution Universiti Teknologi Malaysia
granting_department Faculty of Engineering - School of Chemical & Energy Engineering
publishDate 2020
url http://eprints.utm.my/id/eprint/92046/1/ZhengXuefengMSChE2020_valet-20210301-085854.pdf.pdf
_version_ 1747818560053313536