Structural Magnetic and Electrical Properties Of La0.67ca0.33mn03 Perovskite Synthesized Via Conventional and Co-Precipitation Methods
The structural, magnetic and electrical properties of lanthanum manganites having a nominal composition of Lao67C~.33Mn0s3y nthesized via co-precipitation method (COP) following sintering treatments at temperature ranging between 1100°C and 1350°C are reported. XRD pattern showed the monophasic o...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Thesis |
| 語言: | English English |
| 出版: |
2004
|
| 主題: | |
| 在線閱讀: | http://psasir.upm.edu.my/id/eprint/6340/1/FSAS_2004_16.pdf |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| id |
my-upm-ir.6340 |
|---|---|
| record_format |
uketd_dc |
| spelling |
my-upm-ir.63402023-10-23T08:40:26Z Structural Magnetic and Electrical Properties Of La0.67ca0.33mn03 Perovskite Synthesized Via Conventional and Co-Precipitation Methods 2004-06 Ahmed Ali Salama, Hazar Ali The structural, magnetic and electrical properties of lanthanum manganites having a nominal composition of Lao67C~.33Mn0s3y nthesized via co-precipitation method (COP) following sintering treatments at temperature ranging between 1100°C and 1350°C are reported. XRD pattern showed the monophasic orthorhombic structure of the sample sintered within the above temperature range for a sintering period of 24 hours. The SEM micrographs showed that the grains are well grown and clear grain boundaries are observed. The grain size increased significantly form 1.7pm to 10.3pm as the sintering temperature increases and were well compacted. Large grains growth with layered features is observed in samples sintered at higher temperature. Ferromagneticparamagnetic phase transition were observed in the f-temperature curves for all the sintered samples. The Curie temperature, T, shifts to lower temperature as the sintering temperature, Ts increases. All the samples show the typical ferromagnetic-paramagnetic phase transition, Tc in the range 267.9 K-259.7 K. The transport properties show the transition of semiconducting to metallic conductivity at Tp, the transition occurs within the range 276 K - 288 K which is higher compared with the data reported earlier. Based on the semiconducting model, Ln(R) oc (- E, /K,T) it was observed that the Activation energy, E, value ranges from 100.40 to 118.73 meV. The colossal magnetoresistance effect appears at low temperature and the highest value of CMR effect was observed at temperature approaching Tp. The highest CMR value was observed near the insulatormetal transition. The maximum MR with a value of -68.2% for H = 1.06 T is obtained in the sample prepared at 1 200°C. The specimens of L a 0 . ~ ~ C a 0 ~p~rehpahre0d~ v ia COP method were compared to the specimen prepared by Conventional Powder method (CPM) for samples sintered at 1300°C. XRD spectrum for the samples exhibit orthorhombic distorted and single-phase perovskite structures. The Curie temperature, Tc and the metal-insulator transition temperature, Tp were obtained by ac susceptibility and four- point probe techniques. The results showed that Tc and Tp were 260 K and 276 K respectively for the COP specimen, which is higher than the results obtained by specimen prepared by CPM with Tc and Tp 245 K and 246 K respectively. These results are due to the high chemical homogeneity and high density for the COP specimen as compared to the CPM specimen. The CMR for the (COP) specimen is observed near the insulator- metal transition with the value of - 56% for H = 1.06 T while for the CPM the CMR value of -34% Perovskite - Synthesis. 2004-06 Thesis http://psasir.upm.edu.my/id/eprint/6340/ http://psasir.upm.edu.my/id/eprint/6340/1/FSAS_2004_16.pdf text en public masters Universiti Putra Malaysia Perovskite - Synthesis. Science and Environmental Studies Shaar, Abdul Halim English |
| institution |
Universiti Putra Malaysia |
| collection |
PSAS Institutional Repository |
| language |
English English |
| advisor |
Shaar, Abdul Halim |
| topic |
Perovskite - Synthesis. |
| spellingShingle |
Perovskite - Synthesis. Ahmed Ali Salama, Hazar Ali Structural Magnetic and Electrical Properties Of La0.67ca0.33mn03 Perovskite Synthesized Via Conventional and Co-Precipitation Methods |
| description |
The structural, magnetic and electrical properties of lanthanum manganites having a
nominal composition of Lao67C~.33Mn0s3y nthesized via co-precipitation method
(COP) following sintering treatments at temperature ranging between 1100°C and
1350°C are reported. XRD pattern showed the monophasic orthorhombic structure of the
sample sintered within the above temperature range for a sintering period of 24 hours.
The SEM micrographs showed that the grains are well grown and clear grain boundaries
are observed. The grain size increased significantly form 1.7pm to 10.3pm as the
sintering temperature increases and were well compacted. Large grains growth with
layered features is observed in samples sintered at higher temperature. Ferromagneticparamagnetic
phase transition were observed in the f-temperature curves for all the
sintered samples. The Curie temperature, T, shifts to lower temperature as the sintering
temperature, Ts increases. All the samples show the typical ferromagnetic-paramagnetic phase transition, Tc in the range 267.9 K-259.7 K. The transport properties show the
transition of semiconducting to metallic conductivity at Tp, the transition occurs within
the range 276 K - 288 K which is higher compared with the data reported earlier. Based
on the semiconducting model, Ln(R) oc (- E, /K,T) it was observed that the Activation
energy, E, value ranges from 100.40 to 118.73 meV. The colossal magnetoresistance
effect appears at low temperature and the highest value of CMR effect was observed at
temperature approaching Tp. The highest CMR value was observed near the insulatormetal
transition. The maximum MR with a value of -68.2% for H = 1.06 T is obtained
in the sample prepared at 1 200°C.
The specimens of L a 0 . ~ ~ C a 0 ~p~rehpahre0d~ v ia COP method were compared to the
specimen prepared by Conventional Powder method (CPM) for samples sintered at
1300°C. XRD spectrum for the samples exhibit orthorhombic distorted and single-phase
perovskite structures. The Curie temperature, Tc and the metal-insulator transition
temperature, Tp were obtained by ac susceptibility and four- point probe techniques. The
results showed that Tc and Tp were 260 K and 276 K respectively for the COP specimen,
which is higher than the results obtained by specimen prepared by CPM with Tc and Tp
245 K and 246 K respectively. These results are due to the high chemical homogeneity
and high density for the COP specimen as compared to the CPM specimen. The CMR
for the (COP) specimen is observed near the insulator- metal transition with the value of
- 56% for H = 1.06 T while for the CPM the CMR value of -34% |
| format |
Thesis |
| qualification_level |
Master's degree |
| author |
Ahmed Ali Salama, Hazar Ali |
| author_facet |
Ahmed Ali Salama, Hazar Ali |
| author_sort |
Ahmed Ali Salama, Hazar Ali |
| title |
Structural Magnetic and Electrical Properties Of La0.67ca0.33mn03 Perovskite Synthesized Via Conventional and Co-Precipitation Methods |
| title_short |
Structural Magnetic and Electrical Properties Of La0.67ca0.33mn03 Perovskite Synthesized Via Conventional and Co-Precipitation Methods |
| title_full |
Structural Magnetic and Electrical Properties Of La0.67ca0.33mn03 Perovskite Synthesized Via Conventional and Co-Precipitation Methods |
| title_fullStr |
Structural Magnetic and Electrical Properties Of La0.67ca0.33mn03 Perovskite Synthesized Via Conventional and Co-Precipitation Methods |
| title_full_unstemmed |
Structural Magnetic and Electrical Properties Of La0.67ca0.33mn03 Perovskite Synthesized Via Conventional and Co-Precipitation Methods |
| title_sort |
structural magnetic and electrical properties of la0.67ca0.33mn03 perovskite synthesized via conventional and co-precipitation methods |
| granting_institution |
Universiti Putra Malaysia |
| granting_department |
Science and Environmental Studies |
| publishDate |
2004 |
| url |
http://psasir.upm.edu.my/id/eprint/6340/1/FSAS_2004_16.pdf |
| _version_ |
1783725731863330816 |